স্টেইনলেস স্টীল, অস্টেনাইটিক
S310H Stainless Steel (S31009) Pipe & Fittings
A high carbon modification of 310 developed for enhanced creep resistance.
Alloy 310 (UNS S31000) is an austenitic stainless steel developed for use in high temperature corrosion resistant applications. The alloy resists oxidation up to 2010°F (1100°C) under mildly cyclic conditions.
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল এর জন্য ডিজাইন করা হয়েছে excellent high-temperature strength and oxidation resistance. The “H” in 310H indicates a উচ্চ কার্বন উপাদান, which improves its ক্রীপ প্রতিরোধ ক্ষমতা at elevated temperatures compared to standard 310 stainless steel.
This steel is widely used in high-temperature industrial applications, such as furnaces, heat exchangers, and thermal processing equipment, where it maintains mechanical integrity and corrosion resistance under prolonged exposure to heat and oxidizing environments.
পিডিএফ ডাউনলোড করুন
পরিসীমা
অনুগ্রহ করে লক্ষ্য করুন
আপনি যদি যা খুঁজছেন তা না পান, অনুগ্রহ করে আপনার সাথে যোগাযোগ করুন। স্থানীয় সেবা কেন্দ্র আপনার নির্দিষ্ট চাহিদা অনুযায়ী.
S310H Stainless Steel Related Specifications
| সিস্টেম / স্ট্যান্ডার্ড | দেশ / অঞ্চল | গ্রেড / পদবী |
| এআইএসআই | যুক্তরাষ্ট্র | 310H |
| ইউএনএস | আন্তর্জাতিক | S31009 |
| ই.এন. / ডব্লিউ.এন.আর. | ইউরোপ | 1.4845 |
| ইএন নাম | ইউরোপ | X8CrNi25-21 |
| ASTM A240 | যুক্তরাষ্ট্র | 310H (plate, sheet, strip) |
| ASTM A213 | যুক্তরাষ্ট্র | TP310H (boiler / HX tubes) |
| ASTM A312 | যুক্তরাষ্ট্র | TP310H (seamless pipe) |
| ASTM A403 | যুক্তরাষ্ট্র | WP310H (butt-weld fittings) |
| জিবি | চীন | 07Cr25Ni20 (310H type) |
| জাপানিজ শিল্প মান | জাপান | SUS310H |
গুণাবলী
রাসায়নিক গঠন
S31009 Pipe
ASTM A312
| রাসায়নিক মৌল | % উপস্থাপন |
| কার্বন (C) | 0.04 - 0.10 |
| ক্রোমিয়াম (Cr) | 24.00 - 26.00 |
| নিকেল (নি) | 19.00 - 22.00 |
| ম্যাঙ্গানিজ (Mn) | 0.00 - 2.00 |
| ফসফরাস (পি) | 0.00 - 0.05 |
| গন্ধক (S) | 0.00 - 0.03 |
| সিলিকন (Si) | 0.00 - 1.00 |
| লৌহ (Fe) | সমতা |
যান্ত্রিক ধর্ম
Pipe
ASTM A312
| যান্ত্রিক সম্পত্তি | মূল্য |
| প্রমাণ চাপ | ২০৫ মিনিট মেগাপাস্কাল |
| টানজনিত শক্তি | ৫১৫ মিনি MPa |
| প্রসার A50 মিমি | 35 Min % |
Applications of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল সহ excellent high-temperature strength and oxidation resistance. Its combination of mechanical integrity and corrosion resistance at elevated temperatures makes it ideal for industrial applications exposed to heat and oxidizing environments.
1. High-Temperature Industrial Applications
Furnace components such as retorts, trays, and baskets
Kiln parts and heat treatment equipment
Boiler and heat exchanger components exposed to prolonged high temperatures
Thermal processing equipment in chemical, petrochemical, and power industries
2. Petrochemical and Chemical Industry
Piping, tanks, and vessels for high-temperature chemical processes
Components handling oxidizing gases or high-temperature vapors
Industrial reactors and processing equipment operating under thermal stress
3. Other Applications
Aerospace and automotive components exposed to high-temperature exhaust or heat
Incinerators and combustion chambers
High-temperature structural parts in industrial machinery
সারসংক্ষেপ
310H stainless steel is used in applications that require high-temperature strength, creep resistance, and oxidation resistance. এর high-carbon, austenitic structure makes it suitable for furnaces, boilers, heat exchangers, chemical equipment, and industrial machinery exposed to extreme heat and oxidizing environments.
Characteristics of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল এর জন্য পরিচিত excellent high-temperature strength, oxidation resistance, and creep resistance. The elevated carbon content provides improved performance in prolonged high-temperature applications, especially compared to standard 310 stainless steel.
১. উচ্চ-তাপমাত্রায় শক্তি
Maintains mechanical integrity at very high temperatures.
Suitable for continuous service up to approximately 1030°C (1885°F) and intermittent exposure up to 1100°C (2010°F).
Higher carbon content enhances ক্রীপ প্রতিরোধ ক্ষমতা for prolonged high-temperature operation.
2. Oxidation and Scaling Resistance
গঠন করে stable chromium oxide layer that protects against scaling in oxidizing atmospheres.
ভালভাবে সম্পাদন করে furnace, boiler, and thermal processing applications.
3. Corrosion Resistance
এর বিরুদ্ধে ভাল প্রতিরোধ general corrosion in oxidizing environments.
Titanium and other stabilizing elements prevent sensitization, minimizing intergranular corrosion in welded components.
4. Mechanical Properties
Excellent ductility and toughness even at elevated temperatures.
Maintains structural stability under thermal stress and high loads.
5. Fabrication and Weldability
Can be welded using conventional methods, though careful control of heat input is recommended to avoid excessive grain growth.
May require post-weld heat treatment in certain high-temperature applications.
6. Applications Related to Characteristics
Furnace components and heat treatment equipment
Boilers, heat exchangers, and thermal processing machinery
Aerospace and automotive components exposed to high temperatures
Industrial piping and structural parts for high-temperature service
সারসংক্ষেপ
310H stainless steel is characterized by high-temperature strength, creep resistance, oxidation resistance, and good weldability. এর high-carbon, austenitic structure makes it ideal for furnaces, boilers, heat exchangers, chemical processing equipment, and other industrial applications exposed to extreme heat.
অতিরিক্ত তথ্য
তৈরি/নির্মাণ
Fabrication of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল সহ excellent high-temperature strength, oxidation resistance, and creep resistance. Fabrication techniques are similar to other austenitic stainless steels, but attention must be paid to high-temperature performance, weldability, and work hardening.
১. গঠন
শীতল কাজের প্রক্রিয়া:
Can be bent, rolled, or deep-drawn, but work hardens rapidly.
Intermediate annealing may be required for extensive forming to restore ductility.
গরম কাজ:
Performed at ১১৫০–৯০০°C (২১০০–১৬৫০°F) to reduce work hardening and improve formability.
Suitable for forging, rolling, and extrusion of large or complex parts.
2. Welding
ব্যবহার করে ওয়েল্ড করা যেতে পারে TIG, MIG, SMAW, or FCAW.
High-carbon content increases the risk of sensitization in some cases; preheating and controlled heat input may be recommended.
Post-weld solution annealing can restore high-temperature properties and reduce residual stresses.
৩. মেশিনিং
যন্ত্রযোগ্যতা হল মধ্যমপন্থী, with rapid work hardening.
ব্যবহার করুন sharp carbide tools, proper feed rates, and coolant for best results.
Suitable for industrial components requiring precision fabrication.
4. Post-Fabrication Treatments
অ্যানিলিং: Restores ductility and relieves stresses from cold working or welding.
Pickling or passivation: Removes scale or oxide layers and improves corrosion resistance.
5. Applications Related to Fabrication
Furnace components, heat treatment equipment, and kiln parts
Boilers, heat exchangers, and industrial piping
Aerospace and automotive components exposed to high-temperature service
Structural parts for chemical, petrochemical, and power generation industries
সারসংক্ষেপ
310H stainless steel is highly fabricable using conventional forming, welding, and machining techniques. Careful control of heat input, work hardening, and post-fabrication treatments ensures high-temperature strength, corrosion resistance, and dimensional stability for furnaces, boilers, heat exchangers, and industrial machinery.
ঢালাইযোগ্যতা
Weldability of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল অসাধারণের সাথে high-temperature strength and oxidation resistance. Its weldability is good, but the high carbon content requires careful control of welding procedures to maintain mechanical properties and corrosion resistance.
১. সাধারণ ওয়েল্ডযোগ্যতা
Can be welded using standard fusion welding methods:
টিআইজি (জিটিএডব্লিউ)
এমআইজি (জিএমএডব্লিউ)
এসএমএডব্লিউ (প্রতিরক্ষিত ধাতু আর্ক ওয়েল্ডিং)
এফসিএডব্লিউ (ফ্লাক্স-কোরেড আর্ক ওয়েল্ডিং)
Suitable for joining components in high-temperature and industrial applications.
2. Considerations for Welding
High carbon content increases the risk of সংবেদনশীলকরণ, which can lead to intergranular corrosion if exposed to corrosive environments.
Controlled heat input and preheating may be required for thick sections to minimize distortion and reduce residual stresses.
সঠিকভাবে ব্যবহার করুন ভরাট ধাতু (commonly 310 or 310H) to maintain high-temperature properties and corrosion resistance.
3. Post-Weld Treatment
সলিউশন এনিলিং may be applied to restore high-temperature strength and ductility.
Pickling and passivation can remove surface oxides formed during welding and improve corrosion resistance.
4. Applications Related to Weldability
Furnace and kiln components
Heat exchangers and boiler parts
High-temperature piping and tanks in chemical and petrochemical industries
Industrial structural parts requiring welded joints for high-temperature service
সারসংক্ষেপ
310H stainless steel has ভাল ওয়েল্ডযোগ্যতা using standard techniques, but attention must be paid to carbon content, heat input, and post-weld treatments. Proper welding ensures strong, corrosion-resistant joints উপযুক্ত high-temperature industrial, chemical, and power generation applications.
যন্ত্রযোগ্যতা
Machinability of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল অসাধারণের সাথে high-temperature strength and oxidation resistance. Like other austenitic stainless steels, it exhibits moderate to low machinability due to its tendency to work harden rapidly.
1. Work Hardening
310H stainless steel work hardens quickly, especially during light cuts or interrupted cuts.
Excessive work hardening can cause tool wear, poor surface finish, and dimensional inaccuracies.
ব্যবহার করুন sharp cutting tools and proper feeds to minimize work hardening.
২. টুলিং সুপারিশসমূহ
কার্বাইড সরঞ্জাম are preferred for efficient cutting and longer tool life.
High-speed steel (HSS) tools may be used at lower cutting speeds.
নিশ্চিত করুন কঠোর ফিক্সচারিং to reduce vibration and improve machining accuracy.
3. Cutting Conditions
Moderate to low cutting speeds are recommended to prevent overheating.
Use adequate coolant or lubrication to dissipate heat and reduce tool wear.
Employ proper feed rates and depth of cut to maintain surface quality.
4. Chip Formation
উৎপাদন করে long, ductile chips due to the austenitic structure.
ব্যবহার করুন chip breakers or controlled cutting techniques to manage chips effectively.
5. Applications Related to Machinability
Industrial components requiring high-temperature performance and corrosion resistance
Heat exchangers, boiler components, and furnace parts
Aerospace and automotive high-temperature components
Chemical processing equipment requiring precise machining
সারসংক্ষেপ
310H stainless steel has মধ্যম যন্ত্রচালনযোগ্যতা, with a high tendency to work harden. Using proper tooling, cutting conditions, and coolant ensures efficient machining and good surface finish. Its combination of machinability, high-temperature strength, and corrosion resistance makes it suitable for industrial, chemical, power generation, and high-temperature applications.
ক্ষয় প্রতিরোধ
Corrosion Resistance of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল এর জন্য পরিচিত চমৎকার ক্ষয় প্রতিরোধ ক্ষমতা, বিশেষ করে high-temperature and oxidizing environments. Its chemical composition ensures protection against various forms of corrosion while maintaining mechanical integrity under thermal stress.
১. সাধারণ ক্ষয় প্রতিরোধ
প্রতিরোধ করে অক্সিডেশন এবং স্কেলিং in air and industrial atmospheres at elevated temperatures.
ভালভাবে সম্পাদন করে মৃদু রাসায়নিক পরিবেশ.
দীর্ঘমেয়াদী প্রকাশের জন্য উপযুক্ত industrial, chemical, and petrochemical applications.
২. উচ্চ-তাপমাত্রার ক্ষয় প্রতিরোধ ক্ষমতা
Titanium stabilization and high chromium content help prevent সংবেদনশীলকরণ এবং আন্তঃকণিক ক্ষয় after welding or heat treatment.
সহ্য করতে পারে oxidizing environments at temperatures up to 1030°C (1885°F) continuous and 1100°C (2010°F) intermittent.
একটি স্থিতিশীল গঠন করে ক্রোমিয়াম অক্সাইড স্তর that protects against scaling and localized attack.
3. Resistance to Localized Corrosion
এর বিরুদ্ধে ভাল প্রতিরোধ crevice and pitting corrosion under oxidizing conditions.
Less suitable for chloride-rich environments at high temperatures, where stress corrosion cracking may occur.
4. Applications Related to Corrosion Resistance
Furnace and kiln components
Heat exchangers and boilers in chemical and petrochemical industries
High-temperature piping and tanks
Aerospace and automotive components exposed to oxidizing gases or exhaust
সারসংক্ষেপ
310H stainless steel offers চমৎকার ক্ষয় প্রতিরোধ ক্ষমতা, বিশেষ করে high-temperature and oxidizing environments. Titanium stabilization and high chromium content ensure resistance to intergranular corrosion and scaling, making 310H ideal for furnaces, boilers, heat exchangers, and industrial equipment exposed to extreme heat.
শীতল কাজের প্রক্রিয়া
Cold Working of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল সহ ভাল নমনীয়তা, allowing various cold working operations. Cold working increases strength through কাজের মাধ্যমে কঠোরতা অর্জন but requires careful handling due to the steel’s high-carbon and austenitic structure.
১. সাধারণ সর্দি কাজ করার প্রক্রিয়া
বক্রকরণ ও গঠন: Suitable for shaping furnace parts, heat exchangers, and piping.
রোলিং: Produces sheets, strips, and coils.
Deep Drawing and Stamping: Used for containers, trays, and intricate components.
Punching and Shearing: Applicable for industrial and chemical equipment components.
২. কাজের কঠোরীকরণ
310H stainless steel কাজ দ্রুত কঠিন হয়ে যায়, increasing tensile and yield strength during deformation.
Excessive cold working may reduce ductility.
মধ্যবর্তী অ্যানিলিং is recommended after extensive forming to restore ductility and relieve stresses.
৩. নির্মাণ সংক্রান্ত বিবেচনা
প্রয়োগ করুন ক্রমান্বয়ে বিকৃতি to avoid cracking or overstressing the material.
Use proper tooling, lubrication, and support to maintain surface finish and dimensional accuracy.
শীতল-প্রক্রিয়াজাত উপাদানগুলির প্রয়োজন হতে পারে চাপ মুক্তি if used in high-temperature or structural applications.
৪. ঠান্ডা কাজের সাথে সম্পর্কিত প্রয়োগসমূহ
Furnace components and heat treatment equipment
Industrial piping, tanks, and structural parts for chemical and petrochemical applications
Components requiring corrosion resistance and dimensional stability after forming
সারসংক্ষেপ
310H stainless steel exhibits good cold working characteristics, allowing bending, rolling, deep drawing, and stamping. Cold working improves strength through কাজের মাধ্যমে কঠোরতা অর্জন while maintaining corrosion resistance, making it suitable for furnaces, boilers, heat exchangers, and other industrial high-temperature applications.
তাপ চিকিৎসা
Heat Treatment of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল এর জন্য ডিজাইন করা হয়েছে উচ্চ-তাপমাত্রার প্রয়োগ. Its heat treatment is primarily aimed at relieving stresses, restoring ductility, and optimizing high-temperature performance, rather than increasing hardness, as austenitic stainless steels are প্রচলিত তাপ প্রক্রিয়াজাতকরণ দ্বারা কঠিনীকরণযোগ্য নয়.
১. দ্রবণ এনিলিং
উদ্দেশ্য: Restore ductility, relieve residual stresses from fabrication or welding, and maintain high-temperature strength.
তাপমাত্রার পরিসর: 1040–1120°C (1900–2050°F)
শীতলীকরণ: Rapid air or water quenching to preserve corrosion resistance and prevent sensitization.
২. মানসিক চাপ মুক্তি
উদ্দেশ্য: Reduce residual stresses from welding, cold working, or machining.
তাপমাত্রার পরিসর: ৪৫০–৬৫০°C (৮৪০–১২০০°F)
Enhances dimensional stability and reduces risk of stress-related cracking.
3. Effects of Heat Treatment
পুনরুদ্ধার করে নমনীয়তা এবং দৃঢ়তা in cold-worked or welded areas.
Relieves আভ্যন্তরীণ চাপ, improving high-temperature performance.
করে শক্তি উল্লেখযোগ্যভাবে বৃদ্ধি পায় না, as 310H is not precipitation-hardenable.
4. Surface Treatment Post Heat
আচার তৈরি বা নিষ্ক্রিয়করণ may be applied after heat treatment to remove scale or oxide layers and restore the protective chromium oxide surface.
৫. তাপ প্রক্রিয়াজাতকরণ সম্পর্কিত প্রয়োগসমূহ
Furnace and kiln components
Heat exchangers and boiler parts
Industrial piping and tanks exposed to high temperatures
Chemical, petrochemical, and power generation equipment requiring thermal stability
সারসংক্ষেপ
Heat treatment of 310H stainless steel focuses on সলিউশন এনিলিং এবং চাপ মুক্তি, বজায় রাখা ductility, corrosion resistance, and high-temperature performance. Proper heat treatment ensures reliable service in furnaces, boilers, heat exchangers, and other industrial high-temperature applications.
তাপ প্রতিরোধ ক্ষমতা
Heat Resistance of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল এর জন্য ডিজাইন করা হয়েছে excellent high-temperature strength and oxidation resistance. Its high carbon content provides enhanced ক্রীপ প্রতিরোধ ক্ষমতা for prolonged service at elevated temperatures.
১. ধারাবাহিক সেবা তাপমাত্রা
Suitable for continuous service in oxidizing atmospheres up to 1030°C (1885°F).
রক্ষণাবেক্ষণ করে mechanical strength, creep resistance, and corrosion resistance উচ্চ তাপমাত্রায়।.
২. বিচ্ছিন্ন সংস্পর্শ
Can withstand short-term or intermittent exposure up to 1100°C (2010°F) without significant scaling or degradation.
যে উপাদানগুলো উন্মুক্ত থাকে সেগুলোর জন্য উপযুক্ত তাপীয় চক্রায়ন অথবা ওঠানামা করা উচ্চ তাপমাত্রা।.
3. Oxidation and Scaling Resistance
একটি স্থিতিশীল গঠন করে ক্রোমিয়াম অক্সাইড স্তর that protects against oxidation and scaling.
Titanium stabilization and high chromium content prevent সংবেদনশীলকরণ and intergranular corrosion after welding or high-temperature service.
৪. সীমাবদ্ধতা
Not recommended for prolonged exposure to high-chloride environments, where stress corrosion cracking may occur.
Extreme thermal shocks should be avoided to prevent thermal fatigue.
৫. তাপ প্রতিরোধ সংক্রান্ত প্রয়োগসমূহ
Furnace and kiln components
Heat exchangers, boilers, and thermal processing equipment
Petrochemical and chemical industry high-temperature piping and tanks
Aerospace and automotive components exposed to extreme heat
সারসংক্ষেপ
310H stainless steel provides চমৎকার তাপ প্রতিরোধ ক্ষমতা, maintaining strength, creep resistance, and corrosion resistance at elevated temperatures up to 1030°C continuous and 1100°C intermittent. Its combination of oxidation resistance and high-temperature performance makes it ideal for industrial, chemical, petrochemical, and high-temperature applications.
গরম কাজ
Hot Working of 310H Stainless Steel
310H stainless steel হল একটি উচ্চ-কার্বনযুক্ত অস্টেনাইটিক স্টেইনলেস স্টীল অসাধারণের সাথে high-temperature strength and oxidation resistance. Hot working allows the steel to be shaped and formed at elevated temperatures while minimizing কাজের মাধ্যমে কঠোরতা অর্জন and preserving mechanical and corrosion-resistant properties.
১. প্রস্তাবিত গরম কাজের তাপমাত্রা
Hot working range: ১১৫০–৯০০°C (২১০০–১৬৫০°F).
Maintaining proper temperature prevents দানা বৃদ্ধি, ensures uniform mechanical properties, and preserves high-temperature performance.
২. গরম কাজের প্রক্রিয়া
গরম রোলিং: Produces sheets, plates, and strips with uniform thickness.
ঢালাই: Suitable for structural and high-temperature components.
এক্সট্রুশন: Allows production of rods, tubes, and complex profiles.
Hot Forming and Pressing: Enables shaping of large or intricate parts with minimal cracking risk.
৩. গরম কাজের সুবিধা
হ্রাস করে কাজের মাধ্যমে কঠোরতা অর্জন ঠান্ডা কাজের তুলনায়।.
উন্নতি করে ductility, toughness, and formability.
Allows production of large, thick, or complex components for high-temperature service.
৪. হট ওয়ার্কিং পরবর্তী প্রক্রিয়াকরণ
অ্যানিলিং may be applied to relieve residual stresses and restore uniform mechanical properties.
আচার তৈরি বা নিষ্ক্রিয়করণ improves surface corrosion resistance after hot working.
৫. গরম কাজের সাথে সম্পর্কিত প্রয়োগসমূহ
Furnace and kiln components
Boilers, heat exchangers, and high-temperature piping
Industrial equipment for chemical and petrochemical processes
Aerospace and automotive parts requiring high-temperature performance
সারসংক্ষেপ
310H stainless steel exhibits excellent hot working characteristics, allowing forging, rolling, extrusion, and forming at ১১৫০–৯০০°সেলসিয়াস. Hot working enhances ductility, reduces work hardening, and enables the production of parts for furnaces, boilers, heat exchangers, and industrial high-temperature applications.