Aluminium, Commercial Alloy
6026 T9 Bar
Tin free aluminium alloy machining bar recently developed to meet European Environmental Protection Directives.
Aluminium alloy 6026 is a recently developed alloy meeting the following European Environmental Protection Directives:
- 2000/53/CE-ELV – For the automotive sector
- 2002/95/CE-RoHS – For the electrical and electronics sector
Alloy 6026 does not contain Tin (Sn) which can cause weakness and cracking of machined parts when subjected to stress and high temperature. Alloy 6026 is a good alternative to alloys 6061 and 6082. Extruded bars in alloy 6026 have the same minimum tensile strength as alloys 2011 & 2030.
DOWNLOAD PDF
Range
PLEASE NOTE
If you do not see what you are looking for, please contact your local service centre with your specific requirements.
6026 T9 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA / International | 6026-T9 |
| UNS | International | A96026 (6026-T9) |
| EN / DIN | Europe | EN AW-6026-T9 |
| EN Name | Europe | AlMgSiBi-T9 |
Properties
Chemical Composition
6026 T9
| Chemical Element | % Present |
| Manganese (Mn) | 0.20 - 1.00 |
| Iron (Fe) | 0.00 - 0.70 |
| Magnesium (Mg) | 0.60 - 1.20 |
| Silicon (Si) | 0.60 - 1.40 |
| Copper (Cu) | 0.20 - 0.50 |
| Lead (Pb) | 0.00 - 0.40 |
| Bismuth (Bi) | 0.50 - 1.50 |
| Zinc (Zn) | 0.00 - 0.30 |
| Tin (Sn) | 0.00 - 0.05 |
| Chromium (Cr) | 0.00 - 0.30 |
| Titanium (Ti) | 0.00 - 0.20 |
| Other (Each) | 0.00 - 0.05 |
| Others (Total) | 0.00 - 0.15 |
| Aluminium (Al) | Balance |
Mechanical Properties
Extruded and Drawn Bar
6026 T9
| Mechanical Property | Value |
| Proof Stress | 330 Min MPa |
| Tensile Strength | 360 Min MPa |
| Elongation A50 mm | 4 Min % |
| Hardness Brinell | 95 Min HB |
| Mechanical Property | Value |
| Proof Stress | 330 Min MPa |
| Tensile Strength | 360 Min MPa |
| Elongation A50 mm | 4 % |
| Hardness Brinell | 95 Min HB |
General Physical Properties
| Physical Property | Value |
| Density | 2.72 g/cm³ |
| Thermal Expansion | 23.4 x 10^-6 /K |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 172 W/m.K |
| Electrical Resistivity | 0.039 x 10^-6 Ω .m |
Applications
- Machined parts especially on high speed automatic lathes
- Hard anodising
- Hot forging
- Automotive components such as brake systems
- Electrical & electronic parts
Characteristics
- Excellent corrosion resistance
- Suitable for anodising to provide both decorative and hard anodised finishes
- Good alternative to alloys 6061 and 6082
- Extruded Bars in alloy 6026 have the same minimum tensile strength as alloys 2011 & 2030
- Good weldability
- 6026 can be used in place of alloys 6082 or 6081, especially where the finished parts require extensive machining on high speed automtatic lathes and machining centres
Additional Information
Machinability
- 6026 can be used in place of alloys 6082 or 6081, especially where the finished parts require extensive machining on high speed automtatic lathes and machining centres.
Weldability
- Weldability of alloy 6026 is good.