Aluminium, Commercial Alloy
4015 H14 Sheet
High quality general purpose aluminium alloy.
Aluminium alloy 4015 is a high quality general purpose alloy. It is a close relation to 3103 AlMn alloy, but with a higher silicon content.
This alloy can be welded, anodized* or painted. (*It should be noted that the anodized finish of alloy 4015 will be much darker and less reflective that on alloys 1050 or 3103 so this is not recommended for decorative applications).
Many users now prefer to use alloy 4015 having switched from other alloys such as 1050 and 3103.
Please note that the mechanical properties quoted are for H14 temper.
DOWNLOAD PDF
Range
PLEASE NOTE
If you do not see what you are looking for, please contact your local service centre with your specific requirements.
4015 H14 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA | 4015-H14 |
| UNS | International | A94015 (4015-H14) |
| EN / DIN | Europe | EN AW-4015-H14 |
| EN Name | Europe | AlSi2Mn-H14 |
Properties
Chemical Composition
Alloy 4015
| Chemical Element | % Present |
| Iron (Fe) | 0.00 - 0.70 |
| Copper (Cu) | 0.00 - 0.20 |
| Magnesium (Mg) | 0.10 - 0.50 |
| Silicon (Si) | 1.40 - 2.20 |
| Zinc (Zn) | 0.00 - 0.20 |
| Manganese (Mn) | 0.60 - 1.20 |
| Other (Each) | 0.00 - 0.05 |
| Others (Total) | 0.00 - 0.15 |
| Aluminium (Al) | Balance |
Mechanical Properties
Sheet 0.2mm to 3.00mm
| Mechanical Property | Value |
| Tensile Strength | 150 - 200 MPa |
| Proof Stress | 120 Min MPa |
| Hardness Brinell | 50 HB |
General Physical Properties
| Physical Property | Value |
| Density | 2.72 g/cm³ |
| Melting Point | 600 °C |
| Thermal Expansion | 24 x 10-6/K |
| Modulus of Elasticity | 70 GPa |
| Thermal Conductivity | 150-200 W/m.K |
| Electrical Resistivity | 0.023-0.029 x 10-6 Ω .m |
Applications
- Industry application include:
- Building
- Food
- Transport
- Packaging
Characteristics
- Good ductility
- Good mechanical strength
- Similar corrosion resistance to the 3000 series alloys
- Suitable for most applications in mill finish or painted
- Not recommended for use in aggressive environments
Additional Information
Fabrication
Corresponds to alloy 3103 in same temper but may not be a direct equivalent.
r/t performance dependent upon thickness – approx figures for H12 r/t min bend radius for 180 degree bend are shown below:
Thickness
0.5-0.8mm: r/t 0.0
0.8-1.5mm: r/t 1.0
1.5-3.0mm: r/t 2.0
| Process | Rating |
| Workability Cold | Very Good |
| Machinability | Acceptable |
| Weldability - Gas | Very Good |
| Weldability - Arc | Very Good |
| Weldability - Resistance | Good |
| Brazability | Very Good |
| Solderability | Very good |
Weldability
Suitable for MIG and TIG welding using normal aluminium welding conditions. Recommended welding wire is 4043 (Al Si5).