Rostfreier Stahl, austenitisch
S310S Stainless Steel (31008) Sheet and Plate
A low carbon version of grade 310 that is less prone to embrittlement and sensitization in service.
An austenitic chromium nickel grade, Alloy 310S displays excellent oxidation resistance up to 1094°C
Alloy 310S displays excellent resistance to oxidation under mildly cyclic conditions. As a result of its high chromium and nickel content, alloy 310S has good resistance to sulphidation and other forms of hot corrosion.
Combined with its low carbon content, the metal is also effective at resisting embrittlement. The metal is commonly utilized in extreme conditions, such as furnace manufacturing and heat treating equipment.
While both hot and work practices can be applied, cold working is not commonly done on stainless steel 310S; however, it is the only way to work harden the metal. This resistance to cold temperatures is useful in cryogenic environments, as 310S is incredibly tough. However, it can be subject to thermal shock and therefore should be treated and hot-worked with care.
310S is widely used in industrielle Hochtemperaturanwendungen where both strength and corrosion resistance are required, such as Öfen, Wärmetauscher und Wärmebehandlungsanlagen.
DOWNLOAD PDF
Bereich
BITTE BEACHTEN
Wenn Sie nicht finden, wonach Sie suchen, wenden Sie sich bitte an Ihren lokales Servicezentrum mit Ihren spezifischen Anforderungen.
S310S Stainless Steel Related Specifications
| System / Standard | Land / Region | Besoldungsgruppe/Bezeichnung |
| AISI | USA | 310S |
| UNS | International | S31008 |
| AISI (related) | USA | 310 (standard carbon, UNS S31000) |
| DE / W.Nr. | Europa | 1.4845 |
| DE Name | Europa | X8CrNi25-21 |
| ASTM A240 | USA | 310 / 310S (plate, sheet, strip) |
| ASTM A276 | USA | 310 / 310S (bars, shapes) |
| ASTM A213 | USA | TP310S (boiler / HX tubes) |
| ASTM A312 | USA | TP310S (seamless pipe) |
| GB | China | 06Cr25Ni20 |
| JIS | Japan | SUS310S |
Eigenschaften
Chemische Zusammensetzung
S31008 Plate
ASTM A240
| Chemisches Element | % Geschenk |
| Kohlenstoff (C) | 0.00 - 0.08 |
| Chrom (Cr) | 24.00 - 26.00 |
| Nickel (Ni) | 19.00 - 22.00 |
| Mangan (Mn) | 0.00 - 2.00 |
| Phosphor (P) | 0.00 - 0.04 |
| Schwefel (S) | 0.00 - 0.03 |
| Silizium (Si) | 0.00 - 1.50 |
| Eisen (Fe) | Bilanz |
Mechanische Eigenschaften
Sheet and Plate
ASTM A240
| Mechanische Eigenschaften | Wert |
| Nachweis von Stress | 205 Min MPa |
| Zugfestigkeit | 515 Min MPa |
| Dehnung A50 mm | 40 Min % |
Applications of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel mit excellent high-temperature oxidation and corrosion resistance. Its low carbon content improves weldability and minimizes the risk of sensitization, making it ideal for industrial applications requiring both high-temperature strength and corrosion resistance.
1. Industrielle Anwendungen im Hochtemperaturbereich
Ofenkomponenten wie zum Beispiel Retorten, Tabletts und Körbe
Ofenteile und Wärmebehandlungsanlagen
Kessel- und Wärmetauscherteile, die über längere Zeit hohen Temperaturen ausgesetzt sind
Thermische Prozessanlagen in der chemischen, petrochemischen und Energieindustrie
2. Petrochemische und chemische Industrie
Rohrleitungen, Tanks und Behälter für chemische Prozesse bei hohen Temperaturen
Bauteile, die mit oxidierenden Gasen oder Hochtemperaturdämpfen umgehen
Industrial reactors and processing equipment under thermal stress
3. Andere Anwendungen
Komponenten für die Luft- und Raumfahrt und die Automobilindustrie, die hohen Temperaturen ausgesetzt sind
Verbrennungsanlagen und Brennkammern
Hochtemperaturbauteile in Industriemaschinen
Zusammenfassung
310S stainless steel is widely used in applications requiring high-temperature strength, oxidation resistance, and corrosion resistance. Seine austenitic, low-carbon structure macht es geeignet für Öfen, Heizkessel, Wärmetauscher, chemische Anlagen und Industriemaschinen ausgesetzt extreme Hitze und oxidierende Umgebungen.
Characteristics of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel bekannt für seine excellent high-temperature oxidation and corrosion resistance. Its low carbon content makes it particularly suitable for welding and fabrication in high-temperature environments.
1. High-Temperature Resistance
Maintains strength and structural integrity at elevated temperatures.
Widersteht Oxidation und Verzunderung in continuous service up to approximately 1020°C (1870°F).
Suitable for intermittent exposure to temperatures up to 1100°C (2010°F).
2. Corrosion Resistance
Good general corrosion resistance in oxidizing atmospheres.
Gut geeignet für milde chemische Umgebungen.
Low carbon content reduces the risk of Sensibilisierung und interkristalline Korrosion, especially in welded components.
3. Mechanical Properties
Excellent ductility and toughness at both high and low temperatures.
Stable austenitic structure ensures consistent performance under thermal stress.
4. Fabrication and Weldability
Easily fabricated and welded due to low carbon content.
Can be cold worked and formed into complex shapes without losing corrosion resistance.
5. Applications Related to Characteristics
Furnace components, kilns, and heat treatment equipment
Kessel, Wärmetauscher und thermische Verarbeitungsmaschinen
Industrial piping and storage tanks exposed to high temperatures
Hochtemperaturkomponenten für die Luft- und Raumfahrt und die Automobilindustrie
Zusammenfassung
310S stainless steel is characterized by high-temperature strength, excellent oxidation and corrosion resistance, and good weldability. Seine austenitic, low-carbon structure macht es ideal für industrial, chemical, and high-temperature applications where both durability and corrosion resistance are essential.
Zusätzliche Informationen
Fabrikation
Fabrication of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel bekannt für seine excellent high-temperature oxidation and corrosion resistance. Its low carbon content enhances weldability and resistance to sensitization, making it suitable for a wide range of fabrication processes.
1. Bildung von
Kaltbearbeitung:
Can be bent, drawn, or rolled, but work hardens rapidly.
Bei umfangreichen Umformungen kann eine Zwischenglühung erforderlich sein, um die Duktilität wiederherzustellen.
Heißes Arbeiten:
Recommended temperature range: 1150-900°C (2100-1650°F).
Suitable for forging, hot rolling, and extrusion of thick or complex parts.
2. Schweißen
Easily welded using conventional methods: TIG, MIG, SMAW, and FCAW.
Low carbon content reduces the risk of Sensibilisierung and intergranular corrosion.
Filler metals: Typically 310S or 310 grades to maintain corrosion resistance and high-temperature performance.
Post-weld pickling or passivation may be applied to restore surface protection.
3. Bearbeitung
Bearbeitbarkeit ist mäßig, with rapid work hardening tendencies.
Verwenden Sie scharfe Hartmetallwerkzeuge, appropriate feed rates, and coolants for efficient cutting.
4. Behandlungen nach der Fertigstellung
Glühen: Stellt die Duktilität wieder her und baut Spannungen ab, die durch Kaltbearbeitung oder Schweißen entstanden sind.
Beizen oder Passivieren: Removes scale or oxide layers to restore corrosion resistance.
5. Anwendungen im Zusammenhang mit der Fabrikation
Ofenkomponenten, Wärmebehandlungsanlagen und Ofenteile
Kessel, Wärmetauscher und Hochtemperatur-Rohrleitungen
Chemical and petrochemical processing equipment
Aerospace and automotive components requiring high-temperature performance
Zusammenfassung
310S stainless steel is highly fabricable using conventional forming, welding, and machining techniques. Its low-carbon austenitic structure ensures excellent weldability, corrosion resistance, and high-temperature performance, making it suitable for industrial, chemical, and high-temperature applications.
Schweißeignung
Weldability of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel mit excellent high-temperature oxidation and corrosion resistance. Seine low carbon content enhances weldability and reduces the risk of sensitization, making it suitable for various welding processes.
1. Welding Methods
Kann mit den üblichen Schmelzschweißverfahren geschweißt werden:
WIG (GTAW) – for precision and clean welds
MIG (GMAW) – for faster, efficient welding
SMAW (Stick Welding) – for general fabrication
FCAW (Lichtbogenschweißen mit Füllung) – suitable for thicker sections
2. Welding Considerations
Low carbon content minimizes interkristalline Korrosion risk after welding.
Preheating is usually Nicht erforderlich, except for very thick sections to reduce distortion.
Richtig Schweißzusatzwerkstoffe (typically 310S or 310) are recommended to maintain high-temperature strength and corrosion resistance.
3. Post-Weld Treatments
Lösungsglühen is sometimes applied for high-temperature service to restore ductility and relieve stresses.
Beizen und Passivieren can remove oxides and enhance corrosion resistance of welded areas.
4. Anwendungen im Zusammenhang mit der Schweißbarkeit
Komponenten von Öfen und Brennöfen
Kessel, Wärmetauscher und Hochtemperatur-Rohrleitungen
Chemical and petrochemical processing equipment
Industrial structures exposed to high temperatures
Zusammenfassung
310S stainless steel has ausgezeichnete Schweißbarkeit due to its low-carbon austenitic structure, allowing it to be joined using conventional welding techniques. Proper welding ensures strong, corrosion-resistant, and high-temperature capable joints, making it suitable for Öfen, Heizkessel, Wärmetauscher und industrielle Hochtemperaturanwendungen.
Bearbeitbarkeit
Machinability of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel mit hervorragenden high-temperature corrosion and oxidation resistance. Like most austenitic stainless steels, it exhibits mäßige Bearbeitbarkeit, primarily due to its high work-hardening tendency.
1. Arbeitsverhärtung
310S stainless steel Arbeit härtet schnell, especially under light cuts or interrupted machining.
Excessive work hardening can lead to Werkzeugverschleiß, schlechte Oberflächengüte und Maßungenauigkeiten.
Verwenden Sie scharfe Schneidwerkzeuge and maintain consistent feed and speed to minimize work hardening.
2. Empfehlungen für die Werkzeugausstattung
Hartmetall-Werkzeuge werden für effizientes Schneiden und längere Werkzeugstandzeiten bevorzugt.
High-speed steel (HSS) tools can be used at lower cutting speeds.
Rigid workholding is recommended to reduce vibration and chatter.
3. Schnittbedingungen
Mäßige bis niedrige Schnittgeschwindigkeiten to avoid overheating and maintain surface finish.
Ausreichend Kühlmittel oder Schmierung helps reduce heat buildup and extends tool life.
Steuerung feed rates and depth of cut to maintain dimensional accuracy and prevent work hardening.
4. Chip-Bildung
Erzeugt lange, dehnbare Späne due to its austenitic structure.
Verwenden Sie chip breakers or controlled cutting Chips effektiv zu verwalten.
5. Anwendungen im Zusammenhang mit der Bearbeitbarkeit
Industrielle Komponenten, die high-temperature corrosion resistance
Heat exchangers, furnace components, and boiler parts
Hochtemperaturkomponenten für die Luft- und Raumfahrt und die Automobilindustrie
Chemical processing equipment requiring precision machining
Zusammenfassung
310S stainless steel has mäßige Bearbeitbarkeit, with a tendency to work harden quickly. Using appropriate tooling, cutting conditions, and coolant, efficient machining and good surface finish can be achieved. Its combination of Bearbeitbarkeit, Hochtemperaturfestigkeit und Korrosionsbeständigkeit macht es geeignet für industrial, chemical, and high-temperature applications.
Korrosionsbeständigkeit
Corrosion Resistance of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel mit excellent corrosion and oxidation resistance, insbesondere in high-temperature environments. Its low carbon content reduces the risk of Sensibilisierung, making it ideal for welded and high-temperature applications.
1. High-Temperature Corrosion Resistance
Ausgezeichnete Beständigkeit gegen Oxidation und Verzunderung bei erhöhter Temperatur.
Can withstand continuous service in oxidizing atmospheres up to 1020°C (1870°F) und intermittierende Exposition bis zu 1100°C (2010°F).
Bildet einen stabilen Chromoxidschicht that protects the surface from scaling and degradation.
2. General Corrosion Resistance
Gute Beständigkeit gegen milde chemische Umgebungen and oxidizing media.
Geringer Kohlenstoffgehalt verhindert Sensibilisierung, reducing the risk of interkristalline Korrosion in welded sections.
3. Beständigkeit gegen örtliche Korrosion
Performs well against Spalt- und Lochfraßkorrosion in oxidizing conditions.
Weniger geeignet für chloridhaltige Umgebungen bei hohen Temperaturen, wo Spannungsrisskorrosion auftreten kann.
4. Anwendungen im Zusammenhang mit der Korrosionsbeständigkeit
Komponenten von Öfen und Brennöfen
Wärmetauscher und Kesselteile
Industrial piping and tanks in chemical and petrochemical industries
Hochtemperaturkomponenten für die Luft- und Raumfahrt und die Automobilindustrie
Zusammenfassung
310S stainless steel offers ausgezeichnete Korrosionsbeständigkeit, besonders in oxidizing and high-temperature environments. Seine low-carbon, austenitic structure ensures resistance to interkristalline Korrosion, making it ideal for Öfen, Heizkessel, Wärmetauscher und Industrieanlagen exposed to high temperatures.
Kaltbearbeitung
Cold Working of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel mit gute Duktilität, und ermöglicht verschiedene Kaltbearbeitungsvorgänge. Its low carbon content helps maintain corrosion resistance during forming, but like other austenitic steels, it exhibits Kaltverfestigung.
1. Gemeinsame Kaltverarbeitungsprozesse
Biegen und Umformen: Suitable for sheets, trays, piping, and structural components.
Rollend: Produces strips, sheets, and coils for industrial and high-temperature applications.
Tiefziehen und Stanzen: Used for complex shapes in furnace components or chemical equipment.
Stanzen und Scheren: Suitable for components requiring precision cutting.
2. Arbeitsverhärtung
310S stainless steel Arbeit härtet schnell, increasing tensile strength but reducing ductility.
Intermediate annealing may be required after extensive forming to restore ductility and relieve stresses.
3. Erwägungen zur Fabrikation
Anwenden allmähliche Verformung um Risse oder eine Überbeanspruchung des Materials zu vermeiden.
Ordnungsgemäße Verwendung tooling, lubrication, and support to maintain dimensional accuracy and surface finish.
Kaltverformte Komponenten erfordern möglicherweise Stressabbau if used in high-temperature service.
4. Anwendungen im Zusammenhang mit der Kaltumformung
Ofenkomponenten und Wärmebehandlungsanlagen
Industrial piping, tanks, and structural parts for chemical and petrochemical industries
Bauteile, die nach dem Umformen Korrosionsbeständigkeit und Maßhaltigkeit erfordern
Zusammenfassung
310S stainless steel exhibits gute Kaltverformungseigenschaften, allowing bending, rolling, deep drawing, and stamping. Cold working increases strength through Kaltverfestigung unter Beibehaltung der Korrosionsbeständigkeit, so dass es geeignet ist für industrial, chemical, and high-temperature applications.
Wärmebehandlung
Heat Treatment of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel konzipiert für hohe Temperaturen und oxidierende Umgebungen. As an austenitic stainless steel, it is nicht härtbar durch konventionelle Wärmebehandlung. Wärmebehandlung wird hauptsächlich verwendet, um relieve stresses, restore ductility, and maintain corrosion resistance.
1. Lösungsglühen
Zweck: Restore ductility, relieve residual stresses from cold working or welding, and maintain corrosion resistance.
Temperaturbereich: 1010–1120°C (1850–2050°F)
Kühlung: Rapid air or water quenching to prevent carbide precipitation and maintain corrosion resistance.
2. Stressabbau
Zweck: Reduce residual stresses from welding, machining, or forming.
Temperaturbereich: 450-650°C (840-1200°F)
Verbessert Formbeständigkeit and reduces risk of stress-related cracking in service.
3. Auswirkungen der Wärmebehandlung
Stellt wieder her. Duktilität und Zähigkeit in kaltverformten oder geschweißten Bereichen.
Entlastet innere Spannungen, zur Verbesserung der Leistung bei hohen Temperaturen.
Unterhält Korrosionsbeständigkeit, especially in welded components.
4. Surface Treatments Post Heat
Beizen oder Passivieren may be applied after heat treatment to remove scale, oxides, or discoloration and restore the protective chromium oxide layer.
5. Anwendungen im Zusammenhang mit der Wärmebehandlung
Komponenten von Öfen und Brennöfen
Wärmetauscher und Kesselteile
Industrielle Rohrleitungen und Tanks, die hohen Temperaturen ausgesetzt sind
Chemical and petrochemical processing equipment
Zusammenfassung
Heat treatment of 310S stainless steel focuses on Lösungsglühen und Spannungsabbau, Beibehaltung Duktilität, Korrosionsbeständigkeit und Hochtemperaturverhalten. Eine ordnungsgemäße Wärmebehandlung gewährleistet einen zuverlässigen Betrieb in Öfen, Heizkessel, Wärmetauscher und andere industrielle Hochtemperaturanwendungen.
Hitzebeständigkeit
Heat Resistance of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel konzipiert für excellent high-temperature strength, oxidation, and scaling resistance. Its chemical composition ensures performance in continuous and intermittent high-temperature service.
1. Kontinuierliche Betriebstemperatur
Geeignet für continuous service in oxidizing atmospheres up to 1020°C (1870°F).
Unterhält mechanical strength, creep resistance, and oxidation resistance bei erhöhter Temperatur.
2. Intermittierende Exposition
Vertragen short-term or intermittent exposure up to 1100°C (2010°F).
Ideal for components subjected to thermal cycling or fluctuating high temperatures.
3. Oxidations- und Verzunderungsbeständigkeit
Bildet einen stabilen Chromoxidschicht on the surface, protecting against scaling and corrosion.
Low carbon content reduces the risk of Sensibilisierung und interkristalline Korrosion, even after welding or high-temperature service.
4. Beschränkungen
Not recommended for high-chloride or highly reducing environments at elevated temperatures, as stress corrosion cracking may occur.
Extreme Temperaturschocks sollten vermieden werden, um zu verhindern thermische Ermüdung.
5. Anwendungen im Zusammenhang mit der Hitzebeständigkeit
Komponenten von Öfen und Brennöfen
Heat exchangers, boilers, and high-temperature piping
Industrial equipment in chemical and petrochemical industries
Aerospace and automotive parts exposed to extreme heat
Zusammenfassung
310S stainless steel offers ausgezeichnete Hitzebeständigkeit, maintaining strength, creep resistance, and oxidation protection at temperatures up to 1020°C continuous und 1100°C intermittent. Seine low-carbon austenitic structure ensures reliable performance in Öfen, Heizkessel, Wärmetauscher und industrielle Hochtemperaturanwendungen.
Heißarbeit
Hot Working of 310S Stainless Steel
310S stainless steel ist eine low-carbon, austenitic stainless steel mit hervorragenden high-temperature corrosion and oxidation resistance. Hot working enables shaping and forming while minimizing Kaltverfestigung and maintaining the steel’s mechanical and corrosion-resistant properties.
1. Empfohlene Warmarbeitstemperatur
Warmarbeitsbereich: 1150-900°C (2100-1650°F).
Proper temperature control prevents Kornwachstum and ensures uniform mechanical properties.
2. Warmarbeitsprozesse
Warmwalzen: Produziert Bleche, Platten und Streifen mit gleichmäßiger Dicke.
Schmieden: Suitable for structural or high-temperature components.
Strangpressen: Ermöglicht die Herstellung von Stangen, Rohren und komplexen Profilen.
Warmumformung und Pressen: Ermöglicht die Formgebung großer oder komplizierter Teile mit minimalem Rissrisiko.
3. Vorteile der Warmumformung
Reduziert Kaltverfestigung im Vergleich zur Kaltbearbeitung.
Verbessert Duktilität, Zähigkeit und Umformbarkeit.
Ermöglicht die Herstellung von große, dicke oder komplexe Bauteile suitable for high-temperature service.
4. Behandlungen nach der Warmarbeit
Glühen angewendet werden, um Eigenspannungen abzubauen und einheitliche mechanische Eigenschaften wiederherzustellen.
Beizen oder Passivieren can enhance surface corrosion resistance after hot working.
5. Anwendungen im Zusammenhang mit der Warmarbeit
Komponenten von Öfen und Brennöfen
Kessel, Wärmetauscher und Hochtemperatur-Rohrleitungen
Industrielle Ausrüstung für chemische und petrochemische Prozesse
Teile für die Luft- und Raumfahrt und die Automobilindustrie, die eine hohe Temperaturleistung erfordern
Zusammenfassung
310S stainless steel exhibits hervorragende Heißverarbeitungseigenschaften, die das Schmieden, Walzen, Strangpressen und Umformen bei 1150-900°C. Hot working improves ductility, reduces work hardening, and enables production of components for Öfen, Heizkessel, Wärmetauscher und industrielle Hochtemperaturanwendungen.