Aluminium, ASTM & FED-QQ
QQ-A-200/11 T6511 Bar & Extrusion
Very high strength aerospace aluminium alloy.
A very high strength aerospace aluminium alloy with, depending upon temper, yield strength of 24-68 ksi (165 – 465 MPa) and tensile strength of 40-78 ksi (275 – 540 MPa).
This alloy is used where high strength is required and where good resistance to general corrosion is NOT important.
DOWNLOAD PDF
Range
PLEASE NOTE
If you do not see what you are looking for, please contact your local service centre with your specific requirements.
QQ-A-200/11 T6511 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA | 7075-T6511 |
| UNS | International | A97075 (7075-T6511) |
| EN / DIN | Europe | EN AW-7075-T6511 / 3.4365 |
| EN Name | Europe | AlZn5.5MgCu-T6511 |
| ASTM B221 | USA | 7075-T6511 extruded bar, rod, shapes & tube |
| BS (Aerospace) | UK | L95-T6511 (7075-T6511 high-strength extrusions) |
| AFNOR | France | A-Z5GU-T6511 |
Properties
Chemical Composition
Alloy QQ A 200/11
SAE AMS QQ-A-200/11
| Chemical Element | % Present |
| Silicon (Si) | 0.00 - 0.40 |
| Iron (Fe) | 0.00 - 0.50 |
| Copper (Cu) | 1.20 - 2.00 |
| Manganese (Mn) | 0.00 - 0.30 |
| Chromium (Cr) | 0.18 - 0.28 |
| Magnesium (Mg) | 2.10 - 2.90 |
| Zinc (Zn) | 5.10 - 6.10 |
| Titanium (Ti) | 0.00 - 0.20 |
| Other (Each) | 0.00 - 0.05 |
| Others (Total) | 0.00 - 0.15 |
| Aluminium (Al) | Balance |
General Physical Properties
| Physical Property | Value |
| Density | 2.81 g/cm³ |
| Melting Point | 635 °C |
| Thermal Expansion | 23.5 x 10-6/K |
| Modulus of Elasticity | 72 GPa |
| Thermal Conductivity | 134-160 W/m.K |
| Electrical Resistivity | 40 % IACS |
Applications
- Aerospace components
- High technology applications
- Defence components
Characteristics
- High strength
- Very good machinability
- Weldable using resistancce, spot & beam methods
- Poor resistance to atmospheric corrosion
Additional Information
Mechanical Properties
These mechanical properties are for bar in the T6511 temper.
| Diameter (mm) | Proof Strength (Min) | Tensile Strength (Min) | Elongation % (Min) |
| Up to & incl. 6.3 | 482 | 538 | 7 |
| Over 6.3 up to & incl. 12.7 | 503 | 558 | 7 |
| Over 12.7 up to & incl. 76.2 | 496 | 558 | 7 |
| Over 76.2 up to & incl. 114 | 489 | 558 | 7 |
| Over 114 up to & incl. 127 | 469 | 538 | 6 |