6101A T6 Bar & Extrusion
Paduan aluminium tempa yang dapat diolah dengan panas yang digunakan dalam pembuatan dan konstruksi komponen dan peralatan distribusi daya listrik.
6101A aluminum is a 6000-series aluminum alloy: There is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. Cited properties are appropriate for the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements.
6101A is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6101A. AlMgSi(A) is the EN chemical designation.
UNDUH PDF
Jangkauan
HARAP DICATAT
Jika Anda tidak melihat apa yang Anda cari, silakan hubungi pusat layanan lokal dengan kebutuhan spesifik Anda.
6101A T6 Aluminium Related Specifications
| Sistem / Standar | Negara / Wilayah | Kelas / Peruntukan |
| AA | AMERIKA SERIKAT | 6101-T6 (electrical conductor alloy, equivalent to 6101A-T6 in use) |
| UNS | Internasional | A96101 (6101 series, used for 6101/6101A in T6 tempers) |
| EN / DIN | Eropa | EN AW-6101A-T6 |
| EN Nama | Eropa | AlMgSi-T6 (6101A) |
Properti
Komposisi Kimia
6101A
| Elemen Kimia | % Hadir |
| Tembaga (Cu) | 0.00 - 0.05 |
| Besi (Fe) | 0.00 - 0.40 |
| Magnesium (Mg) | 0.40 - 0.90 |
| Lainnya (Masing-masing) | 0.00 - 0.03 |
| Lainnya (Total) | 0.00 - 0.10 |
| Silikon (Si) | 0.30 - 0.70 |
Sifat Mekanis
Extruded Bar Up to 150mm
6101A
| Properti Mekanis | Nilai |
| Stres Bukti | 170 Min MPa |
| Perpanjangan A50 mm | 8 Menit % |
| Kekuatan Tarik | 200 Min N/mm2 |