ອາລູມິນຽມ, ໂລຫະປະສົມທາງການຄ້າ
2011 T6 Bar
High mechanical strength alloy that machines exceptionally well.
Often called a free machining alloy or ‘FMA’ it is well suited to use in automatic lathes.
ດາວໂຫຼດ PDF
ຂອບເຂດ
| Product Form | Imperial Sizes | Metric Sizes |
| Round Bar | 3⁄16"- 16" | 6mm - 50mm |
ກະລຸນາຮັບຊາບ
ຖ້າທ່ານບໍ່ເຫັນສິ່ງທີ່ທ່ານກຳລັງຊອກຫາ, ກະລຸນາຕິດຕໍ່ຫາທ່ານ ສູນບໍລິການທ້ອງຖິ່ນ ກັບຄວາມຕ້ອງການສະເພາະຂອງທ່ານ.
2011 T6 Aluminium Related Specifications
| ລະບົບ / ມາດຕະຖານ | ປະເທດ / ພາກພື້ນ | ຊັ້ນ / ຕຳແໜ່ງ |
| AA | ສະຫະລັດອາເມລິກາ | 2011-T6 |
| ສະຫະປະຊາຊາດ | ສາກົນ | A92011 (2011-T6) |
| ອັງກິດ / DIN | ເອີຣົບ | EN AW-2011 / 3.1655 (T6) |
| ຊື່ EN | ເອີຣົບ | AlCu6BiPb – T6 |
| ASTM B211 | ສະຫະລັດອາເມລິກາ | 2011-T6 bar, rod, wire |
| GB | ຈີນ | 2A01-T6 |
| ຈີໄອເອສ | ຍີ່ປຸ່ນ | A2011-T6 |
| ບີເອສ | ອັງກິດ | FC1 (2011-T6 bar) |
| AFNOR | France | A-U5PbBi (2011-T6) |
ຊັບສິນ
ສ່ວນປະກອບທາງເຄມີ
Alloy 2011
| ທາດເຄມີ | % ປັດຈຸບັນ |
| ທາດເຫຼັກ (Fe) | 0.00 - 0.70 |
| ທອງແດງ (Cu) | 5.00 - 6.00 |
| Lead (Pb) | 0.20 - 0.40 |
| Bismuth (Bi) | 0.20 - 0.60 |
| ອື່ນໆ (ແຕ່ລະອັນ) | 0.00 - 0.05 |
| ອື່ນໆ (ທັງໝົດ) | 0.00 - 0.15 |
| ຊິລິໂຄນ (Si) | 0.00 - 0.40 |
| ສັງກະສີ (Zn) | 0.00 - 0.30 |
| ອາລູມິນຽມ (Al) | ຍອດເງິນ |
ຄຸນສົມບັດທາງກົນຈັກ
Rod and Bar Up to 75mm Dia.
| ຊັບສິນທາງກົນຈັກ | ມູນຄ່າ |
| ການຍືດຕົວ A50 ມມ | 6 Min % |
| ຄວາມຕ້ານທານແຮງດຶງ | 310 Min MPa |
| ຫຼັກຖານຄວາມກົດດັນ | 230 Min MPa |
| ຄວາມແຂງ Brinell | 110 HB |
| ການຍືດຕົວ A | 8 Min % |
Extruded Rod and Bar Up to 75mm Dia.
| ຊັບສິນທາງກົນຈັກ | ມູນຄ່າ |
| ຄວາມຕ້ານທານແຮງດຶງ | 310 Min MPa |
| ຫຼັກຖານຄວາມກົດດັນ | 230 Min MPa |
| ຄວາມແຂງ Brinell | 110 HB |
| ການຍືດຕົວ A | 8 Min % |
ຄຸນສົມບັດທາງກາຍະພາບທົ່ວໄປ
| ຊັບສິນທາງກາຍະພາບ | ມູນຄ່າ |
| ຄວາມໜາແໜ້ນ | 2.83 g/cm³ |
| ໂມດູນຄວາມຍືດຫຍຸ່ນ | 70 GPa |
| ການຂະຫຍາຍຕົວທາງຄວາມຮ້ອນ | 22.9 x 10-6/K |
| ຈຸດລະລາຍ | 535 °C |
ແອັບພລິເຄຊັນ
- 2011 is typically used in applications that require parts manufactured by repetition machining. These applications may include:
- Appliance parts & trim
- Automotive trim
- Fasteners and fittings
- Ordnance
ຄຸນລັກສະນະ
- Machining at high speeds produces fine chips that are easily removed. The excellent machining characteristics allow the production of complex and detailed parts. In some circumstances 2011 can replace free machining brass without the need for alterations to tooling.
- It has poor corrosion resistance, which means parts made from 2011 tend to be anodised to provide additional surface protection.
- Alloy 2011 has extremely poor weldability and thus welding is not recommended. However, as it is used for machined parts there is rarely a need to weld this alloy.
ຂໍ້ມູນເພີ່ມເຕີມ
ການຜະລິດ
| ຂະບວນການ | ການໃຫ້ຄະແນນ |
| ຄວາມສາມາດໃນການເຮັດວຽກໄດ້ - ເຢັນ | Fair |
| ຄວາມສາມາດໃນການປຸງແຕ່ງ | ດີເລີດ |
| ຄວາມສາມາດໃນການເຊື່ອມ - ອາຍແກັສ | Poor |
| ຄວາມສາມາດໃນການເຊື່ອມ - Arc | Poor |
| ຄວາມສາມາດໃນການເຊື່ອມ - ຄວາມຕ້ານທານ | Poor |
| ຄວາມສາມາດໃນການເປັນໂລຫະປະສົມ | Poor |
| ຄວາມສາມາດໃນການເຊື່ອມ | Fair |
ຄວາມສາມາດໃນການເຊື່ອມ
Alloy 2011 has extremely poor weldability and thus welding is not recommended. However, as it is used for machined parts there is rarely a need to weld this alloy.