321 Stainless Steel (S32100) Coil

Aço inoxidável, Austenítico

A titanium-stabilised chromium-nickel austenitic stainless steel with very good corrosion resistance.

Stainless steel 321 is the stabilized version of stainless steel 304. The 18/8 blend of chromium and nickel is tempered with titanium to give type 321 protection from intergranular corrosion that can occur after heat treatment. It is protected from temperatures ranging from 800 to 1500° F. The metal displays high strength and resistance to various forms of corrosions, including that from aqueous environments.

Type 321 finds application in heavy welding components, along with dynamic environments that are subject to changes.

However, the addition of titanium limits the application of 321 in terms of working. The metal is not recommended for certain welding techniques as it is not consumable. Beyond this, stainless steel 321 has excellent forming characteristics, does not require annealing after being welded, and displays toughness in a range of temperatures.

The metal shows strength even when exposed to cryogenic temperatures. Additionally, it is often chosen over Type 304 for its increased resistance to creep and rupture. Both metals may be susceptible to stress corrosion cracking.

BAIXAR PDF

Faixa

Bar Products	Tamanhos Imperiais	Tamanhos Métricos
Barra Redonda Latonada H9	1⁄8" - 7⁄8"	4mm - 25mm
Round Bar Smooth Turned H9/H10	1" - 3"	30mm
Barra Redonda Descabeçada K12/K16	3 1⁄4" - 6"	-

Sheet Size	Finish	Thicknesses
2500 x 1250	2B	1.5mm - 3.0mm

ATENÇÃO

Se você não encontrar o que procura, entre em contato com seu centro de serviço local com seus requisitos específicos.

321 Stainless Steel Related Specifications

Sistema / Padrão	País / Região	Grau / Designação
AISI	EUA	321
UNS	Internacional	S32100
PT-BR / nº de série.	Europa	1.4541
Nome em Português	Europa	X6CrNiTi18-10
ASTM A240	EUA	321 (plate, sheet, strip)
ASTM A182	EUA	F321 (forgings, flanges)
ASTM A213	EUA	TP321 (boiler / HX tubes)
ASTM A312	EUA	TP321 (seamless pipe)
GB	China	06Cr18Ni11Ti
JIS	Japão	SUS321
BS	Reino Unido	321S31
AFNOR	França	Z6CNT18-10

Propriedades

Composição Química

-                                        Elemento Químico
+                                        % Presente
-                                        Cromo (Cr)
+.00 - 19.00
-                                        Níquel (Ni)
+.00 - 12.00
-                                        Molibdênio (Mo)
+.00 - 0.75
-                                        Cobre (Cu)
+.00 - 0.75
-                                        Titânio (Ti)
+.00 - 0.70
-                                        Carbono (C)
+.00 - 0.08
-                                        Manganês (Mn)
+.00 - 2.00
-                                        Silício (Si)
+.25 - 1.00
-                                        Fósforo (P)
+.00 - 0.04
-                                        Enxofre (S)
+.00 - 0.03
-                                        Nitrogênio (N)
+.00 - 0.10

Propriedades Mecânicas

321 Stainless Steel Bar

-                                        Propriedade Mecânica
+                                        Valor
-.2% Proof Stress
+N/mm2
-                                        Alongamento A50 mm
+%
-                                        Dureza Brinell
+max HB

321 Stainless Steel Sheet

ASTM A240

-                                        Propriedade Mecânica
+                                        Valor
-                                        Tensão de Escoamento
+MPa
-                                        Resistência à Tração
+MPa
-                                        Alongamento A50 mm
+Min %

Propriedades Físicas Gerais

-                                        Propriedade Física
+                                        Valor
-                                        Densidade
+.09 g/cm³
-                                        Ponto de Fusão
+-1427 °C
-                                        Módulo de Elasticidade
+GPa
-                                        Resistividade elétrica
+.074 x 10-6 Ω .m
-                                        Condutividade Térmica
+.1 W/m.K

Applications of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio com excellent resistance to intergranular corrosion e good high-temperature strength. Its stability in welded and heat-affected areas makes it suitable for a wide range of industrial and high-temperature applications.

1. High-Temperature Industrial Applications

Furnace parts, heat exchangers, and chimneys
Boiler components, hot gas ducts, and superheaters
Componentes expostos a temperatures up to ~900°C (1650°F)

2. Chemical and Petrochemical Industry

Tanks, piping, and valves handling mildly corrosive chemicals
Equipment operating under oxidizing and high-temperature conditions
Componentes que necessitam de welded assemblies with intergranular corrosion resistance

3. Aerospace and Automotive Applications

Sistemas de escapamento e componentes de turbocompressor
High-temperature automotive components exposed to oxidizing environments

4. Food and Pharmaceutical Processing

Equipamento que requer resistance to corrosion during cleaning and sterilization
Processing vessels exposed to hot and corrosive environments

5. Architectural and Structural Applications

Structures exposed to moderately high temperatures and polluted atmospheres
Cladding, panels, and piping in industrial buildings

6. Comparison to Other Austenitic Grades

More heat-resistant than 304/304L
Ofertas better weldability and resistance to intergranular corrosion than standard 304 in high-temperature applications
Titanium addition prevents sensitization in welded areas

Resumo

321 stainless steel is widely used in high-temperature, chemical, aerospace, and industrial applications devido ao seu excellent intergranular corrosion resistance and thermal stability. Seu titanium stabilization makes it particularly suitable for welded components that require durability under heat and corrosive conditions.

Characteristics of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio designed to resist intergranular corrosion and maintain high strength at elevated temperatures. The addition of titanium stabilizes the material, preventing chromium carbide precipitation during welding or high-temperature service.

1. Resistência à Corrosão

Excelente resistência a oxidation and corrosion em moderate to high-temperature environments.
Titanium addition prevents sensibilização, maintaining corrosion resistance in welded areas.
Suitable for environments with oxidizing chemicals and atmospheric exposure.

2. Desempenho em Alta Temperatura

Retém mechanical strength at temperatures up to ~900°C (1650°F).
Adequado para continuous high-temperature service em atmosferas oxidantes.
Exhibits good creep and stress-rupture properties.

3. Propriedades Mecânicas

Excelente resistência à tração, ductilidade e tenacidade, even at elevated temperatures.
Work-hardens moderately during cold forming, allowing increased strength where required.
Mantém dimensional stability in welded assemblies.

4. Fabrication and Formability

Pode ser cold-worked (rolling, bending, deep drawing) and hot-worked (forging, extrusion, hot rolling) efficiently.
Titanium stabilization ensures welded structures maintain corrosion resistance without post-weld heat treatment.
Low risk of intergranular corrosion in welded or heat-affected zones.

5. Weldability

Excelente soldabilidade com TIG, MIG, and resistance welding.
Titanium prevents carbide formation during welding, eliminating the need for recozimento de solução pós-soldagem na maioria dos casos.

6. Applications Leveraging Characteristics

High-temperature furnace components, heat exchangers, and boilers
Equipamentos de processamento químico e tubulações
Sistemas de escapamento aeroespacial e automotivo
Equipamentos para processamento de alimentos e farmacêuticos
Architectural structures exposed to heat and industrial atmospheres

Resumo

321 stainless steel is distinguished by excellent corrosion resistance, high-temperature strength, titanium stabilization, and good weldability. Its properties make it ideal for industrial, chemical, aerospace, and high-temperature applications, particularly where welded assemblies require durability and resistance to intergranular corrosion.

Informações Adicionais

Soldabilidade

Weldability of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio com excelsa soldabilidade, thanks to its low carbon content and titanium addition. The titanium prevents precipitação de carbeto de cromo, reducing the risk of intergranular corrosion in welded areas.

1. Processos de Soldagem Adequados

TIG (GTAW): Ideal for precise and thin-section welds
MIG (GMAW): Efficient for thicker sections and industrial applications
SMAW (Shielded Metal Arc Welding): Suitable for field welding and maintenance
Soldagem por Resistência Spot and seam welding for sheet metal applications

2. Low Carbon and Titanium Benefits

Titanium stabilizes the steel, preventing chromium carbide formation na zona afetada pelo calor.
Elimina a necessidade de recozimento de solução pós-soldagem na maioria dos casos.
Ensures resistência à corrosão is maintained in welded and heat-affected areas.

3. Recomendações de Material de Preenchimento

Use matching titanium-stabilized fillers, such as ER321, for maintaining corrosion resistance and mechanical properties.
For dissimilar welds with austenitic stainless steel, ensure compatible filler material is selected to prevent sensitization.

4. Entrada de Calor e Controle de Distorção

Aços inoxidáveis austeníticos possuem alta expansão térmica, which can lead to distortion.
Moderate heat input and proper sequencing minimize warping.
Intermittent tack welding can help maintain dimensional accuracy.

5. Aplicações que Aproveitam a Soldabilidade

Equipamentos químicos e petroquímicos
High-temperature furnace components
Marine and coastal equipment
Sistemas de escapamento aeroespacial e automotivo
Equipamentos para processamento de alimentos e farmacêuticos

Resumo

321 stainless steel provides excelsa soldabilidade due to titanium stabilization and low carbon content. Welded joints maintain high corrosion resistance and structural integrity, making 321 ideal for industrial, chemical, high-temperature, marine, and food-processing applications.

Fabricação

Fabrication of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio com excellent corrosion resistance and high-temperature stability. Its low carbon content and titanium addition allow for versatile fabrication using conventional metalworking processes, while maintaining mechanical properties and corrosion resistance.

Formando

Conformação a Frio:
- Adequado para bending, rolling, drawing, and stamping
- Work-hardens moderately; intermediate têmpera de recozimento may be required for extensive deformation
Conformação a Quente:
- Recommended for complex or thick sections at 1010–1175°C (1850–2150°F)
- Ensures uniform mechanical properties and reduces work-hardening

2. Corte e Cisalhamento

Pode ser cortado com laser, waterjet, plasma, or mechanical methods.
Sharp tools and correct feeds minimize surface work hardening.

3. Usinagem

Moderate difficulty due to Tenacidade e tendência ao encruamento
Ferramentas de metal duro preferred for high-speed operations
Usar coolants or lubricants to reduce heat and improve surface finish

4. Soldagem

Excelente soldabilidade com TIG, MIG, SMAW, or resistance welding
Titanium prevents corrosão intergranular in welded areas
Filler material: ER321 recommended for matching composition and corrosion resistance
Post-weld heat treatment is generally não exigido

5. Conformação a Frio e a Quente

Cold working increases strength through work hardening; solution annealing may be needed to restore ductility
Hot working produces uniform properties and is recommended for thick or complex components

6. Acabamento de Superfície

Disponível em 2B (mill finish), BA (bright annealed), and polished surfaces
Cold working may require additional polishing or pickling for aesthetic or corrosion-sensitive applications

7. Aplicações que Utilizam Fabricação

Chemical and petrochemical vessels and piping
High-temperature furnace and boiler components
Sistemas de escapamento aeroespacial e automotivo
Equipamentos para processamento de alimentos e farmacêuticos
Architectural structures exposed to heat or industrial atmospheres

Resumo

321 stainless steel is highly versatile and easy to fabricate, oferecendo excelente cold and hot formability, machining, and welding properties. Titanium stabilization ensures corrosion resistance is maintained throughout fabrication, tornando-o ideal para industrial, chemical, aerospace, and high-temperature applications.

Conformação a Quente

Hot Working of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio com excelente trabalhabilidade a quente, tornando-o adequado para forging, rolling, extrusion, and forming at elevated temperatures. Hot working reduces work hardening and ensures uniform mechanical properties while preserving corrosion resistance.

1. Temperatura Recomendada de Trabalho a Quente

Faixa típica: 1010–1175°C (1850–2150°F)
Exceder esta faixa pode causar crescimento de grão, reducing toughness.
Working below this range increases flow stress, raising the risk of cracking.

2. Processos Adequados de Conformação a Quente

Laminação a Quente: Sheets, plates, and structural components
Forjamento a Quente: Peças de alta resistência ou de formato complexo
Extrusão a Quente: Barras, tubos e perfis
Prensagem/Conformação a Quente: Componentes espessos ou grandes difíceis de conformar a frio

3. Vantagens da Conformação a Quente

Reduz encruamento em comparação com conformação a frio
Enhances ductilidade e tenacidade
Produz uniform grain structure and mechanical properties
Allows fabrication of componentes grandes ou complexos

4. Tratamentos Pós-Trabalho a Quente

Solubilização pode ser aplicado para aliviar tensões residuais e restaurar a ductilidade
Decapagem ou passivação enhances surface corrosion resistance after hot working

5. Aplicações que Utilizam Conformação a Quente

Componentes de máquinas industriais
High-temperature chemical process equipment
Furnace and boiler components
Peças estruturais que exigem conformação em alta temperatura

Resumo

321 stainless steel demonstrates excelente trabalhabilidade a quente, allowing it to be forged, rolled, or formed at 1010–1175°C. Hot working improves ductility, reduces work hardening, and ensures uniform mechanical properties while preserving corrosion resistance, making it ideal for industrial, chemical, high-temperature, and structural applications.

Resistência ao calor

Heat Resistance of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio projetado para aplicações de alta temperatura. The addition of titanium prevents precipitação de carbeto de cromo, allowing the steel to maintain corrosion resistance and mechanical strength em altas temperaturas.

1. Temperatura de Serviço Contínuo

Suitable for continuous service in oxidizing atmospheres up to ~870°C (1600°F)
Maintains mechanical properties and corrosion resistance in this range
Prolonged exposure above 870°C may cause slight scaling and reduction in toughness

Exposição Intermitente

Tolerar intermittent heating up to ~925°C (1700°F) sem degradação superficial significativa
Suitable for parts exposed to occasional thermal cycles

3. Resistência à Oxidação

Forma um camada protetora de óxido de cromo em atmosferas oxidantes
Maintains corrosion resistance under moderate high-temperature conditions
Not recommended for strongly oxidizing or sulfidizing environments at very high temperatures

4. Efeitos Térmicos nas Propriedades Mecânicas

Retém resistência à tração e ductilidade em temperaturas moderadamente altas
Áreas trabalhadas a frio podem perder alguns benefícios de encruamento após exposição prolongada ao calor
Grain growth may occur if exposed to excessive heat without solution annealing

5. Aplicações Relacionadas à Resistência ao Calor

Furnace and boiler components
Heat exchangers, hot gas ducts, and superheaters
Equipamentos de alta temperatura para indústrias química e petroquímica
Sistemas de escapamento aeroespacial e automotivo

6. Comparison to Other Austenitic Grades

Heat resistance is slightly lower than 347 stainless steel but superior to 304 and 304L
Preferred when weldability and corrosion resistance are more critical than extreme high-temperature strength

Resumo

321 stainless steel provides excelente desempenho em altas temperaturas, with continuous service up to ~870°C and intermittent exposure up to ~925°C. Titanium stabilization prevents sensitization, maintaining corrosion resistance and mechanical properties in aplicações soldadas e de alta temperatura, tornando-o ideal para industrial, chemical, and aerospace environments.

Usinabilidade

Machinability of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio que exibe usinabilidade moderada. Sua tenacidade, tendência ao encruamento e baixa condutividade térmica exigem special attention to tooling, cutting parameters, and lubrication during machining to achieve high-quality surfaces and efficient production.

1. Comportamento de Encruamento

321 stainless steel endurece rapidamente during cutting.
Superfícies endurecidas aumentam as forças de corte e aceleram o desgaste da ferramenta.
Continuous, smooth cutting is recommended to minimize localized work hardening.

2. Recomendações de Ferramentas

Ferramentas de metal duro são preferidos para usinagem de alta velocidade ou de serviço pesado.
Ferramentas de aço rápido (HSS) can be used at lower speeds for light to medium operations.
Ferramentas com ângulos de saída positivos reduzir forças de corte e melhorar o acabamento superficial.

3. Velocidades e Avanços de Corte

Slower cutting speeds than carbon steels are recommended.
Moderate to heavy feeds ensure continuous chip flow and prevent local work hardening.
Avoid dwelling or stopping on the workpiece to prevent hard spots.

4. Resfriamento e lubrificação

Baixa condutividade térmica causa acúmulo de calor na zona de corte.
Usar fluido de corte ou fluidos de corte para reduzir o calor, prolongar a vida útil da ferramenta e melhorar o acabamento superficial.
A lubrificação de alta pressão ajuda a evacuar cavacos eficientemente.

5. Formação de Cavaco

Chips são tough, stringy, and difficult to manage.
Usar chip breakers or special inserts to control chip flow during machining.

6. Acabamento Superficial

Achievable with sharp tools, proper feeds, and adequate cooling.
Áreas endurecidas pelo trabalho podem precisar passagens de acabamento to achieve desired surface quality.

Resumo

321 stainless steel has usinabilidade moderada and requires careful tool selection, cutting parameters, and lubrication. When properly managed, high-quality surfaces and dimensional accuracy are achievable, making it suitable for chemical, aerospace, automotive, and high-temperature industrial applications.

Resistência à corrosão

Corrosion Resistance of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio com excellent resistance to intergranular corrosion and good general corrosion resistance. The addition of titanium prevents precipitação de carbeto de cromo, maintaining corrosion resistance in welded and high-temperature environments.

1. Resistência Geral à Corrosão

Resistente a oxidation and corrosion em ambientes atmosféricos e levemente corrosivos.
Adequado para industrial, chemical, and food-processing applications.
Maintains corrosion resistance even after welding or thermal exposure due to titanium stabilization.

2. Resistência à Corrosão Intergranular

Titanium forms stable carbides, preventing chromium carbide formation along grain boundaries.
Reduz o risco de sensibilização during welding or high-temperature service.
Ideal para welded assemblies without requiring post-weld heat treatment.

3. Chloride and Pitting Resistance

Fornece moderate resistance to chloride-induced pitting compared with 304 stainless steel.
Less resistant than 316 or 317 grades but sufficient for most industrial and chemical applications.

4. Corrosão em Alta Temperatura

Resistente a Oxidação e incrustação at elevated temperatures (continuous service up to ~870°C, intermittent up to ~925°C).
Funciona bem em oxidizing atmospheres and moderate chemical environments.
Não recomendado para strongly oxidizing or sulfidizing environments at very high temperatures.

5. Aplicações que se Beneficiam da Resistência à Corrosão

Furnace components, boilers, and heat exchangers
Equipamentos químicos e petroquímicos
Sistemas de escapamento aeroespacial e automotivo
Equipamentos para processamento de alimentos e farmacêuticos
Welded industrial structures exposed to heat and atmospheric corrosion

Resumo

321 stainless steel offers excelente resistência à corrosão geral e intergranular, especialmente em welded or high-temperature applications. Titanium stabilization ensures durability in chemical, industrial, aerospace, and high-temperature environments, making it a reliable choice where corrosion resistance is critical.

Tratamento Térmico

Heat Treatment of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio, which is not hardened by heat treatment. O tratamento térmico é usado principalmente para aliviar tensões, restaurar a ductilidade e manter a resistência à corrosão, em vez de aumentar a dureza.

1. Recozimento de Solução

Propósito:
- Restaurar a ductilidade após trabalho a frio ou conformação
- Aliviar tensões residuais
- Dissolve any undesired chromium carbides that may form in improper heating
Faixa de Temperatura: 1010–1120°C (1850–2050°F)
Refrigeração: Rapid air or water quench to maintain fully austenitic structure
Efeito:
- Returns mechanical properties to the annealed condition
- Preserva a resistência à corrosão devido à estabilização com titânio

2. Alívio do estresse

Propósito: Reduzir tensões residuais de conformação, dobramento ou soldagem
Faixa de Temperatura: 450–650°C (840–1200°F)
Efeito: Minimiza distorção e reduz o risco de trincas por corrosão sob tensão sem alterar significativamente as propriedades mecânicas

3. Cold-Worked Condition Considerations

A conformação a frio aumenta a resistência, mas diminui a ductilidade
Intermediate solution annealing may be applied to restore formability for further fabrication steps

4. Post-Weld Heat Treatment

Geralmente não exigido due to titanium stabilization and low carbon content
o recozimento de alívio de tensões pode ser aplicado para conjuntos soldados sensíveis à dimensão ou a altas temperaturas

5. Limitações

Tratamento térmico faz não aumenta significativamente a dureza
Exposição prolongada acima de ~500°C pode reduzir ligeiramente os efeitos de encruamento

Resumo

Heat treatment of 321 stainless steel is mainly for stress relief, ductility restoration, and maintaining corrosion resistance. Solution annealing and stress relief ensure optimal mechanical and chemical performance, making 321 ideal for aplicações soldadas, processadas a frio e em altas temperaturas.

Laminação a Frio

Cold Working of 321 Stainless Steel

321 stainless steel is a aço inoxidável austenítico estabilizado com titânio que exibe excelentes propriedades de trabalho a frio. Cold working increases Força e dureza através de encruamento, mantendo boa resistência à corrosão e ductilidade.

1. Comportamento de Encruamento

321 stainless steel work-hardens moderately durante a deformação a frio.
A resistência e a dureza aumentam, enquanto a ductilidade diminui à medida que a deformação progride.
Excessive cold working may require têmpera de recozimento to restore formability.

2. Processos de Trabalho em Comum para Gripe

Rolamento: Chapas, tiras e placas
Desenho Tubos, varetas e fios
Dobragem e Conformação: Componentes estruturais, suportes e clipes
Estampagem e Repuxo: Peças industriais e alimentícias

3. Mechanical Properties Control

O trabalho a frio permite o ajuste de resistência à tração, limite de escoamento e dureza.
Extensive cold work may require têmpera de recozimento para restaurar a ductilidade para fabricação posterior.

4. Efeito na Resistência à Corrosão

A estabilização com titânio previne precipitação de carbeto de cromo, mantendo a resistência à corrosão após trabalho a frio.
Resistente a corrosão intergranular em áreas soldadas ou muito trabalhadas.

5. Considerações Pós-Formatação

Solution annealing can relieve stresses and restore ductility if multiple cold-working steps are planned.
Cold working may slightly induce magnetism due to minor martensitic transformation, typically negligible.

6. Aplicações que Utilizam Trabalho a Frio

Molassas, clipes e fixadores
Componentes estruturais que exigem maior resistência
Tubos, varetas e fios para equipamentos químicos e de processamento de alimentos
Formed components requiring corrosion resistance and strength

Resumo

321 stainless steel exhibits excelentes características de trabalho a frio, allowing increased strength through work hardening while preserving corrosion resistance. Proper management of deformation and intermediate annealing ensures high-quality, durable components for aplicações industriais, químicas, de processamento de alimentos, marítimas e estruturais.

Pesquise o produto que você precisa

Uma ampla rede de centros de serviços na China, apoiada por sólidas instalações de processamento.

Palavras-chave populares

Categorias

Nenhum registro encontrado

Ver todos os resultados

Ligas comerciais de aço inoxidável

Aço Inoxidável 31635 (316Ti)

Metais

Aço inoxidável

Alumínio

Cobre

Latão

Bronze de alumínio

Cobre Níquel

Bronze fosforoso e bronze com chumbo

Ligas de níquel

Aços especiais

Titânio

Centro de usinagem

Roteamento CNC

Corte a laser

Serviços de fabricação

Corte de bobinas

Vaso de pressão

Acabamentos especiais

AVISO LEGAL

Esses dados são apenas indicativos e, como tal, não devem ser confiados em substituição da especificação completa. Em particular, os requisitos de propriedades mecânicas variam amplamente dependendo do temperamento, produto e dimensões do produto. Todas as informações são baseadas em nosso conhecimento atual e são fornecidas de boa fé. Nenhuma responsabilidade será aceita pela Empresa em relação a qualquer ação tomada por terceiros com base nelas. Observe que a data de ‘Atualização da Ficha Técnica’ mostrada acima não garante a precisão ou se a ficha técnica está atualizada.

As informações fornecidas nesta folha de dados foram extraídas de várias fontes reconhecidas, incluindo normas EN, referências reconhecidas do setor (impressas e on-line) e dados dos fabricantes. Não é dada nenhuma garantia de que as informações sejam da edição mais recente dessas fontes ou sobre a precisão das mesmas. O material fornecido pela Empresa pode variar significativamente em relação a esses dados, mas estará em conformidade com todos os padrões relevantes e aplicáveis. Como os produtos detalhados podem ser usados para uma ampla variedade de finalidades e como a Empresa não tem controle sobre seu uso, a Empresa exclui especificamente todas as condições ou garantias expressas ou implícitas por estatuto ou de outra forma quanto a dimensões, propriedades e/ou adequação a qualquer finalidade específica, expressa ou implícita. A orientação dada pela Empresa a qualquer terceiro é dada apenas para a assistência dessa parte e sem responsabilidade por parte da Empresa. Todas as transações estão sujeitas às Condições de Venda atuais da Empresa. A extensão das responsabilidades da Empresa perante qualquer cliente está claramente definida nessas Condições, cuja cópia está disponível mediante solicitação.