QQ-A-200/11 T73 Bar & Extrusion
Very high strength aerospace aluminium alloy.
A very high strength aerospace aluminium alloy with, depending upon temper, yield strength of 24-68 ksi (165 – 465 MPa) and tensile strength of 40-78 ksi (275 – 540 MPa).
This alloy is used where high strength is required and where good resistance to general corrosion is NOT important.
ดาวน์โหลด PDF
ช่วง
PLEASE NOTE
If you do not see what you are looking for, please contact your local service centre with your specific requirements.
QQ-A-200/11 T73 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA | 7075-T73 |
| UNS | International | A97075 (7075-T73) |
| EN / DIN | Europe | EN AW-7075-T73 / 3.4365 |
| EN Name | Europe | AlZn5.5MgCu-T73 |
| ASTM B221 | USA | 7075-T73 extruded bar, rod, shapes & tube |
| BS (Aerospace) | UK | L95 (7075 extruded alloy, T73 where specified) |
| AFNOR | France | A-Z5GU-T73 |
Properties
Chemical Composition
Alloy QQ A 200/11
SAE AMS QQ-A-200/11
| Chemical Element | % Present |
| Silicon (Si) | 0.00 - 0.40 |
| Iron (Fe) | 0.00 - 0.50 |
| Copper (Cu) | 1.20 - 2.00 |
| Manganese (Mn) | 0.00 - 0.30 |
| Chromium (Cr) | 0.18 - 0.28 |
| Magnesium (Mg) | 2.10 - 2.90 |
| Zinc (Zn) | 5.10 - 6.10 |
| Titanium (Ti) | 0.00 - 0.20 |
| Other (Each) | 0.00 - 0.05 |
| Others (Total) | 0.00 - 0.15 |
| Aluminium (Al) | Balance |
General Physical Properties
| Physical Property | Value |
| Density | 2.81 g/cm³ |
| Melting Point | 635 °C |
| Thermal Expansion | 23.5 x 10-6/K |
| Modulus of Elasticity | 72 GPa |
| Thermal Conductivity | 134-160 W/m.K |
| Electrical Resistivity | 40 % IACS |
การประยุกต์ใช้
- Aerospace components
- High technology applications
- Defence components
Characteristics
- High strength
- Very good machinability
- Weldable using resistancce, spot & beam methods
- Poor resistance to atmospheric corrosion
Additional Information
Mechanical Properties
These mechanical properties are for bar in the T73 temper.
| Diameter (mm) | Proof Strength (Min) | Tensile Strength (Min) | Elongation % (Min) |
| Up to & incl. 6.3 | 400 | 469 | 7 |
| Over 6.3 up to & incl. 38 | 420 | 483 | 8 |
| Over 38 up to & incl. 76.2 | 407 | 476 | 8 |
| Over 76.2 up to & incl. 114 | 393 | 469 | 7 |