Aluminium, BS-L
L102 T4511 Bar
High strength aerospace aluminium alloy mainly used for structural components.
L102 is used in a wide variety of high strength applications across numerous industries including defence and construction.
PDF İNDİR
Menzil
LÜTFEN DİKKAT
Aradığınız şeyi göremiyorsanız, lütfen yerel servis merkezi özel gereksinimlerinizle.
L102 T4511 Aluminium Related Specifications
| Sistem / Standart | Ülke / Bölge | Sınıf / Görevlendirme |
| AA | ABD | 2014A-T4511 |
| UNS | Uluslararası | A92014 (2014A-T4511) |
| EN / DIN | Avrupa | EN AW-2014A-T4511 / 3.1255 |
| EN Adı | Avrupa | AlCu4SiMg-T4511 |
| GB | Çin | 2A14-T4511 |
| JIS | Japan | A2014-T4511 |
| BS (Aerospace) | BIRLEŞIK KRALLIK | L102-T4511 (2014A extruded bars & sections) |
| AFNOR | Fransa | A-U4SG-T4511 |
Özellikler
Kimyasal Bileşim
Alloy L102
BS L102 (1971)
| Kimyasal Element | % Mevcut |
| Bakır (Cu) | 3.90 - 5.00 |
| Krom (Cr) | 0.00 - 0.10 |
| Demir (Fe) | 0.00 - 0.50 |
| Magnezyum (Mg) | 0.20 - 0.80 |
| Manganez (Mn) | 0.40 - 1.20 |
| Nickel (Ni) | 0.00 - 0.20 |
| Lead (Pb) | 0.00 - 0.05 |
| Silisyum (Si) | 0.50 - 0.90 |
| Tin (Sn) | 0.00 - 0.05 |
| Çinko (Zn) | 0.00 - 0.20 |
| Titanium + Zirconium (Ti+Zr) | 0.00 - 0.20 |
| Alüminyum (Al) | Denge |
Mekanik Özellikler
Alloy L102 - Mechanical Properties of T4511 temper at various diameters
BS L102 (1971)
| Mekanik Mülkiyet | Değer |
| <10mm Proof Stress | 235 Min |
| < 10mm Tensile Strength | 370 Min |
| < 10mm Elongation | 11% Min |
| 10mm - 20mm Proof Stress | 260 Min |
| 10mm - 20mm Tensile Strength | 400 Min |
| 10mm - 20mm Elongation | 11% Min |
| 20mm - 75mm Proof Stress | 270 Min |
| 20mm - 75mm Tensile Strength | 410 Min |
| 20mm - 75mm Elongation | 14% min |
| 75mm - 150mm Proof Stress | 260 Min |
| 75mm - 150mm Tensile Strength | 400 Min |
| 75mm - 150mm Elongation | 12% Min |
| 150mm - 200mm Proof Stress | 230 Min |
| 150mm - 200mm Tensile Strength | 370 Min |
| 150mm - 200mm Elongation | 8% min |
Genel Fiziksel Özellikler
Alloy L102
BS L102 (1971)
| Fiziksel Özellikler | Değer |
| Yoğunluk | 2800 g/cm³ |
| Erime Noktası | 640 °C |
| Termal Genleşme | 22.8 x 10-6/K |
| Elastisite Modülü | 73000 GPa |
| Termal İletkenlik | 134 W/m.K |
Uygulamalar
- High strength structural components
- Aircraft (e.g. fittings and wheels)
- Military vehicles & bridges
- Forgings for trucks and machinery (hydraulic etc)
- Weapons manufacture
- Structural applications
Özellikler
- Heat treatable alloy
- High mechanical strength slightly higher than 2011 and 2017A