Alüminyum, Ticari Alaşım
2011 T6 Bar
High mechanical strength alloy that machines exceptionally well.
Often called a free machining alloy or ‘FMA’ it is well suited to use in automatic lathes.
PDF İNDİR
Menzil
| Product Form | Imperial Sizes | Metric Sizes |
| Round Bar | 3⁄16"- 16" | 6mm - 50mm |
LÜTFEN DİKKAT
Aradığınız şeyi göremiyorsanız, lütfen yerel servis merkezi özel gereksinimlerinizle.
2011 T6 Aluminium Related Specifications
| Sistem / Standart | Ülke / Bölge | Sınıf / Görevlendirme |
| AA | ABD | 2011-T6 |
| UNS | Uluslararası | A92011 (2011-T6) |
| EN / DIN | Avrupa | EN AW-2011 / 3.1655 (T6) |
| EN Adı | Avrupa | AlCu6BiPb – T6 |
| ASTM B211 | ABD | 2011-T6 bar, rod, wire |
| GB | Çin | 2A01-T6 |
| JIS | Japan | A2011-T6 |
| BS | BIRLEŞIK KRALLIK | FC1 (2011-T6 bar) |
| AFNOR | Fransa | A-U5PbBi (2011-T6) |
Özellikler
Kimyasal Bileşim
Alloy 2011
| Kimyasal Element | % Mevcut |
| Demir (Fe) | 0.00 - 0.70 |
| Bakır (Cu) | 5.00 - 6.00 |
| Lead (Pb) | 0.20 - 0.40 |
| Bismuth (Bi) | 0.20 - 0.60 |
| Diğer (Her biri) | 0.00 - 0.05 |
| Diğerleri (Toplam) | 0.00 - 0.15 |
| Silisyum (Si) | 0.00 - 0.40 |
| Çinko (Zn) | 0.00 - 0.30 |
| Alüminyum (Al) | Denge |
Mekanik Özellikler
Rod and Bar Up to 75mm Dia.
| Mekanik Mülkiyet | Değer |
| Elongation A50 mm | 6 Min % |
| Çekme Dayanımı | 310 Min MPa |
| Kanıt Stres | 230 Min MPa |
| Sertlik Brinell | 110 HB |
| Elongation A | 8 Min % |
Extruded Rod and Bar Up to 75mm Dia.
| Mekanik Mülkiyet | Değer |
| Çekme Dayanımı | 310 Min MPa |
| Kanıt Stres | 230 Min MPa |
| Sertlik Brinell | 110 HB |
| Elongation A | 8 Min % |
Genel Fiziksel Özellikler
| Fiziksel Özellikler | Değer |
| Yoğunluk | 2.83 g/cm³ |
| Elastisite Modülü | 70 GPa |
| Termal Genleşme | 22.9 x 10-6/K |
| Erime Noktası | 535 °C |
Uygulamalar
- 2011 is typically used in applications that require parts manufactured by repetition machining. These applications may include:
- Appliance parts & trim
- Automotive trim
- Fasteners and fittings
- Ordnance
Özellikler
- Machining at high speeds produces fine chips that are easily removed. The excellent machining characteristics allow the production of complex and detailed parts. In some circumstances 2011 can replace free machining brass without the need for alterations to tooling.
- It has poor corrosion resistance, which means parts made from 2011 tend to be anodised to provide additional surface protection.
- Alloy 2011 has extremely poor weldability and thus welding is not recommended. However, as it is used for machined parts there is rarely a need to weld this alloy.
Ek Bilgi
Fabrikasyon
| Süreç | Değerlendirme |
| İşlenebilirlik - Soğuk | Fair |
| İşlenebilirlik | Excellent |
| Kaynaklanabilirlik - Gaz | Zayıf |
| Kaynaklanabilirlik - Ark | Zayıf |
| Kaynaklanabilirlik - Direnç | Zayıf |
| Yüzsüzlük | Zayıf |
| Solderability | Fair |
Kaynaklanabilirlik
Alloy 2011 has extremely poor weldability and thus welding is not recommended. However, as it is used for machined parts there is rarely a need to weld this alloy.