Aluminium, Commercial Alloy
6101A T6 Bar & Extrusion
A heat treatable wrought aluminium alloy used in the manufacture and construction of electrical power distribution components and equipment.
6101A aluminum is a 6000-series aluminum alloy: There is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. Cited properties are appropriate for the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements.
6101A is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6101A. AlMgSi(A) is the EN chemical designation.
TẢI XUỐNG PDF
Phạm vi
XIN LƯU Ý
Nếu bạn không tìm thấy thông tin mình cần, vui lòng liên hệ với trung tâm dịch vụ địa phương theo các yêu cầu cụ thể của quý khách.
6101A T6 Aluminium Related Specifications
| Hệ thống / Tiêu chuẩn | Quốc gia / Khu vực | Cấp bậc / Chức danh |
| AA | Hoa Kỳ | 6101-T6 (electrical conductor alloy, equivalent to 6101A-T6 in use) |
| UNS | Quốc tế | A96101 (6101 series, used for 6101/6101A in T6 tempers) |
| EN / DIN | Châu Âu | EN AW-6101A-T6 |
| Tên (tiếng Anh) | Châu Âu | AlMgSi-T6 (6101A) |
Thuộc tính
Thành phần hóa học
6101A
| Nguyên tố hóa học | Quà tặng % |
| Đồng (Cu) | 0.00 - 0.05 |
| Sắt (Fe) | 0.00 - 0.40 |
| Magnesium (Mg) | 0.40 - 0.90 |
| Other (Each) | 0.00 - 0.03 |
| Others (Total) | 0.00 - 0.10 |
| Silic (Si) | 0.30 - 0.70 |
Tính chất cơ học
Extruded Bar Up to 150mm
6101A
| Tính chất cơ học | Giá trị |
| Áp suất giới hạn | 170 Min MPa |
| Độ giãn dài tại 50 mm | 8 Min % |
| Độ bền kéo | 200 Min N/mm2 |