Metastable austenitic stainless steel
301 Stainless Steel
301 stainless steel is a high-strength, austenitic stainless steel known for its excellent mechanical properties, high work-hardening capability, and good corrosion resistance. It is widely used in applications requiring a combination of strength, ductility, and moderate resistance to corrosion.
301 Stainless Steel (SUS301 / 1.4310) is an austenitic chromium-nickel stainless steel known for its high strength, excellent corrosion resistance, and outstanding formability.
Its typical chemical composition includes 16–18% Chromium (Cr) và 6–8% Nickel (Ni) with a low carbon content.
By cold working, 301 stainless steel can significantly increase in strength and hardness, making it ideal for applications that require high strength, light weight, and durability.
TẢI XUỐNG PDF
XIN LƯU Ý
Nếu bạn không tìm thấy thông tin mình cần, vui lòng liên hệ với trung tâm dịch vụ địa phương theo các yêu cầu cụ thể của quý khách.
301 Stainless Steel Related Specifications
| Hệ thống / Tiêu chuẩn | Quốc gia / Khu vực | Cấp bậc / Chức danh |
| AISI | Hoa Kỳ | 301 |
| UNS | Quốc tế | S30100 |
| EN / Số hiệu. | Châu Âu | 1.4310 |
| Tên (tiếng Anh) | Châu Âu | X10CrNi18-8 |
| ASTM A240 | Hoa Kỳ | 301 (plate, sheet, strip) |
| ASTM A276 | Hoa Kỳ | 301 (bars, shapes) |
| ASTM A666 | Hoa Kỳ | 301 (annealed / cold-worked strip) |
| Anh | Trung Quốc | 1Cr17Ni7 |
| JIS | Nhật Bản | SUS301 |
| BS | Vương quốc Anh | 301S21 |
Thuộc tính
Thành phần hóa học
| Element | Content (%) |
| C | ≤ 0.15 |
| Si | ≤ 1.00 |
| Mn | ≤ 2.00 |
| Cr | 16.0–18.0 |
| Ni | 6.0–8.0 |
| N | ≤ 0.10 |
| S, P | ≤ 0.03 |
Tính chất cơ học
| Điều kiện | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (HRB/HRC) |
| Annealed (Soft) | 520–750 | 205 | 40 | ≤ 90 HRB |
| 1/4 Hard | 930 | 520 | 25 | 95 HRB |
| 1/2 Hard | 1070 | 760 | 15 | 30 HRC |
| 3/4 Hard | 1240 | 930 | 10 | 35 HRC |
| Full Hard | 1320–1570 | 1100 | 7 | 40 HRC |
Các tính chất vật lý chung
| Property | Unit | Typical Value |
| Mật độ | g/cm³ | 7.93 |
| Melti | °C | 140 |
| Sp | J/ | 5 |
| Th | W/ | 1 |
| Ele | µΩ· | 0.7 |
| Elas | GPa | 1 |
| Shear | GPa | 77 |
| Poisso | — | 0.3 |
| Therm | µm | 17.3 |
| (Values are nominal and may vary slightly with composition and processing conditions.) | ||
- Mật độ
- With a density of approximately 7.,
- Therm
- Exhibits moderate thermal conductivity and a coefficient of thermal expansion similar to other austenitic stainless steels, allowing good dimensional stability during heating and cooli
- Electrical Properti
- Electrical resistivity is relatively high, typical of non-conductive austenitic alloys, suitable for non-magnetic and corrosion-resistant electri
- Magne
- Non-magnetic in the annealed condition but becomes magnetic after cold w, d
- Ela
- High modulus of elasticity and low thermal conductivity make it stable under mechanical stress and
Applications of 301 Stainless Steel
301 stainless steel is a high-strength, austenitic stainless steel with excellent formability and moderate corrosion resistance. Its combination of strength, ductility, and corrosion resistance makes it suitable for a variety of structural, industrial, and decorative applications.
1. Automotive Industry
Exterior trim and decorative moldings
Structural components in vehicle bodies
Springs and suspension components
Fasteners and brackets requiring high strength
2. Industrial and Structural Applications
Các bộ phận bằng kim loại tấm dùng cho máy móc và thiết bị
Industrial fasteners, screws, and rivets
Structural supports and frameworks
Components exposed to moderate corrosion and wear
3. Architectural and Decorative Applications
Cladding panels and interior/exterior trim
Decorative metalwork and handrails
Elevator panels, facades, and furniture components
4. Springs and High-Strength Components
Tension and compression springs
Clips, straps, and precision-formed components
Các thành phần cần thiết high work-hardening capability
5. Electrical and Mechanical Equipment
Motor parts, brackets, and enclosures
Springs and wire forms in electrical assemblies
Protective covers and housings for machinery
6. Limited Chemical or Food Applications
Light-duty chemical equipment in non-aggressive environments
Food processing equipment where moderate corrosion resistance is sufficient
Tóm tắt
301 stainless steel is widely used in applications requiring high strength, good formability, and moderate corrosion resistance. Typical industries include automotive, industrial machinery, architectural, and spring applications, where its combination of strength and ductility provides reliable performance.
Characteristics of 301 Stainless Steel
301 stainless steel is a high-strength, austenitic stainless steel with excellent formability and moderate corrosion resistance. It is often used in applications requiring high strength, good ductility, and moderate corrosion resistance.
1. Mechanical Strength
High tensile and yield strength, especially after gia công nguội
Rapid work-hardening capability, which allows forming of springs, clips, and high-strength components
Maintains good toughness even at low temperatures
2. Khả năng chống ăn mòn
Khả năng chống chịu tốt đối với atmospheric and mild chemical corrosion
Khả năng chống chịu ở mức trung bình đối với chlorides; less corrosion-resistant than 304 or 316
Dễ bị sự ăn mòn giữa các hạt if welded without low-carbon or stabilized variants (e.g., 301L)
3. Formability and Ductility
Tuyệt vời đặc tính gia công nguội; can be rolled, bent, stamped, or drawn
Can be deep-drawn for complex components without cracking
High ductility combined with high strength makes it suitable for structural and decorative applications
4. Heat Resistance
Moderate heat resistance, suitable for continuous service up to 425°C (800°F)
Intermittent exposure up to 870°C (1600°F) is possible, but prolonged high-temperature use may reduce corrosion resistance
5. Weldability
Can be welded using conventional methods (TIG, MIG, SMAW)
High work-hardening rate requires careful heat control in the heat-affected zone (HAZ)
Low-carbon variants (301L) reduce risk of quá trình nhạy cảm hóa and intergranular corrosion
6. Magnetic Properties
Về cơ bản non-magnetic in the annealed state
Can become slightly magnetic after gia công nguội
Tóm tắt
301 stainless steel combines high strength, excellent formability, moderate corrosion resistance, and moderate heat resistance. Its rapid work-hardening and ductility make it ideal for automotive, industrial, architectural, and spring applications, where both strength and formability are required.
Đặc điểm
Sản xuất
Fabrication of 301 Stainless Steel
301 stainless steel is highly formable and can be fabricated using a wide range of standard stainless-steel processing methods. Its ability to achieve high strength through cold working makes it suitable for applications requiring both durability and flexibility. However, its strong work-hardening behavior requires careful control during fabrication.
1. Tạo hình
301 exhibits excellent cold formability, especially in the annealed condition.
It can be readily formed into complex shapes, including deep-drawn, stamped, or roll-formed components.
Because of rapid work hardening, forming operations may require gia nhiệt trung gian to restore ductility.
2. Cắt và xén
Cutting operations such as shearing, sawing, and laser cutting are readily performed.
Due to its work-hardening tendency, tooling must be sharp and feed rates should be consistent to avoid edge hardening.
3. Gia công
301 stainless steel is more difficult to machine than carbon steel.
Use slower cutting speeds, rigid setups, and ample coolant to avoid tool wear and heat buildup.
Carbide tools are recommended for best performance.
4. Hàn
301 has good weldability with conventional fusion and resistance welding processes.
Care must be taken to minimize sensitization in the heat-affected zone.
Low-carbon filler metals such as 308L are preferred if filler is required.
5. Gia công nguội
301 is capable of achieving very high strength levels through cold rolling, bending, or drawing.
Mechanical properties can be precisely controlled by adjusting the amount of cold work applied.
Extensive cold working will reduce ductility and may require annealing to prevent cracking.
6. Annealing
Annealing after heavy cold work restores ductility and removes residual stress.
Nhiệt độ ủ thông thường: 1010–1120°C, followed by rapid cooling.
7. Surface Finishing
Can be polished to a bright finish or supplied in various commercial finishes such as 2B or BA.
Work-hardened surfaces may require more aggressive polishing methods.
Tóm tắt
301 stainless steel is versatile, highly formable, and easily fabricated into both light and structural components. Its strong work-hardening ability offers excellent mechanical strength, while its good weldability and formability make it suitable for a wide range of manufacturing processes.
Khả năng hàn
Weldability of 301 Stainless Steel
301 stainless steel has good weldability and can be joined using most conventional fusion and resistance welding techniques. However, due to its higher carbon content compared with 304, special attention is needed to avoid sensitization and maintain corrosion resistance after welding.
Key Welding Characteristics
1. Compatible with Standard Welding Methods
301 stainless steel can be welded using:
TIG (GTAW)
MIG (GMAW)
Shielded Metal Arc Welding (SMAW)
Resistance welding (spot and seam)
These methods generally produce strong and reliable welds.
2. Sensitization Risk
The higher carbon content increases the risk of carbide precipitation (sensitization) in the heat-affected zone during welding.
Sensitization can reduce corrosion resistance, especially in chloride or acidic environments.
Sử dụng low heat input and avoiding prolonged exposure in the sensitization temperature range (450–850°C) helps minimize this risk.
3. Lựa chọn vật liệu hàn
Welding is often performed without filler metal for thin sections.
If filler is needed, recommended fillers include:
ER308L / E308L (preferred for minimizing carbide precipitation)
ER308 (acceptable for higher-strength welds)
4. Post-Weld Treatment
Annealing after welding can restore maximum corrosion resistance, especially for applications requiring high durability.
For many structural and decorative uses, post-weld annealing may not be necessary.
5. Distortion Control
301 stainless steel has high thermal expansion and can distort during welding.
Use:
Controlled heat input
Adequate fixturing
Intermittent welding techniques, if suitable
6. Resistance Welding Performance
301 exhibits excellent resistance welding characteristics due to its high electrical resistance.
Strong, clean weld nuggets can be achieved with proper parameters.
Tóm tắt
301 stainless steel is readily weldable and performs well with most welding processes. While sensitization and distortion are considerations, proper heat control, suitable filler metals, and post-weld treatments ensure strong, corrosion-resistant welds.
Khả năng gia công
Machinability of 301 Stainless Steel
301 stainless steel has khả năng gia công ở mức trung bình, similar to other austenitic stainless steels, but is more challenging to machine than carbon steels due to its tỷ lệ làm cứng do biến dạng cao and toughness. With proper tooling, lubrication, and machining practices, good surface finishes and tool life can still be achieved.
1. High Work-Hardening Rate
301 hardens rapidly during cutting operations.
Light cuts or slow feeds can cause the material surface to harden, increasing tool wear.
Continuous, heavy feeds are recommended to avoid rubbing and strain hardening.
2. Khuyến nghị về dụng cụ
Dụng cụ cacbua are preferred for high productivity and longer tool life.
High-speed steel (HSS) tools may be used at lower speeds but will wear faster.
Positive rake angles help reduce cutting forces and heat generation.
3. Tốc độ cắt và tốc độ tiến dao
Cutting speeds should be lower than those used for carbon steel to control heat.
Sử dụng moderate to heavy feed rates to keep the tool engaged and minimize work-hardening.
4. Heat Control and Coolant
Machining generates significant heat due to the alloy’s low thermal conductivity.
Flood coolant or high-performance cutting oils improve tool life and surface quality.
Proper lubrication also helps in chip evacuation.
5. Quá trình hình thành chip
301 produces miếng khoai tây chiên dai và xơ.
Chip breakers or specially shaped inserts improve chip control and reduce safety hazards.
6. Bề mặt hoàn thiện
Good surface finishes are achievable with the correct combination of tool geometry and cutting parameters.
Avoid dwell times, as stopping the tool on the workpiece can create hard spots.
Tóm tắt
301 stainless steel is fully machinable but requires controlled cutting parameters, sharp tooling, và effective cooling to counter its work-hardening nature. When proper techniques are applied, machining performance is comparable to other austenitic grades such as 304.
Khả năng chống ăn mòn
Corrosion Resistance of 301 Stainless Steel
301 stainless steel offers khả năng chống ăn mòn tốt in a wide range of environments, though its performance is slightly lower than that of 304 due to its higher carbon content. It is suitable for many general-purpose applications but requires careful consideration in more aggressive or chloride-containing conditions.
1. Khả năng chống ăn mòn nói chung
Exhibits good resistance to atmospheric corrosion, fresh water, and many organic chemicals.
Performs well in mildly corrosive industrial environments.
Not ideal for strong acids, alkalis, or environments requiring the highest level of corrosion protection.
2. Sensitization Risk
The higher carbon content increases the risk of sự kết tủa cacbua crom in the heat-affected zone during welding or thermal exposure.
Sensitization can significantly reduce corrosion resistance, especially in:
Chloride-rich environments
Acidic or reducing environments
Areas around welds
Post-weld annealing can restore optimal corrosion resistance.
3. Resistance to Chlorides
Offers limited resistance to chloride-induced corrosion.
Dễ bị pitting và crevice corrosion in marine environments or environments containing halides.
Not recommended for seawater immersion.
4. Stress Corrosion Cracking (SCC)
Austenitic grades like 301 can be prone to chloride stress corrosion cracking, especially at elevated temperatures.
Cold-worked 301 is more susceptible due to higher tensile stresses.
5. Improved Resistance After Annealing
Solution annealing dissolves carbides and restores chromium to the grain boundaries.
Enhances resistance to intergranular corrosion.
6. Comparison with Other Grades
Corrosion resistance is:
Better than: Ferritic and martensitic grades
Comparable to: 201/202 in many environments
Lower than: 304, 304L, 316, 316L, and other Mo-bearing grades
Tóm tắt
301 stainless steel provides reliable corrosion resistance for general applications but is not ideal for chloride-rich, acidic, or highly corrosive environments. Proper heat treatment, stress relief, and material selection help ensure long-term durability.
Gia công nguội
Cold Working of 301 Stainless Steel
301 stainless steel is highly responsive to cold working and is one of the most work-hardenable austenitic stainless steels. Through deformation processes such as rolling, bending, drawing, or stamping, 301 can achieve significant increases in strength while reducing ductility. This makes it ideal for applications requiring high mechanical strength without heat treatment.
1. High Work-Hardening Rate
301 has a very high rate of strain hardening, meaning its strength increases rapidly with deformation.
Cold working can transform some austenite into martensite, further increasing hardness and tensile strength.
Mechanical properties can be precisely tailored by adjusting the amount of cold reduction.
2. Strength Levels Achievable
Cold working allows 301 to reach:
Half-hard
Three-quarter-hard
Full-hard
Extra-hard conditions
These conditions offer progressively higher strength but reduced formability.
3. Forming Operations
In the annealed condition, 301 has excellent formability and can undergo deep drawing, bending, and roll forming.
As work-hardening progresses, formability decreases, and gia nhiệt trung gian có thể cần thiết để phục hồi độ dẻo.
4. Effect on Ductility
Extensive cold reduction significantly lowers elongation and increases brittleness.
Components requiring multiple forming steps typically require quá trình ủ between operations.
5. Effect on Magnetic Properties
Although annealed 301 is non-magnetic, cold working induces martensite formation, which:
Makes the material từ tính
Increases strength and hardness
This behavior is often used for magnetic stainless-steel applications.
6. Welding After Cold Working
Cold-worked 301 may lose strength near welded areas due to recrystallization.
If strength retention is critical, post-weld heat treatment or reworking may be required.
7. Spring and Structural Applications
Because of its ability to achieve high strength through cold working, 301 is widely used in:
Springs
Clips and clamps
Structural components
High-strength stamped parts
Tóm tắt
301 stainless steel exhibits outstanding cold-working behavior, allowing it to reach very high strength levels without heat treatment. Its combination of work-hardening capability, formability, and adjustable mechanical properties makes it one of the most versatile materials for high-strength stainless-steel applications.
Xử lý nhiệt
Heat Treatment of 301 Stainless Steel
301 stainless steel is an thép không gỉ austenit with high work-hardening potential. Unlike some martensitic or precipitation-hardening grades, it is not hardened by conventional heat treatment. Instead, heat treatment is primarily used to restore ductility, relieve stresses, and improve corrosion resistance after cold working or welding.
1. Annealing / Solution Treatment
Mục đích:
Relieve stresses from cold working
Restore ductility
Dissolve chromium carbides to prevent sensitization
Typical Temperature: 1010–1120°C (1850–2050°F)
Làm mát: Làm nguội nhanh bằng không khí hoặc nước để duy trì cấu trúc austenit hoàn toàn
Tác dụng:
Resets mechanical properties to annealed condition
Improves formability and corrosion resistance
2. Giảm căng thẳng
Mục đích: Giảm ứng suất dư do quá trình tạo hình, uốn hoặc hàn
Phạm vi nhiệt độ: 450–650°C (840–1200°F)
Tác dụng: Minimizes distortion and the risk of stress corrosion cracking without significantly altering mechanical properties
3. Các yếu tố cần lưu ý về trạng thái gia công nguội
Cold-worked 301 achieves very high strength, but ductility is reduced.
Quá trình ủ trung gian may be applied between forming operations to restore ductility.
Repeated cold working and annealing allow for precise control of strength and hardness.
4. Xử lý nhiệt sau hàn
301 stainless steel can be welded in the cold-worked or annealed condition.
Post-weld annealing is sometimes applied to restore ductility and corrosion resistance, especially in critical applications.
5. Hạn chế
Heat treatment does not significantly increase hardness; 301 is primarily strengthened through cold working.
High-temperature exposure (above ~500°C) for prolonged periods can reduce work-hardening effects and alter mechanical properties.
Tóm tắt
Heat treatment of 301 stainless steel is focused on stress relief, annealing, and corrosion protection rather than hardening. By using solution treatment and controlled stress relief, 301 stainless steel maintains its excellent ductility, formability, and corrosion resistance, making it suitable for structural, spring, and high-strength applications.
Khả năng chịu nhiệt
Heat Resistance of 301 Stainless Steel
301 stainless steel is an thép không gỉ austenit with moderate heat resistance. It is designed primarily for structural and mechanical applications, not for prolonged high-temperature service. Its performance at elevated temperatures is influenced by its composition, cold-working condition, and thermal exposure duration.
1. Nhiệt độ hoạt động liên tục
Suitable for continuous service up to 425–500°C (800–930°F) trong môi trường oxy hóa.
Above this temperature, mechanical strength may decrease, and scaling can occur over prolonged exposure.
2. Tiếp xúc gián đoạn
Can tolerate intermittent exposure up to 870°C (1600°F) without catastrophic failure.
Intermittent heating allows for short-term high-temperature performance in applications such as heat-treated springs or components subjected to occasional thermal cycles.
3. Khả năng chống oxy hóa
Tạo thành một lớp oxit crôm bảo vệ at elevated temperatures that helps resist scaling in air.
Not suitable for highly oxidizing environments or prolonged exposure at extreme temperatures, unlike high-temperature grades (e.g., 310, 321).
4. Ảnh hưởng của nhiệt đến các tính chất cơ học
Prolonged exposure to temperatures above 500°C can cause:
Reduced tensile strength
Loss of work-hardening benefits
Grain growth if heat-treated improperly
5. Các ứng dụng liên quan đến khả năng chịu nhiệt
Structural components exposed to moderate temperatures
Automotive springs and clips
General mechanical equipment with occasional thermal exposure
Sheet metal or formed components in industrial machinery
6. Comparison to High-Temperature Grades
Heat resistance is lower than 304, 321, and 310 stainless steels.
301 is primarily chosen for high strength, formability, and cold-worked applications, not long-term high-temperature service.
Tóm tắt
301 stainless steel provides khả năng chịu nhiệt ở mức trung bình, suitable for continuous service up to ~500°C and short-term exposure up to ~870°C. Its high strength and work-hardening characteristics make it ideal for structural and mechanical components, but it is not recommended for prolonged high-temperature applications.
Gia công nóng
Hot Working of 301 Stainless Steel
301 stainless steel is an thép không gỉ austenit với chất lượng tuyệt vời hot workability. Hot working allows the material to be shaped, formed, or rolled at elevated temperatures while avoiding excessive work hardening and preserving ductility and toughness.
1. Nhiệt độ làm việc nóng khuyến nghị
Typical hot working range: 1010–1175°C (1850–2150°F)
Working above this range may cause sự phát triển của hạt, while below this range increases flow stress and the risk of cracking.
2. Các quy trình gia công nóng phù hợp
Cán nóng: For plates, sheets, strips, and structural sections.
Rèn nóng: For components requiring high strength and complex shapes.
Ép đùn nóng: For rods, tubes, and profiles.
Hot Forming / Pressing: Allows shaping of larger or thicker sections with reduced cracking risk.
3. Ưu điểm của gia công nóng
Reduces the effects of quá trình làm cứng so với gia công nguội.
Tăng cường độ dẻo và độ bền.
Produces uniform mechanical properties and grain structure.
Allows fabrication of large or complex components.
4. Các biện pháp xử lý sau gia công nhiệt
Ủ can be applied to relieve stresses and restore uniform mechanical properties.
Ngâm axit hoặc xử lý thụ động may improve surface corrosion resistance after hot working.
5. Các ứng dụng liên quan đến gia công nóng
Automotive and aerospace structural components
Heavy-duty springs and clips
Industrial machinery and equipment requiring forming at elevated temperatures
Components where cold working is limited due to size or complexity
Tóm tắt
301 stainless steel exhibits excellent hot workability, enabling rolling, forging, extrusion, and forming at 1010–1175°C. Hot working improves ductility, reduces work hardening, and allows the production of large or complex components while maintaining strength and toughness.