Thép không gỉ, loại austenit
316Ti Stainless Steel (S31635) Sheet
A chromium-nickel-molybdenum-titanium austenitic stainless steel.
Grade 316 is an austenitic grade second only to 304 in commercial importance. 316 stainless steel contains an addition of molybdenum that gives it improved corrosion resistance. This is particularly apparent for pitting and crevice corrosion in chloride environments.
For elevated temperature applications the stabilised grade 316Ti stainless steel should be employed.
Stainless steel grade 316Ti contains a small amount of titanium. Titanium content is typically only around 0.5%. The titanium atoms stabilise the structure of the 316 at temperatures over 800°C. This prevents carbide precipitation at the grain boundaries and protects the metal from corrosion. The main advantage of 316Ti is that it can be held at higher temperatures for a longer period without sensitisation (precipitation) occurring. 316Ti retains physical and mechanical properties similar to standard grades of 316.
TẢI XUỐNG PDF
Phạm vi
XIN LƯU Ý
Nếu bạn không tìm thấy thông tin mình cần, vui lòng liên hệ với trung tâm dịch vụ địa phương theo các yêu cầu cụ thể của quý khách.
316Ti Stainless Steel Related Specifications
| Hệ thống / Tiêu chuẩn | Quốc gia / Khu vực | Cấp bậc / Chức danh |
| AISI | Hoa Kỳ | 316Ti |
| UNS | Quốc tế | S31635 |
| EN / Số hiệu. | Châu Âu | 1.4571 |
| Tên (tiếng Anh) | Châu Âu | X6CrNiMoTi17-12-2 |
| ASTM A240 | Hoa Kỳ | 316Ti (plate, sheet, strip) |
| ASTM A182 | Hoa Kỳ | F316Ti (forgings, flanges) |
| ASTM A213 | Hoa Kỳ | TP316Ti (boiler / HX tubes) |
| ASTM A312 | Hoa Kỳ | TP316Ti (seamless pipe) |
| Anh | Trung Quốc | 06Cr17Ni12Mo2Ti |
| JIS | Nhật Bản | SUS316Ti |
Thuộc tính
Thành phần hóa học
316Ti Stainless Steel Steel
EN10088-3
| Nguyên tố hóa học | Quà tặng % |
| Cacbon (C) | 0.00 - 0.08 |
| Crom (Cr) | 16.50 - 18.50 |
| Molypden (Mo) | 2.00 - 2.50 |
| Silic (Si) | 0.00 - 1.00 |
| Phốt pho (P) | 0.00 - 0.05 |
| Lưu huỳnh (S) | 0.00 - 0.03 |
| Niken (Ni) | 10.50 - 13.50 |
| Titan (Ti) | 0.40 - 0.70 |
| Mangan (Mn) | 0.00 - 2.00 |
| Sắt (Fe) | Cân bằng |
Tính chất cơ học
Bar Up to 160mm Diameter
EN10088-3
| Tính chất cơ học | Giá trị |
| Áp suất giới hạn | 200 MPa |
| Độ bền kéo | 500 đến 700 MPa |
| Độ giãn dài tại 50 mm | 40 phút 1 bàn thắng, 3 pha kiến tạo |
| Độ cứng Brinell | 215 Tốc độ tối đa |
Các tính chất vật lý chung
| Tính chất vật lý | Giá trị |
| Mật độ | 8,0 g/cm³ |
| Điểm nóng chảy | 1.400 °C |
| Sự giãn nở nhiệt | 15,9 × 10⁻⁶/K |
| Hệ số đàn hồi | 193 GPa |
| Độ dẫn nhiệt | 16,3 W/m·K |
| Điện trở suất | 0,74 × 10⁻⁶ Ω·m |
Applications of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan cùng với khả năng chống ăn mòn tuyệt vời và high-temperature stability. The addition of titanium improves intergranular corrosion resistance, making it suitable for welded and high-temperature applications.
1. Ngành công nghiệp hóa chất và hóa dầu
Storage tanks, reactors, and piping for corrosive chemicals
Heat exchangers and condensers operating under high-temperature conditions
Components in oxidizing and mildly reducing chemical environments
2. Power Generation and High-Temperature Equipment
Boiler and furnace components
Heat exchangers, superheaters, and chimneys
Equipment exposed to temperatures up to ~925°C (1700°F) intermittently
3. Food and Pharmaceutical Processing
Vessels and piping exposed to corrosive liquids and cleaning chemicals
Các thành phần cần thiết hygienic surfaces and high corrosion resistance
Equipment that undergoes frequent welding or assembly
4. Marine and Offshore Applications
Equipment and structures exposed to seawater and coastal atmospheres
Pump shafts, valves, and fittings in marine environments
5. Aerospace and Automotive Applications
Exhaust systems and turbocharger components
High-temperature, welded components where corrosion and thermal resistance are critical
6. Comparison to 316/316L
Sự ổn định của titan ngăn ngừa quá trình nhạy cảm hóa during welding, unlike standard 316 or 316L
Phù hợp với high-temperature welded assemblies
Duy trì tính chất cơ học and corrosion resistance at elevated temperatures
Tóm tắt
316Ti stainless steel is widely used in chemical, marine, pharmaceutical, food-processing, and high-temperature industrial applications due to its excellent corrosion resistance, titanium stabilization, and thermal stability. Its ability to resist intergranular corrosion in welded assemblies makes it a reliable choice for demanding environments.
Characteristics of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan that combines the corrosion resistance of 316 stainless steel with enhanced intergranular corrosion resistance và high-temperature stability. The addition of titanium makes it particularly suitable for welded components and high-temperature service.
1. Khả năng chống ăn mòn
Khả năng chống chịu tuyệt vời đối với quá trình oxy hóa và ăn mòn thông thường trong mildly corrosive environments.
Sự ổn định của titan ngăn ngừa sự kết tủa cacbua crom, minimizing the risk of sự ăn mòn giữa các hạt tại các vùng hàn.
Hoạt động tốt trong industrial, chemical, and marine environments.
2. High-Temperature Performance
Duy trì mechanical strength and dimensional stability at elevated temperatures.
Phù hợp với continuous service up to ~925°C (1700°F) intermittently, depending on the environment.
Chống lại oxidation and scaling in high-temperature applications.
3. Mechanical Properties
Tuyệt vời tensile strength, ductility, and toughness in both annealed and welded conditions.
Có thể cold-worked or hot-worked to adjust strength and hardness.
Titanium addition ensures mechanical properties are maintained during welding and high-temperature exposure.
4. Fabrication and Weldability
Tốt formability and workability using conventional cold and hot working processes.
Weldable with TIG, MIG, SMAW, and resistance welding methods.
Titanium stabilization eliminates the need for quá trình ủ sau hàn in most cases.
5. Applications Leveraging Characteristics
Chemical processing equipment (reactors, heat exchangers, piping)
High-temperature boiler, furnace, and superheater components
Marine and offshore equipment exposed to corrosive atmospheres
Thiết bị chế biến thực phẩm và dược phẩm
Aerospace and automotive high-temperature welded components
Tóm tắt
316Ti stainless steel combines excellent corrosion resistance, high-temperature stability, and titanium stabilization to prevent sensitization in welded or high-temperature applications. Its properties make it ideal for chemical, marine, high-temperature industrial, and food-processing applications where reliability and durability are critical.
Thông tin bổ sung
Khả năng hàn
Weldability of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan cùng với khả năng hàn tuyệt vời. The titanium addition prevents sự kết tủa cacbua crom, maintaining corrosion resistance in welded and heat-affected zones.
1. Suitable Welding Processes
TIG (GTAW): Rất phù hợp cho các chi tiết mỏng và các mối hàn chính xác
MIG (GMAW): Suitable for thicker sections and industrial applications
SMAW (Stick Welding): Commonly used for field and maintenance welding
Hàn điện trở: Spot and seam welding for sheet metal components
2. Lợi ích của việc ổn định titan
Titanium binds with carbon, preventing chromium carbide formation in the heat-affected zone.
Giảm nguy cơ sự ăn mòn giữa các hạt sau khi hàn.
Eliminates the need for quá trình ủ sau hàn in most cases.
3. Khuyến nghị về vật liệu độn
Sử dụng ER316Ti or ER316L filler wire for matching composition and corrosion resistance.
Ensure compatible filler material when welding dissimilar austenitic stainless steels.
4. Heat Input and Distortion Control
Thép không gỉ austenit có độ giãn nở nhiệt cao, điều này có thể gây ra hiện tượng méo hình.
Use moderate heat input and proper welding sequencing to minimize warping.
Tack welds can help maintain dimensional accuracy.
5. Applications Leveraging Weldability
Chemical processing equipment and piping
Heat exchangers, superheaters, and high-temperature boilers
Marine and offshore components
Aerospace and automotive exhaust systems
Thiết bị chế biến thực phẩm và dược phẩm
Tóm tắt
316Ti stainless steel exhibits khả năng hàn tuyệt vời, with titanium stabilization preventing intergranular corrosion in welded zones. It is ideal for high-temperature, chemical, marine, and food-processing applications where welded assemblies require durability and corrosion resistance.
Sản xuất
Fabrication of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan mà kết hợp excellent corrosion resistance, high-temperature strength, and good formability. Its fabrication properties make it suitable for cold and hot working, machining, and welding while maintaining mechanical properties and corrosion resistance.
1. Tạo hình
Đúc nguội:
Suitable for bending, rolling, deep drawing, and stamping
Work-hardens moderately; intermediate solution annealing may be needed for extensive deformation
Đúc nóng:
Recommended for complex or thick components at 1010–1175°C (1850–2150°F)
Produces uniform mechanical properties and reduces work-hardening
2. Cắt và xén
Can be cut using laser, plasma, waterjet, or mechanical methods
Sharp tools and proper feeds minimize work hardening and surface roughness
3. Gia công
Moderate machinability due to toughness and work-hardening tendency
Dụng cụ cacbua preferred for high-speed or heavy-duty operations
Coolants and lubricants are essential to reduce heat and improve surface finish
4. Hàn
Excellent weldability with TIG, MIG, SMAW, and resistance welding
Sự ổn định của titan ngăn ngừa intergranular corrosion in heat-affected zones
Matching filler metals (ER316Ti) ensure optimal corrosion resistance
5. Cold and Hot Working
Cold working increases strength through quá trình làm cứng
Hot working produces uniform ductility and mechanical properties, ideal for thick or complex components
6. Hoàn thiện bề mặt
Available in 2B, BA, and polished finishes
Cold-working may require additional polishing or pickling for aesthetic or corrosion-sensitive applications
7. Các ứng dụng tận dụng công nghệ chế tạo
Chemical and petrochemical equipment, reactors, and piping
High-temperature boiler and furnace components
Marine and offshore structures
Các bộ phận hàng không vũ trụ và ô tô
Thiết bị chế biến thực phẩm và dược phẩm
Tóm tắt
316Ti stainless steel is highly versatile for fabrication, offering excellent cold and hot formability, machining, and welding. Titanium stabilization ensures corrosion resistance is preserved throughout fabrication, making it ideal for industrial, chemical, marine, and high-temperature applications.
Gia công nóng
Hot Working of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan cùng với khả năng gia công khi nóng tuyệt vời, allowing it to be forged, rolled, or formed at elevated temperatures while maintaining mechanical properties and corrosion resistance.
1. Nhiệt độ làm việc nóng khuyến nghị
Phạm vi thông thường: 1010–1175°C (1850–2150°F)
Vượt quá phạm vi này có thể gây ra sự phát triển của hạt, reducing toughness
Working below this range increases flow stress and the risk of cracking
2. Các quy trình gia công nóng phù hợp
Cán nóng: Plates, sheets, and structural components
Rèn nóng: High-strength or complex-shaped parts
Ép đùn nóng: Rods, tubes, and profiles
Ép nóng/Định hình: Thick or large components difficult to cold-work
3. Ưu điểm của gia công nóng
Giảm quá trình làm cứng so với gia công nguội
Cải thiện độ dẻo và độ bền
Sản xuất uniform grain structure and mechanical properties
Cho phép sản xuất large or complex components
4. Các biện pháp xử lý sau gia công nhiệt
Solution annealing may be applied to relieve residual stresses and restore ductility
Ngâm axit hoặc xử lý thụ động can enhance surface corrosion resistance
5. Các ứng dụng tận dụng gia công nóng
Các bộ phận của máy móc công nghiệp
Chemical and petrochemical high-temperature equipment
Furnace, boiler, and heat exchanger components
Structural parts requiring elevated-temperature shaping
Tóm tắt
316Ti stainless steel demonstrates khả năng gia công khi nóng tuyệt vời, allowing components to be formed or forged at 1010–1175°C. Hot working improves ductility, toughness, and uniform mechanical properties while preserving corrosion resistance, making it suitable for chemical, high-temperature, industrial, and structural applications.
Khả năng chịu nhiệt
Heat Resistance of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan designed for các ứng dụng ở nhiệt độ cao. Titanium stabilization prevents sự kết tủa cacbua crom, ensuring corrosion resistance and mechanical stability at elevated temperatures.
1. Nhiệt độ hoạt động liên tục
Phù hợp với continuous service up to ~925°C (1700°F) in oxidizing atmospheres
Duy trì mechanical strength, dimensional stability, and corrosion resistance in this range
Prolonged exposure above this temperature may slightly reduce ductility or cause surface scaling
2. Tiếp xúc gián đoạn
Có thể chịu đựng được intermittent heating above 925°C without significant surface degradation
Rất thích hợp cho các bộ phận tiếp xúc với chu kỳ nhiệt
3. Khả năng chống oxy hóa
Tạo thành một lớp oxit crôm bảo vệ that resists oxidation and scaling
Hoạt động tốt trong industrial furnaces, boilers, and heat exchangers
Không nên dùng cho strongly sulfidizing or highly oxidizing environments at extreme temperatures
4. Ảnh hưởng của nhiệt đến các tính chất cơ học
Retains độ bền kéo và độ dẻo at moderate high temperatures
Cold-worked areas may lose some work-hardening benefits after prolonged heat exposure
Grain growth may occur if exposed to excessive heat without proper solution annealing
5. Applications Leveraging Heat Resistance
High-temperature chemical processing equipment
Furnace, boiler, and superheater components
Heat exchangers and exhaust systems in industrial and aerospace applications
Marine and offshore components exposed to elevated temperatures
Tóm tắt
316Ti stainless steel exhibits excellent high-temperature performance, with continuous service up to ~925°C. Titanium stabilization ensures mechanical properties and corrosion resistance are preserved in welded or high-temperature applications, making it ideal for chemical, industrial, marine, and aerospace environments.
Khả năng gia công
Machinability of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan cùng với khả năng gia công ở mức trung bình. Its toughness, work-hardening tendency, and low thermal conductivity require special attention to tooling, cutting speeds, and lubrication to achieve high-quality machining results.
1. Hiện tượng cứng hóa do gia công
316Ti stainless steel work-hardens quickly during machining.
Bề mặt cứng làm tăng lực cắt và làm gia tăng tốc độ mòn của dụng cụ.
Continuous, smooth cutting minimizes localized work hardening.
2. Khuyến nghị về dụng cụ
Dụng cụ cacbua are preferred for high-speed or heavy-duty machining.
Dụng cụ bằng thép tốc độ cao (HSS) can be used at lower speeds for lighter operations.
Các công cụ với góc nghiêng dương giảm lực cắt và cải thiện độ nhẵn bề mặt.
3. Tốc độ cắt và tốc độ tiến dao
Slower cutting speeds compared with carbon steels are recommended.
Moderate to heavy feeds ensure continuous chip flow and prevent hard spots.
Avoid stopping or dwelling on the workpiece to prevent local work-hardening.
4. Làm mát và bôi trơn
Nguyên nhân do độ dẫn nhiệt thấp sự tích tụ nhiệt tại vùng cắt.
Sử dụng chất làm mát hoặc dung dịch cắt để giảm nhiệt, kéo dài tuổi thọ dụng cụ và cải thiện độ nhẵn bề mặt.
High-pressure lubrication helps evacuate chips efficiently.
5. Quá trình hình thành chip
Chips là tough, stringy, and sticky, requiring chip breakers or controlled feeds to manage.
6. Bề mặt hoàn thiện
High-quality surface finish can be achieved with sharp tools, proper feeds, and adequate cooling.
Work-hardened areas may require những đường chuyền quyết định.
Tóm tắt
316Ti stainless steel has khả năng gia công ở mức trung bình, requiring careful tool selection, cutting parameters, and cooling. When properly managed, it can be machined with high precision and excellent surface finish, making it suitable for chemical, high-temperature, marine, aerospace, and food-processing applications.
Khả năng chống ăn mòn
Corrosion Resistance of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan cùng với khả năng chống ăn mòn tuyệt vời, particularly in welded and high-temperature applications. Titanium addition prevents sự kết tủa cacbua crom, reducing the risk of intergranular corrosion.
1. Khả năng chống ăn mòn nói chung
Có khả năng chống chịu cao đối với quá trình oxy hóa và ăn mòn thông thường in atmospheric and mildly corrosive environments.
Phù hợp với chemical, industrial, marine, and food-processing applications.
Maintains corrosion resistance even after welding or thermal exposure.
2. Intergranular Corrosion Resistance
Titanium binds with carbon, preventing chromium carbide formation along grain boundaries.
Giảm thiểu quá trình nhạy cảm hóa in the heat-affected zone during welding.
Eliminates the need for post-weld solution annealing in most cases.
3. Pitting and Crevice Corrosion
Performs moderately well in chloride-containing environments.
More resistant than 304/304L stainless steel but slightly less resistant than 316/317 in severe chloride conditions.
Phù hợp với marine, coastal, and mildly corrosive chemical applications.
4. Ăn mòn ở nhiệt độ cao
Maintains corrosion resistance during continuous service up to ~925°C (1700°F) intermittently.
Chống lại oxidation and scaling in hot, oxidizing atmospheres.
Not suitable for strongly oxidizing or sulfidizing environments at extreme temperatures.
5. Các ứng dụng tận dụng khả năng chống ăn mòn
Chemical processing equipment (reactors, piping, heat exchangers)
Marine and offshore structures
Thiết bị chế biến thực phẩm và dược phẩm
Aerospace and automotive high-temperature components
Boiler, furnace, and heat exchanger parts
Tóm tắt
316Ti stainless steel provides excellent general and intergranular corrosion resistance, đặc biệt là ở welded and high-temperature environments. Titanium stabilization ensures durability and reliability in chemical, marine, industrial, and food-processing applications, making it a robust choice for demanding conditions.
Xử lý nhiệt
Heat Treatment of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan đó là not hardenable by heat treatment. Xử lý nhiệt chủ yếu được sử dụng để relieve stresses, restore ductility, and maintain corrosion resistance, thay vì để tăng độ cứng.
1. Ủ dung dịch
Mục đích:
Restore ductility after cold working or forming
Relieve residual stresses
Dissolve any undesired chromium carbides that may form if exposed to improper temperatures
Phạm vi nhiệt độ: 1010–1120°C (1850–2050°F)
Làm mát: Rapid air or water quench to preserve austenitic structure
Tác dụng:
Restores mechanical properties to annealed condition
Preserves corrosion resistance due to titanium stabilization
2. Giảm căng thẳng
Mục đích: Giảm ứng suất dư do quá trình tạo hình, uốn hoặc hàn
Phạm vi nhiệt độ: 450–650°C (840–1200°F)
Tác dụng: Giảm thiểu biến dạng và giảm nguy cơ nứt do ăn mòn dưới ứng suất mà không làm thay đổi đáng kể các tính chất cơ học
3. Post-Weld Heat Treatment
Nói chung không bắt buộc because titanium stabilization prevents sensitization
Stress relief annealing may be applied for dimension-sensitive or high-temperature welded assemblies
4. Cold-Worked Condition Considerations
Cold working increases strength but decreases ductility
Intermediate solution annealing may be applied to restore formability for further fabrication steps
5. Hạn chế
Heat treatment does not significantly increase hardness
Prolonged exposure above ~500°C may reduce cold work strengthening effects slightly
Tóm tắt
Heat treatment of 316Ti stainless steel is mainly for giảm ứng suất, phục hồi độ dẻo và duy trì khả năng chống ăn mòn. Solution annealing and stress relief ensure optimal mechanical and chemical performance, making 316Ti ideal for welded, cold-worked, and high-temperature applications.
Gia công nguội
Cold Working of 316Ti Stainless Steel
316Ti stainless steel is a thép không gỉ austenit được ổn định bằng titan cùng với đặc tính gia công nguội tuyệt vời. Cold working improves độ bền và độ cứng thông qua quá trình làm cứng do biến dạng cơ học đồng thời vẫn duy trì khả năng chống ăn mòn và độ dẻo tốt.
1. Hiện tượng cứng hóa do gia công
316Ti stainless steel work-hardens moderately to rapidly trong quá trình biến dạng lạnh.
Độ bền và độ cứng tăng lên, trong khi độ dẻo giảm dần khi quá trình biến dạng diễn ra.
Extensive cold working may require quá trình ủ để khôi phục độ dẻo nhằm phục vụ cho các công đoạn gia công tiếp theo.
2. Các quy trình xử lý thông thường
Cuộn: Tấm, dải và tấm phẳng
Bản vẽ: Ống, thanh và dây
Uốn và tạo hình: Các bộ phận kết cấu, giá đỡ và kẹp
Dập và dập sâu: Các bộ phận dùng trong công nghiệp và chế biến thực phẩm
3. Mechanical Property Control
Gia công nguội cho phép điều chỉnh độ bền kéo, giới hạn chảy và độ cứng.
Solution annealing can be used if ductility needs to be restored for further forming.
4. Ảnh hưởng đến khả năng chống ăn mòn
Sự ổn định của titan ngăn ngừa sự kết tủa cacbua crom, duy trì khả năng chống ăn mòn sau khi gia công nguội.
Chống lại sự ăn mòn giữa các hạt ở các khu vực hàn hoặc đã qua gia công nhiều.
5. Những vấn đề cần lưu ý sau khi định hình
Solution annealing may be applied to relieve stresses and restore ductility if multiple cold-working steps are planned.
Cold working may induce slight magnetism due to minor martensitic transformation, usually negligible.
6. Các ứng dụng tận dụng quá trình gia công nguội
Lò xo, kẹp và ốc vít
Các bộ phận kết cấu đòi hỏi độ bền cao hơn
Ống, thanh và dây dùng cho thiết bị chế biến hóa chất và thực phẩm
Formed components requiring both corrosion resistance and strength
Tóm tắt
316Ti stainless steel exhibits đặc tính gia công nguội tuyệt vời, allowing increased strength through work hardening while preserving corrosion resistance. Proper management of deformation and intermediate annealing ensures high-quality, durable components for các ứng dụng trong lĩnh vực công nghiệp, hóa chất, chế biến thực phẩm, hàng hải và kết cấu.