স্টেইনলেস স্টিল, মার্কেটেনসিটিক
420 Stainless Steel (S42000) Bar
A martensitic machining bar with machinability enhanced through the addition of sulphur.
As with most other free-machining stainless steels the improvement in machinability is achieved by addition of sulphur which forms manganese sulphide inclusions; this sulphur addition also lowers the corrosion resistance, weldability and formability to below that of its non-free machining equivalent Grade 410.
420 stainless steel is a high-carbon martensitic stainless steel known for its high hardness, good wear resistance, and moderate corrosion resistance. It is commonly used in applications that require cutting edges, wear resistance, and the ability to be hardened.
Martensitic stainless steels are optimised for high hardness, and other properties are to some degree compromised. Fabrication must be by methods that allow for poor weldability and usually also allow for a final harden and temper heat treatment. Corrosion resistance is lower than the common austenitic grades, and their useful operating temperature range is limited by their loss of ductility at sub-zero temperatures and loss of strength by over-tempering at elevated temperatures.
পিডিএফ ডাউনলোড করুন
Range Enquiry
অনুগ্রহ করে লক্ষ্য করুন
আপনি যদি যা খুঁজছেন তা না পান, অনুগ্রহ করে আপনার সাথে যোগাযোগ করুন। স্থানীয় সেবা কেন্দ্র আপনার নির্দিষ্ট চাহিদা অনুযায়ী.
420 Stainless Steel Related Specifications
| সিস্টেম / স্ট্যান্ডার্ড | দেশ / অঞ্চল | গ্রেড / পদবী |
| এআইএসআই | যুক্তরাষ্ট্র | 420 |
| ইউএনএস | আন্তর্জাতিক | S42000 |
| ই.এন. / ডব্লিউ.এন.আর. | ইউরোপ | 1.4021 |
| ইএন নাম | ইউরোপ | X20Cr13 |
| ASTM A276 | যুক্তরাষ্ট্র | Type 420 (bars, shapes) |
| এএসটিএম এ৩১৪ | যুক্তরাষ্ট্র | Type 420 (forged/rolled bars) |
| ASTM A743 | যুক্তরাষ্ট্র | CA-40 (cast 420-type) |
| জিবি | চীন | 2Cr13 |
| জাপানিজ শিল্প মান | জাপান | SUS420J1 / SUS420J2 |
| বিএস | যুক্তরাজ্য | 420S37 / 420S45 |
গুণাবলী
রাসায়নিক গঠন
1.4021 Steel
EN 10088-3
| রাসায়নিক মৌল | % উপস্থাপন |
| কার্বন (C) | 0.16 - 0.25 |
| ক্রোমিয়াম (Cr) | 12.00 - 14.00 |
| ম্যাঙ্গানিজ (Mn) | 0.00 - 1.50 |
| সিলিকন (Si) | 0.00 - 1.00 |
| ফসফরাস (পি) | 0.00 - 0.04 |
| গন্ধক (S) | 0.00 - 0.03 |
| লৌহ (Fe) | সমতা |
যান্ত্রিক ধর্ম
Bar Up to 160mm Dia / Thickness
EN 10088-3
| যান্ত্রিক সম্পত্তি | মূল্য |
| প্রমাণ চাপ | 500 - 600 MPa |
| টানজনিত শক্তি | 700 - 950 MPa |
| Elongation A | 12 - 13 % |
সাধারণ ভৌত বৈশিষ্ট্যসমূহ
| শারীরিক ধর্ম | মূল্য |
| ঘনত্ব | ৭.৭৫ গ্রাম/ঘন সেমি |
| তাপীয় প্রসারণ | 10.3 x 10-6/K |
| স্থিতিস্থাপকতার মডিউল | ২০০ জিপিএ |
| তাপ পরিবাহকতা | 24.9 W/m.K |
| বৈদ্যুতিক প্রতিরোধকতা | 0.55 x 10-6 Ω .m |
Applications of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত excellent hardness, good wear resistance, and moderate corrosion resistance. এটি ব্যাপকভাবে ব্যবহৃত হয় এমন অ্যাপ্লিকেশনগুলিতে যেগুলোর জন্য cutting performance, precision, and durability.
1. Cutting Tools and Blades
Knives, scissors, and surgical instruments
Razors and trimming tools
Industrial cutting and shaping tools
2. Mechanical and Industrial Components
Gears, shafts, and bushings
Bearings and valve components
Dies, molds, and wear-resistant parts
3. Automotive and Aerospace Applications
High-strength fasteners and pins
Springs and precision components
Components requiring wear resistance under stress
4. Household and Decorative Applications
Kitchen knives and utensils
Tools and hardware exposed to moderate wear and moisture
Decorative fittings requiring moderate corrosion resistance
সারসংক্ষেপ
420 stainless steel combines high hardness, good wear resistance, and moderate corrosion resistance, এটিকে এর জন্য আদর্শ করে তোলে cutting tools, precision mechanical components, industrial parts, and household items. It is particularly suitable for applications requiring sharp edges, durability, and dimensional stability.
Characteristics of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত high hardness, excellent wear resistance, and moderate corrosion resistance. এটি ব্যাপকভাবে ব্যবহৃত হয় এমন অ্যাপ্লিকেশনগুলিতে যেগুলোর জন্য cutting performance, durability, and dimensional stability.
১. রাসায়নিক গঠন
কার্বন 0.15–0.40% – provides high hardness and wear resistance
ক্রোমিয়াম 12–14% – gives corrosion resistance and hardenability
Minor elements such as manganese, silicon, and nickel enhance mechanical properties
2. Hardness and Mechanical Properties
হতে পারে ৫০-৫৫ HRC পর্যন্ত কঠোর করা তাপ প্রক্রিয়াজাতকরণের পর
উত্তম tensile strength and wear resistance
মধ্যম নমনীয়তা এবং দৃঢ়তা, designed primarily for hard, wear-resistant applications
৩. ক্ষয় প্রতিরোধ
Moderate resistance to জারণ এবং মৃদু ক্ষয়কারী পরিবেশ
Better than carbon steels but lower than austenitic stainless steels (e.g., 304, 316)
উপযুক্ত kitchen tools, industrial components, and precision parts exposed to mild moisture or chemical exposure
4. Machinability and Fabrication
মেশিনযোগ্য অ্যানিলড কন্ডিশন
হতে পারে polished to a bright finish for aesthetic or functional applications
Welding is possible but may reduce hardness in the heat-affected zone; post-weld heat treatment is recommended
৫. আবেদনসমূহ
Knives, scissors, and cutting tools
Gears, shafts, bearings, and wear-resistant mechanical components
Springs, dies, molds, and precision engineering parts
Kitchen utensils and decorative hardware
সারসংক্ষেপ
420 stainless steel is characterized by high hardness, excellent wear resistance, and moderate corrosion resistance. এর বৈশিষ্ট্যের সংমিশ্রণ এটিকে আদর্শ করে তোলে cutting tools, precision mechanical components, industrial parts, and household items প্রয়োজনীয় durability and dimensional stability.
অতিরিক্ত তথ্য
তৈরি/নির্মাণ
Fabrication of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত good hardness, wear resistance, and moderate corrosion resistance. Fabrication requires careful handling due to its high carbon content and potential for hardening during processing.
১. গঠন
গরম কাজ:
Best performed in the অ্যানিলড কন্ডিশন.
প্রচলিত গরম কাজ করার তাপমাত্রা: ৯০০–১০৫০°সে (১৬৫০–১৯২০°ফা).
Avoid overheating to prevent grain growth and loss of toughness.
শীতল কাজের প্রক্রিয়া:
Possible in the অ্যানিলড অবস্থা.
Cold deformation increases strength through প্রসারজনিত কঠোরতা, but excessive deformation can cause cracking.
Suitable for bending, stamping, and rolling thin sections.
২. মেশিনিং
Machining is easier in the annealed condition.
Hardened 420 is যন্ত্রাংশ তৈরি করা কঠিন, requiring carbide tooling and proper cooling.
কাটিং ফ্লুইড ব্যবহার করুন reduce heat and maintain tool life.
৩. ওয়েল্ডিং
Welding is limited due to high carbon content.
Preheating and post-weld stress relief are recommended to prevent cracking.
ব্যবহার করুন মিলযুক্ত বা কম-কার্বন ফিলার সামগ্রী for better corrosion resistance and strength.
৪. তাপ শোধন
Annealing is used before fabrication to soften the steel for forming or machining.
Hardening followed by tempering is applied after fabrication to achieve desired hardness and wear resistance.
৫. পৃষ্ঠতল চিকিৎসা
Polishing or passivation can improve corrosion resistance and appearance.
Surface finishing is particularly important for cutlery, surgical instruments, and precision components.
৬. ফ্যাব্রিকেশন থেকে উপকৃত অ্যাপ্লিকেশন
Cutlery and knives
Surgical instruments and medical tools
Industrial tooling and valve components
Precision mechanical parts requiring wear resistance
সারসংক্ষেপ
420 stainless steel fabrication is typically performed in the অ্যানিলড কন্ডিশন to allow hot or cold forming, machining, and limited welding. Post-fabrication তাপ প্রয়োগ ও পৃষ্ঠতল মসৃণকরণ সর্বোত্তমভাবে নিশ্চিত করুন hardness, wear resistance, and moderate corrosion resistance, making 420 ideal for cutting tools, surgical instruments, and precision mechanical components.
ঢালাইযোগ্যতা
Weldability of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত good hardness, wear resistance, and moderate corrosion resistance. Welding this steel requires care due to its high carbon content and tendency to harden, which can lead to cracking if not properly managed.
সাধারণ বিবেচনা
High carbon content increases the risk of cracking during welding.
Preferred welding in the annealed or soft condition to reduce brittleness.
Preheating and post-weld heat treatment are recommended to minimize residual stresses and prevent martensitic hardening.
২. প্রিহিটিং
Preheat to 150–250°C (300–480°F) before welding.
Helps reduce thermal stress and the risk of cracking তাপ-প্রভাবিত অঞ্চলে (HAZ).
৩. ওয়েল্ডিং পদ্ধতি
TIG (GTAW) and MIG (GMAW) are commonly used for precision welds.
স্টিক ওয়েল্ডিং (এসএমএডব্লিউ) is possible but requires skilled control.
ব্যবহার করুন নিম্ন-হাইড্রোজেন ইলেকট্রোড ফাটল ধরার ঝুঁকি কমাতে।.
৪. ফিলার সামগ্রী
ব্যবহার করুন matching 420 filler metal for best corrosion resistance and mechanical properties.
Lower carbon or martensitic stainless fillers can be used to reduce cracking risk.
৫. ওয়েল্ডের পর তাপ চিকিৎসা
Stress relief or tempering after welding is critical to restore toughness.
Avoid quenching immediately after welding unless specifically required.
Typical post-weld tempering: 150–250°C (300–480°F) for 1–2 hours.
৬. সীমাবদ্ধতা
ঢালাই hardened condition is not recommended.
Not suitable for applications requiring high corrosion resistance in welded joints without proper post-weld treatment.
Careful control of তাপ ইনপুট is necessary to prevent distortion and cracking.
7. Applications
Welded components in cutlery and knives (annealed condition)
Light-duty industrial components
Mechanical parts requiring moderate corrosion resistance after welding
সারসংক্ষেপ
420 stainless steel is weldable with caution, preferably in the অ্যানিলড কন্ডিশন. যথাযথ preheating, controlled welding, low-hydrogen filler, and post-weld tempering are essential to prevent cracking and ensure good mechanical properties. While weldability is limited compared to austenitic stainless steels, it can be effectively welded for cutlery, tools, and moderate-duty mechanical applications.
যন্ত্রযোগ্যতা
Machinability of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত good hardness, wear resistance, and moderate corrosion resistance. Its machinability depends heavily on its তাপ প্রক্রিয়াকরণ শর্ত, with the annealed state being much easier to machine than the hardened state.
১. সাধারণ বৈশিষ্ট্য
অ্যানিল করা অবস্থা
Machinable with standard high-speed steel (HSS) or carbide tools.
প্রদান করে মসৃণ পৃষ্ঠতল এবং মাত্রিক নিয়ন্ত্রণ।.
Hardened condition:
Machining is difficult due to high hardness (up to ~50 HRC).
প্রয়োজন কার্বাইড টুলিং, slow cutting speeds, এবং ample coolant.
Strain hardening: High-carbon content may cause work hardening during machining.
২. প্রস্তাবিত কাটিং প্যারামিটার
কাটার গতি Lower speeds compared to mild steels to prevent tool wear.
ফিড রেট Moderate, to balance surface finish and tool life.
কাটার গভীরতা Shallow cuts in hardened material to avoid excessive tool stress.
কুল্যান্ট Use water-soluble oil or cutting fluid to reduce heat and friction.
৩. টুলিং
Hardened 420: Best machined with carbide or ceramic tools.
Annealed 420: Can be machined with high-speed steel (HSS) tools.
থ্রেডিং এবং ট্যাপ করা Use slow speeds and sharp tooling to prevent galling.
৪. সুবিধা
Achieves মসৃণ পৃষ্ঠতল অ্যানিল করা অবস্থায়।.
Allows precise machining of complex shapes before hardening.
Hardened 420 retains shape and wear resistance after final machining and polishing.
৫. সীমাবদ্ধতা
High carbon content reduces machinability in hardened condition.
Excessive heat during machining may cause tool wear or surface discoloration.
সতর্কতার সাথে প্রয়োজন cooling and cutting control in hardened condition.
6. Applications Benefiting from Machining
Cutlery and knives
Surgical instruments
Precision components such as valve parts and industrial tools
সারসংক্ষেপ
420 stainless steel is moderately machinable in the annealed condition এবং difficult to machine when hardened. যথাযথ tool selection, cutting speeds, feed rates, and coolant use অর্জন করার জন্য অপরিহার্য accurate dimensions, good surface finish, and tool longevity, এটিকে এর জন্য আদর্শ করে তোলে cutlery, surgical instruments, and precision industrial components.
ক্ষয় প্রতিরোধ
Corrosion Resistance of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত good hardness and wear resistance. এবং এর ক্ষয় প্রতিরোধের ক্ষমতা মধ্যমপন্থী, higher than ordinary carbon steels but lower than austenitic stainless steels such as 304 or 316.
1. General Corrosion Properties
প্রদান করে moderate resistance to atmospheric corrosion and mild oxidizing environments.
প্রবণ pitting and rusting in chloride-rich or marine environments.
Polished surfaces improve corrosion resistance by reducing surface roughness.
২. ক্ষয় প্রতিরোধ ক্ষমতাকে প্রভাবিত করার কারণগুলি
Carbon content: Higher carbon improves hardness but slightly reduces corrosion resistance.
সারফেস ফিনিস: Smooth, polished, or passivated surfaces significantly improve resistance.
তাপীয় পরিচর্যা Hardened 420 may be more prone to corrosion due to microstructural changes.
পরিবেশ Best suited for dry or mildly corrosive environments; avoid prolonged exposure to saltwater or acidic conditions.
3. ক্ষয়রোধী ক্ষমতা বৃদ্ধি
পালিশ করা Reduces surface roughness, minimizing sites for corrosion initiation.
প্যাসিভেশন: Treatment with nitric or citric acid forms a protective oxide layer.
Proper maintenance: Regular cleaning prevents accumulation of corrosive agents.
৪. ক্ষয়রোধীতার উপকারী প্রয়োগ
Cutlery, knives, and surgical instruments in low-corrosion environments
Industrial tools and precision components exposed to mild conditions
Valve components and fittings in non-marine environments
৫. সীমাবদ্ধতা
উপযুক্ত নয় মেরিন বা অত্যন্ত অ্যাসিডিক পরিবেশ সুরক্ষামূলক আবরণ ছাড়াই।.
Prolonged exposure to moisture can lead to rust and pitting.
Welding without proper care may reduce corrosion resistance তাপ-প্রভাবিত অঞ্চলে।.
সারসংক্ষেপ
420 stainless steel offers মাঝারি রাসায়নিক প্রতিরোধ ক্ষমতা, উপযুক্ত cutlery, surgical instruments, and industrial tools in mild environments. Its corrosion resistance can be enhanced through polishing, passivation, and careful maintenance, কিন্তু এটি not recommended for prolonged exposure to aggressive or marine environments.
শীতল কাজের প্রক্রিয়া
Cold Working of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত good hardness, wear resistance, and moderate corrosion resistance. Cold working is a key process for shaping and strengthening this steel, but it must be performed with care due to its high carbon content and work-hardening tendency.
১. সাধারণ বৈশিষ্ট্য
শীতল কাজের পরিমাণ বৃদ্ধি পায় শক্তি এবং কঠোরতা through প্রসারজনিত কঠোরতা.
Excessive cold working can lead to cracking, especially in hardened or heat-treated conditions.
উপযুক্ত bending, rolling, stamping, and drawing in the annealed state.
২. প্রস্তাবিত অভ্যাস
Perform cold working in the অ্যানিলড কন্ডিশন to reduce brittleness.
ব্যবহার করুন ক্রমান্বয়ে বিকৃতি rather than aggressive forming to prevent fractures.
তৈলাক্তকরণ during forming helps reduce surface defects and tool wear.
Intermediate অ্যানিলিং may be necessary for extensive deformation to restore ductility.
৩. ঠান্ডা কাজের প্রভাব
Increased hardness and strength proportional to the amount of deformation.
নমনীয়তার হ্রাস as work hardening progresses.
Enhanced surface finish and dimensional precision in certain forming processes.
৪. কোল্ড ওয়ার্কিং-এর সুবিধাভোগী অ্যাপ্লিকেশন
Cutlery and knives (pre-hardening shaping)
Surgical instruments
Springs and small mechanical components
Precision tools and industrial fittings
৫. সীমাবদ্ধতা
Hardened or overworked 420 is difficult to form and prone to cracking.
সতর্কতার সাথে প্রয়োজন তাপমাত্রা নিয়ন্ত্রণ and potential মধ্যবর্তী এনিলিং for large deformations.
Cold working alone cannot achieve final maximum hardness—post-working তাপ শোধন is usually required.
সারসংক্ষেপ
Cold working of 420 stainless steel is most effective in the annealed condition, allowing shaping through bending, rolling, stamping, and drawing. It increases strength and hardness but reduces ductility, so careful control of deformation and intermediate annealing is essential. After cold working, তাপ শোধন is typically applied to achieve final hardness and wear resistance, making it ideal for cutlery, surgical instruments, springs, and precision mechanical components.
তাপ চিকিৎসা
Heat Treatment of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত high hardness, wear resistance, and moderate corrosion resistance. Heat treatment is essential to achieve optimal hardness, strength, and dimensional stability.
১. এনিলিং
উদ্দেশ্য: গঠন, যন্ত্রাংশ নির্মাণ বা ঠান্ডা কাজের জন্য ইস্পাতকে নরম করে।.
প্রক্রিয়া:
তাপমাত্রা পর্যন্ত গরম করুন 800–900°C (1470–1650°F).
Hold at temperature to allow uniform microstructure.
Slow cooling in the furnace or in still air.
ফলাফল Steel becomes soft, ductile, and machinable.
2. Hardening (Quenching)
উদ্দেশ্য: Increases hardness and wear resistance.
প্রক্রিয়া:
তাপমাত্রা পর্যন্ত গরম করুন 980–1050°C (1800–1920°F) until fully austenitized.
Quench in air, oil, or water depending on section size.
ফলাফল Martensitic structure is formed, producing high hardness (~50 HRC).
3. Tempering
উদ্দেশ্য: Relieves stresses and improves toughness while maintaining hardness.
প্রক্রিয়া:
Heat quenched steel to 150–250°C (300–480°F).
Hold for 1–2 hours, then air cool.
প্রভাব: Reduces brittleness, enhances wear resistance, and stabilizes the martensitic structure.
৪. তাপ চিকিত্সার প্রভাব
Annealed 420: নরম, নমনীয়, গঠন এবং যন্ত্রপাতির কাজের জন্য উপযুক্ত।.
Hardened 420: High hardness and wear resistance, suitable for cutting tools and knives.
Tempered 420: Balanced hardness and toughness, less prone to cracking during service.
5. Applications of Heat-Treated 420 Stainless Steel
Cutlery and knives
Surgical instruments
শিল্প সরঞ্জাম এবং নির্ভুল যন্ত্রাংশ
Wear-resistant parts
৬. সীমাবদ্ধতা
Excessive tempering may reduce hardness and wear resistance.
Overheating during quenching can cause distortion or cracking.
Heat-treated 420 should be handled carefully to maintain dimensional accuracy.
সারসংক্ষেপ
দ্য heat treatment of 420 stainless steel involves annealing, hardening, and tempering to achieve the desired combination of hardness, wear resistance, and toughness. Proper control of temperatures and times is critical, making it suitable for cutlery, surgical instruments, industrial tools, and precision wear-resistant components.
তাপ প্রতিরোধ ক্ষমতা
Heat Resistance of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত high hardness, wear resistance, and moderate corrosion resistance. এর তাপ প্রতিরোধ ক্ষমতা limited compared to austenitic stainless steels such as 304 or 316.
১. সাধারণ বৈশিষ্ট্য
সহ্য করতে পারে intermittent exposure to temperatures up to 315°C (600°F) যান্ত্রিক বৈশিষ্ট্যের উল্লেখযোগ্য ক্ষতি ছাড়াই।.
Continuous exposure to high temperatures may lead to oxidation, scaling, and loss of hardness.
অক্ষুণ্ণ রাখে moderate mechanical strength at moderately elevated temperatures but is not suitable for high-temperature service.
উচ্চ তাপমাত্রার প্রভাব
কাঠিন্য হ্রাস Martensitic structure may soften if exposed to high heat.
অক্সিডেশন এবং স্কেলিং: Occurs at elevated temperatures, particularly in air or oxidizing atmospheres.
Dimensional changes: Extended exposure to heat can cause minor distortion.
৩. ব্যবহারিক বিবেচনা
সেরা ব্যবহৃত ambient to moderately elevated temperatures.
সুপারিশ করা হয় না continuous service above 315°C (600°F).
হতে পারে heat treated to optimize hardness and wear resistance, but high service temperatures will reduce hardness over time.
4. Applications
Cutlery and knives (not exposed to extreme heat)
Surgical instruments and tools
Industrial tooling where high wear resistance is more critical than heat resistance
5. Summary
420 stainless steel has limited heat resistance, উপযুক্ত মধ্যম-তাপমাত্রার প্রয়োগ. এটি আদর্শ cutting tools, knives, surgical instruments, and industrial components where hardness, wear resistance, and corrosion resistance are important, but it is not recommended for high-temperature or continuous heat applications.
গরম কাজ
Hot Working of 420 Stainless Steel
420 stainless steel হল একটি high-carbon martensitic stainless steel এর জন্য পরিচিত high hardness, wear resistance, and moderate corrosion resistance. Hot working is an important process to shape the steel before it is hardened, as it improves ductility and reduces the risk of cracking.
১. সাধারণ নির্দেশাবলী
Hot working should be performed in the অ্যানিলড কন্ডিশন to prevent cracking.
প্রচলিত গরম কাজ করার তাপমাত্রা: ৯০০–১০৫০°সে (১৬৫০–১৯২০°ফা).
Avoid overheating, which can cause দানা বৃদ্ধি, reducing toughness.
২. সাধারণ হট ওয়ার্কিং প্রক্রিয়া
গরম রোলিং Used to form sheets, plates, and bars.
গরম ফোরজিং Shapes parts such as blades, tools, and industrial components.
হট এক্সট্রুশন Produces complex profiles and precision components.
৩. গরম কাজের সুবিধা
হ্রাস করে শক্তি এবং দৃঢ়তা সাময়িকভাবে, allowing easier forming.
Minimizes the risk of cracking or brittleness.
প্রচার করে homogeneous microstructure throughout the workpiece.
৪. হর্ট ওয়ার্কিং-পরবর্তী বিবেচনা
অ্যানিলিং: May be necessary after hot working to relieve stresses.
Machining: Typically easier after hot working in the annealed condition.
তাপীয় পরিচর্যা Hardening and tempering applied afterward to achieve final hardness and wear resistance.
৫. সীমাবদ্ধতা
High-carbon content limits hot working compared to lower-carbon martensitic steels.
প্রয়োজন careful temperature control to avoid surface oxidation or scaling.
Not suitable for shaping in the সম্পূর্ণ শক্ত অবস্থায়.
৬. হট ওয়ার্কিং থেকে উপকৃত অ্যাপ্লিকেশন
Industrial knives and blades
Surgical instruments
Wear-resistant tooling and components
Precision mechanical parts before final hardening
সারসংক্ষেপ
Hot working of 420 stainless steel is performed in the অ্যানিলড কন্ডিশন at temperatures of ৯০০–১০৫০°সে (১৬৫০–১৯২০°ফা). It allows shaping through rolling, forging, or extrusion, reduces brittleness, and produces a homogeneous microstructure. After hot working, annealing, machining, and final heat treatment কাঙ্ক্ষিততা অর্জনের জন্য প্রয়োগ করা হয় hardness, wear resistance, and mechanical properties for applications such as cutlery, surgical instruments, and industrial tools.