স্টেইনলেস স্টীল, অস্টেনাইটিক
S310S Stainless Steel (31008) Sheet and Plate
A low carbon version of grade 310 that is less prone to embrittlement and sensitization in service.
An austenitic chromium nickel grade, Alloy 310S displays excellent oxidation resistance up to 1094°C
Alloy 310S displays excellent resistance to oxidation under mildly cyclic conditions. As a result of its high chromium and nickel content, alloy 310S has good resistance to sulphidation and other forms of hot corrosion.
Combined with its low carbon content, the metal is also effective at resisting embrittlement. The metal is commonly utilized in extreme conditions, such as furnace manufacturing and heat treating equipment.
While both hot and work practices can be applied, cold working is not commonly done on stainless steel 310S; however, it is the only way to work harden the metal. This resistance to cold temperatures is useful in cryogenic environments, as 310S is incredibly tough. However, it can be subject to thermal shock and therefore should be treated and hot-worked with care.
310S is widely used in high-temperature industrial applications where both দৃঢ়তা এবং ক্ষয় প্রতিরোধ ক্ষমতা are required, such as furnaces, heat exchangers, and thermal processing equipment.
পিডিএফ ডাউনলোড করুন
পরিসীমা
অনুগ্রহ করে লক্ষ্য করুন
আপনি যদি যা খুঁজছেন তা না পান, অনুগ্রহ করে আপনার সাথে যোগাযোগ করুন। স্থানীয় সেবা কেন্দ্র আপনার নির্দিষ্ট চাহিদা অনুযায়ী.
S310S Stainless Steel Related Specifications
| সিস্টেম / স্ট্যান্ডার্ড | দেশ / অঞ্চল | গ্রেড / পদবী |
| এআইএসআই | যুক্তরাষ্ট্র | 310S |
| ইউএনএস | আন্তর্জাতিক | S31008 |
| AISI (related) | যুক্তরাষ্ট্র | 310 (standard carbon, UNS S31000) |
| ই.এন. / ডব্লিউ.এন.আর. | ইউরোপ | 1.4845 |
| ইএন নাম | ইউরোপ | X8CrNi25-21 |
| ASTM A240 | যুক্তরাষ্ট্র | 310 / 310S (plate, sheet, strip) |
| ASTM A276 | যুক্তরাষ্ট্র | 310 / 310S (bars, shapes) |
| ASTM A213 | যুক্তরাষ্ট্র | TP310S (boiler / HX tubes) |
| ASTM A312 | যুক্তরাষ্ট্র | TP310S (seamless pipe) |
| জিবি | চীন | 06Cr25Ni20 |
| জাপানিজ শিল্প মান | জাপান | SUS310S |
গুণাবলী
রাসায়নিক গঠন
S31008 Plate
ASTM A240
| রাসায়নিক মৌল | % উপস্থাপন |
| কার্বন (C) | 0.00 - 0.08 |
| ক্রোমিয়াম (Cr) | 24.00 - 26.00 |
| নিকেল (নি) | 19.00 - 22.00 |
| ম্যাঙ্গানিজ (Mn) | 0.00 - 2.00 |
| ফসফরাস (পি) | 0.00 - 0.04 |
| গন্ধক (S) | 0.00 - 0.03 |
| সিলিকন (Si) | 0.00 - 1.50 |
| লৌহ (Fe) | সমতা |
যান্ত্রিক ধর্ম
Sheet and Plate
ASTM A240
| যান্ত্রিক সম্পত্তি | মূল্য |
| প্রমাণ চাপ | ২০৫ মিনিট মেগাপাস্কাল |
| টানজনিত শক্তি | ৫১৫ মিনি MPa |
| প্রসার A50 মিমি | ৪০ মিনিট ১টিপি৩টি |
Applications of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel সহ excellent high-temperature oxidation and corrosion resistance. Its low carbon content improves weldability and minimizes the risk of sensitization, making it ideal for industrial applications requiring both high-temperature strength and corrosion resistance.
1. High-Temperature Industrial Applications
Furnace components such as retorts, trays, and baskets
Kiln parts and heat treatment equipment
Boiler and heat exchanger components exposed to prolonged high temperatures
Thermal processing equipment in chemical, petrochemical, and power industries
2. Petrochemical and Chemical Industry
Piping, tanks, and vessels for high-temperature chemical processes
Components handling oxidizing gases or high-temperature vapors
Industrial reactors and processing equipment under thermal stress
3. Other Applications
Aerospace and automotive components exposed to high-temperature exhaust or heat
Incinerators and combustion chambers
High-temperature structural parts in industrial machinery
সারসংক্ষেপ
310S stainless steel is widely used in applications requiring high-temperature strength, oxidation resistance, and corrosion resistance. এর austenitic, low-carbon structure makes it suitable for furnaces, boilers, heat exchangers, chemical equipment, and industrial machinery exposed to extreme heat and oxidizing environments.
Characteristics of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel এর জন্য পরিচিত excellent high-temperature oxidation and corrosion resistance. Its low carbon content makes it particularly suitable for welding and fabrication in high-temperature environments.
1. High-Temperature Resistance
Maintains strength and structural integrity at elevated temperatures.
প্রতিরোধ করে অক্সিডেশন এবং স্কেলিং in continuous service up to approximately 1020°C (1870°F).
Suitable for intermittent exposure to temperatures up to 1100°C (2010°F).
২. ক্ষয় প্রতিরোধ ক্ষমতা
Good general corrosion resistance in oxidizing atmospheres.
ভালভাবে সম্পাদন করে মৃদু রাসায়নিক পরিবেশ.
Low carbon content reduces the risk of সংবেদনশীলকরণ এবং আন্তঃকণিক ক্ষয়, especially in welded components.
৩. যান্ত্রিক ধর্ম
Excellent ductility and toughness at both high and low temperatures.
Stable austenitic structure ensures consistent performance under thermal stress.
৪. নির্মাণ ও ওয়েল্ডযোগ্যতা
Easily fabricated and welded due to কম কার্বন উপাদান.
Can be cold worked and formed into complex shapes without losing corrosion resistance.
5. Applications Related to Characteristics
Furnace components, kilns, and heat treatment equipment
Boilers, heat exchangers, and thermal processing machinery
Industrial piping and storage tanks exposed to high temperatures
Aerospace and automotive high-temperature components
সারসংক্ষেপ
310S stainless steel is characterized by high-temperature strength, excellent oxidation and corrosion resistance, and good weldability. এর austenitic, low-carbon structure makes it ideal for industrial, chemical, and high-temperature applications where both durability and corrosion resistance are essential.
অতিরিক্ত তথ্য
তৈরি/নির্মাণ
Fabrication of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel এর জন্য পরিচিত excellent high-temperature oxidation and corrosion resistance. Its low carbon content enhances weldability and resistance to sensitization, making it suitable for a wide range of fabrication processes.
১. গঠন
শীতল কাজের প্রক্রিয়া:
Can be bent, drawn, or rolled, but work hardens rapidly.
Intermediate annealing may be required for extensive forming to restore ductility.
গরম কাজ:
Recommended temperature range: ১১৫০–৯০০°C (২১০০–১৬৫০°F).
Suitable for forging, hot rolling, and extrusion of thick or complex parts.
2. Welding
Easily welded using conventional methods: TIG, MIG, SMAW, and FCAW.
Low carbon content reduces the risk of সংবেদনশীলকরণ and intergranular corrosion.
Filler metals: Typically 310S or 310 grades to maintain corrosion resistance and high-temperature performance.
Post-weld pickling or passivation may be applied to restore surface protection.
৩. মেশিনিং
যন্ত্রযোগ্যতা হল মধ্যমপন্থী, with rapid work hardening tendencies.
ব্যবহার করুন sharp carbide tools, appropriate feed rates, and coolants for efficient cutting.
4. Post-Fabrication Treatments
অ্যানিলিং: Restores ductility and relieves stresses from cold working or welding.
Pickling or passivation: Removes scale or oxide layers to restore corrosion resistance.
5. Applications Related to Fabrication
Furnace components, heat treatment equipment, and kiln parts
Boilers, heat exchangers, and high-temperature piping
Chemical and petrochemical processing equipment
Aerospace and automotive components requiring high-temperature performance
সারসংক্ষেপ
310S stainless steel is highly fabricable using conventional forming, welding, and machining techniques. Its low-carbon austenitic structure ensures excellent weldability, corrosion resistance, and high-temperature performance, এটিকে উপযুক্ত করে তোলে industrial, chemical, and high-temperature applications.
ঢালাইযোগ্যতা
Weldability of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel সহ excellent high-temperature oxidation and corrosion resistance. এর কম কার্বন উপাদান enhances weldability and reduces the risk of sensitization, making it suitable for various welding processes.
1. Welding Methods
Can be welded using standard fusion welding methods:
টিআইজি (জিটিএডব্লিউ) – for precision and clean welds
এমআইজি (জিএমএডব্লিউ) – for faster, efficient welding
SMAW (Stick Welding) – for general fabrication
এফসিএডব্লিউ (ফ্লাক্স-কোরেড আর্ক ওয়েল্ডিং) – suitable for thicker sections
2. Welding Considerations
Low carbon content minimizes আন্তঃকণিক ক্ষয় risk after welding.
Preheating is usually প্রয়োজন নেই, except for very thick sections to reduce distortion.
যথাযথ ভরাট ধাতু (typically 310S or 310) are recommended to maintain high-temperature strength and corrosion resistance.
3. Post-Weld Treatments
সলিউশন এনিলিং is sometimes applied for high-temperature service to restore ductility and relieve stresses.
Pickling and passivation can remove oxides and enhance corrosion resistance of welded areas.
4. Applications Related to Weldability
Furnace and kiln components
Boilers, heat exchangers, and high-temperature piping
Chemical and petrochemical processing equipment
Industrial structures exposed to high temperatures
সারসংক্ষেপ
310S stainless steel has উত্তম ওয়েল্ডযোগ্যতা due to its low-carbon austenitic structure, allowing it to be joined using conventional welding techniques. Proper welding ensures strong, corrosion-resistant, and high-temperature capable joints, এটিকে উপযুক্ত করে তোলে furnaces, boilers, heat exchangers, and industrial high-temperature applications.
যন্ত্রযোগ্যতা
Machinability of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel অসাধারণের সাথে high-temperature corrosion and oxidation resistance. Like most austenitic stainless steels, it exhibits মধ্যম যন্ত্রচালনযোগ্যতা, primarily due to its high work-hardening tendency.
1. Work Hardening
310S stainless steel কাজ দ্রুত কঠিন হয়ে যায়, especially under light cuts or interrupted machining.
Excessive work hardening can lead to tool wear, poor surface finish, and dimensional inaccuracies.
ব্যবহার করুন sharp cutting tools and maintain consistent feed and speed to minimize work hardening.
২. টুলিং সুপারিশসমূহ
কার্বাইড সরঞ্জাম are preferred for efficient cutting and longer tool life.
High-speed steel (HSS) tools can be used at lower cutting speeds.
Rigid workholding is recommended to reduce vibration and chatter.
3. Cutting Conditions
Moderate to low cutting speeds to avoid overheating and maintain surface finish.
যথেষ্ট coolant or lubrication helps reduce heat buildup and extends tool life.
নিয়ন্ত্রণ feed rates and depth of cut to maintain dimensional accuracy and prevent work hardening.
4. Chip Formation
উৎপাদন করে long, ductile chips due to its austenitic structure.
ব্যবহার করুন chip breakers or controlled cutting to manage chips effectively.
5. Applications Related to Machinability
Industrial components requiring high-temperature corrosion resistance
Heat exchangers, furnace components, and boiler parts
Aerospace and automotive high-temperature components
Chemical processing equipment requiring precision machining
সারসংক্ষেপ
310S stainless steel has মধ্যম যন্ত্রচালনযোগ্যতা, with a tendency to work harden quickly. Using appropriate tooling, cutting conditions, and coolant, efficient machining and good surface finish can be achieved. Its combination of machinability, high-temperature strength, and corrosion resistance makes it suitable for industrial, chemical, and high-temperature applications.
ক্ষয় প্রতিরোধ
Corrosion Resistance of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel সহ excellent corrosion and oxidation resistance, বিশেষ করে উচ্চ-তাপমাত্রার পরিবেশ. Its low carbon content reduces the risk of সংবেদনশীলকরণ, making it ideal for welded and high-temperature applications.
1. High-Temperature Corrosion Resistance
এর বিরুদ্ধে চমৎকার প্রতিরোধ অক্সিডেশন এবং স্কেলিং উচ্চ তাপমাত্রায়।.
Can withstand continuous service in oxidizing atmospheres up to 1020°C (1870°F) and intermittent exposure up to 1100°C (2010°F).
একটি স্থিতিশীল গঠন করে ক্রোমিয়াম অক্সাইড স্তর that protects the surface from scaling and degradation.
২. সাধারণ ক্ষয় প্রতিরোধ
এর বিরুদ্ধে ভাল প্রতিরোধ মৃদু রাসায়নিক পরিবেশ and oxidizing media.
Low carbon content prevents সংবেদনশীলকরণ, reducing the risk of আন্তঃকণিক ক্ষয় in welded sections.
3. Resistance to Localized Corrosion
Performs well against crevice and pitting corrosion in oxidizing conditions.
Less suitable for chloride-rich environments at high temperatures, where stress corrosion cracking may occur.
4. Applications Related to Corrosion Resistance
Furnace and kiln components
Heat exchangers and boiler parts
Industrial piping and tanks in chemical and petrochemical industries
Aerospace and automotive high-temperature components
সারসংক্ষেপ
310S stainless steel offers চমৎকার ক্ষয় প্রতিরোধ ক্ষমতা, বিশেষ করে oxidizing and high-temperature environments. এর low-carbon, austenitic structure ensures resistance to আন্তঃকণিক ক্ষয়, এটিকে এর জন্য আদর্শ করে তোলে furnaces, boilers, heat exchangers, and industrial equipment exposed to high temperatures.
শীতল কাজের প্রক্রিয়া
Cold Working of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel সহ ভাল নমনীয়তা, allowing various cold working operations. Its low carbon content helps maintain corrosion resistance during forming, but like other austenitic steels, it exhibits কাজের মাধ্যমে কঠোরতা অর্জন.
১. সাধারণ সর্দি কাজ করার প্রক্রিয়া
বক্রকরণ ও গঠন: Suitable for sheets, trays, piping, and structural components.
রোলিং: Produces strips, sheets, and coils for industrial and high-temperature applications.
Deep Drawing and Stamping: Used for complex shapes in furnace components or chemical equipment.
Punching and Shearing: Suitable for components requiring precision cutting.
২. কাজের কঠোরীকরণ
310S stainless steel কাজ দ্রুত কঠিন হয়ে যায়, increasing tensile strength but reducing ductility.
Intermediate অ্যানিলিং may be required after extensive forming to restore ductility and relieve stresses.
৩. নির্মাণ সংক্রান্ত বিবেচনা
প্রয়োগ করুন ক্রমান্বয়ে বিকৃতি to avoid cracking or overstressing the material.
সঠিকভাবে ব্যবহার করুন tooling, lubrication, and support to maintain dimensional accuracy and surface finish.
শীতল-প্রক্রিয়াজাত উপাদানগুলির প্রয়োজন হতে পারে চাপ মুক্তি if used in high-temperature service.
৪. ঠান্ডা কাজের সাথে সম্পর্কিত প্রয়োগসমূহ
Furnace components and heat treatment equipment
Industrial piping, tanks, and structural parts for chemical and petrochemical industries
Components requiring corrosion resistance and dimensional stability after forming
সারসংক্ষেপ
310S stainless steel exhibits good cold working characteristics, allowing bending, rolling, deep drawing, and stamping. Cold working increases strength through কাজের মাধ্যমে কঠোরতা অর্জন while maintaining corrosion resistance, making it suitable for industrial, chemical, and high-temperature applications.
তাপ চিকিৎসা
Heat Treatment of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel এর জন্য ডিজাইন করা হয়েছে high-temperature and oxidizing environments. As an austenitic stainless steel, it is প্রচলিত তাপ প্রক্রিয়াজাতকরণ দ্বারা কঠিনীকরণযোগ্য নয়. তাপ চিকিত্সা প্রধানত ব্যবহৃত হয় চাপ উপশম করুন, নমনীয়তা পুনরুদ্ধার করুন এবং ক্ষয়-প্রতিরোধ ক্ষমতা বজায় রাখুন.
১. দ্রবণ এনিলিং
উদ্দেশ্য: Restore ductility, relieve residual stresses from cold working or welding, and maintain corrosion resistance.
তাপমাত্রার পরিসর: ১০১০–১১২০°C (১৮৫০–২০৫০°F)
শীতলীকরণ: Rapid air or water quenching to prevent carbide precipitation and maintain corrosion resistance.
২. মানসিক চাপ মুক্তি
উদ্দেশ্য: Reduce residual stresses from welding, machining, or forming.
তাপমাত্রার পরিসর: ৪৫০–৬৫০°C (৮৪০–১২০০°F)
উন্নতি করে dimensional stability and reduces risk of stress-related cracking in service.
3. Effects of Heat Treatment
পুনরুদ্ধার করে নমনীয়তা এবং দৃঢ়তা in cold-worked or welded areas.
Relieves আভ্যন্তরীণ চাপ, improving high-temperature performance.
রক্ষণাবেক্ষণ করে ক্ষয় প্রতিরোধ ক্ষমতা, especially in welded components.
4. Surface Treatments Post Heat
আচার তৈরি বা নিষ্ক্রিয়করণ may be applied after heat treatment to remove scale, oxides, or discoloration and restore the protective chromium oxide layer.
৫. তাপ প্রক্রিয়াজাতকরণ সম্পর্কিত প্রয়োগসমূহ
Furnace and kiln components
Heat exchangers and boiler parts
Industrial piping and tanks exposed to high temperatures
Chemical and petrochemical processing equipment
সারসংক্ষেপ
Heat treatment of 310S stainless steel focuses on সলিউশন এনিলিং এবং চাপ মুক্তি, বজায় রাখা ductility, corrosion resistance, and high-temperature performance. Proper heat treatment ensures reliable service in furnaces, boilers, heat exchangers, and other industrial high-temperature applications.
তাপ প্রতিরোধ ক্ষমতা
Heat Resistance of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel এর জন্য ডিজাইন করা হয়েছে excellent high-temperature strength, oxidation, and scaling resistance. Its chemical composition ensures performance in continuous and intermittent high-temperature service.
১. ধারাবাহিক সেবা তাপমাত্রা
উপযুক্ত continuous service in oxidizing atmospheres up to 1020°C (1870°F).
রক্ষণাবেক্ষণ করে mechanical strength, creep resistance, and oxidation resistance উচ্চ তাপমাত্রায়।.
২. বিচ্ছিন্ন সংস্পর্শ
সহ্য করতে পারে short-term or intermittent exposure up to 1100°C (2010°F).
Ideal for components subjected to thermal cycling or fluctuating high temperatures.
3. Oxidation and Scaling Resistance
একটি স্থিতিশীল গঠন করে ক্রোমিয়াম অক্সাইড স্তর on the surface, protecting against scaling and corrosion.
Low carbon content reduces the risk of সংবেদনশীলকরণ এবং আন্তঃকণিক ক্ষয়, even after welding or high-temperature service.
৪. সীমাবদ্ধতা
সুপারিশ করা হয় না high-chloride or highly reducing environments at elevated temperatures, as stress corrosion cracking may occur.
Extreme thermal shocks should be avoided to prevent thermal fatigue.
৫. তাপ প্রতিরোধ সংক্রান্ত প্রয়োগসমূহ
Furnace and kiln components
Heat exchangers, boilers, and high-temperature piping
Industrial equipment in chemical and petrochemical industries
Aerospace and automotive parts exposed to extreme heat
সারসংক্ষেপ
310S stainless steel offers চমৎকার তাপ প্রতিরোধ ক্ষমতা, maintaining strength, creep resistance, and oxidation protection at temperatures up to 1020°C continuous এবং 1100°C intermittent. এর low-carbon austenitic structure ensures reliable performance in furnaces, boilers, heat exchangers, and industrial high-temperature applications.
গরম কাজ
Hot Working of 310S Stainless Steel
310S stainless steel হল একটি low-carbon, austenitic stainless steel অসাধারণের সাথে high-temperature corrosion and oxidation resistance. Hot working enables shaping and forming while minimizing কাজের মাধ্যমে কঠোরতা অর্জন and maintaining the steel’s mechanical and corrosion-resistant properties.
১. প্রস্তাবিত গরম কাজের তাপমাত্রা
Hot working range: ১১৫০–৯০০°C (২১০০–১৬৫০°F).
Proper temperature control prevents দানা বৃদ্ধি and ensures uniform mechanical properties.
২. গরম কাজের প্রক্রিয়া
গরম রোলিং: Produces sheets, plates, and strips with uniform thickness.
ঢালাই: Suitable for structural or high-temperature components.
এক্সট্রুশন: Allows production of rods, tubes, and complex profiles.
Hot Forming and Pressing: Enables shaping of large or intricate parts with minimal cracking risk.
৩. গরম কাজের সুবিধা
হ্রাস করে কাজের মাধ্যমে কঠোরতা অর্জন ঠান্ডা কাজের তুলনায়।.
উন্নতি করে ductility, toughness, and formability.
তৈরি করার সক্ষমতা প্রদান করে large, thick, or complex components suitable for high-temperature service.
৪. হট ওয়ার্কিং পরবর্তী প্রক্রিয়াকরণ
অ্যানিলিং may be applied to relieve residual stresses and restore uniform mechanical properties.
আচার তৈরি বা নিষ্ক্রিয়করণ can enhance surface corrosion resistance after hot working.
৫. গরম কাজের সাথে সম্পর্কিত প্রয়োগসমূহ
Furnace and kiln components
Boilers, heat exchangers, and high-temperature piping
Industrial equipment for chemical and petrochemical processes
Aerospace and automotive parts requiring high-temperature performance
সারসংক্ষেপ
310S stainless steel exhibits excellent hot working characteristics, allowing forging, rolling, extrusion, and forming at ১১৫০–৯০০°সেলসিয়াস. Hot working improves ductility, reduces work hardening, and enables production of components for furnaces, boilers, heat exchangers, and industrial high-temperature applications.