Acier inoxydable, austénitique
201-201L-202-204 Stainless Steel Sheet & Plate
The 200 series of low nickel austenitic stainless steels.
Traditionally only popular in the United States, the 200 series of stainless steels are becoming more popular worldwide due to the significantly lower nickel content than the 300 series. As the price of nickel has risen, this has driven more interest in the 200 series as a viable and cost-effective alternative.
200 series stainless steel is an acier inoxydable austénitique that offers a cost-effective alternative to 300 series stainless steel. By using higher manganese and lower nickel, it maintains good corrosion resistance, formability, and strength while reducing material costs.
With this increased interest, producers of stainless steels have been refining the 200 series with enhanced grades and new grades. Although typically to fulfil a specific requirement for a particular application, these new grades are often simply improvements to existing grades.
TELECHARGER LE PDF
Veuillez noter
Si vous ne voyez pas ce que vous cherchez, veuillez contacter votre Centre de services local avec vos exigences spécifiques.
Related Specifications
AISI 201 stainless steel corresponds to the following specifications:
- UNS20100/EN1.4372/SUS 201/STS 201
AISI 201L stainless steel corresponds to the following specifications:
- UNS20103/EN1.4371
AISI 202 stainless steel corresponds to the following specifications:
- UNS20200/EN1.4373/SUS 202/STS 202
AISI 204C stainless steel corresponds to the following specifications:
- UNS20400/EN1.4597
Propriétés
Composition chimique
| Élément chimique | % Présent |
| Chrome (Cr) | 16.00 - 18.00 |
| Manganèse (Mn) | 6.80 - 8.50 |
| Nickel (Ni) | 2.00 - 5.00 |
| Nitrogen (N) | 0.00 - 0.25 |
| Fer (Fe) | Équilibre |
Propriétés mécaniques
| Propriété mécanique | Valeur |
| Limite d'élasticité conventionnelle | 310 Min MPa |
| La résistance à la traction | 655 Min MPa |
| Allongement A50 mm | 40 min % |
Propriétés physiques générales
| Propriété physique | Valeur |
| Densité | 7.80 g/cm³ |
| Dilatation thermique | 17 x 10-6/K |
| Module d'élasticité | 200 GPa |
| Conductivité thermique | 15 W/m.K |
Applications of 200 Series Stainless Steel
200 series stainless steel is an austenitic stainless steel with good corrosion resistance, excellent formability, and moderate strength. Its lower nickel content and cost-effectiveness make it suitable for a wide range of applications, particularly where moderate corrosion resistance is acceptable.
1. Kitchenware and Appliances
Sinks, cookware, and utensils
Refrigerators, ovens, and other household appliances
Dish racks, trays, and food storage containers
2. Architectural and Decorative Applications
Interior and exterior panels
Handrails, elevator panels, and decorative trims
Ceiling panels and furniture components
3. Automotive Industry
Decorative trim and interior panels
Non-structural components where moderate corrosion resistance is sufficient
4. Industrial and Equipment Applications
Pièces en tôle pour machines et équipements
Light-duty fasteners, brackets, and structural components
Protective covers and housings for non-corrosive environments
5. Construction and Infrastructure
Decorative railings and cladding
Indoor fixtures and fittings exposed to mild corrosive conditions
Résumé
200 series stainless steel is widely used in applications requiring good formability, moderate corrosion resistance, and cost efficiency. It is particularly popular in kitchenware, household appliances, architectural components, and decorative applications, where it serves as a more economical alternative to 300 series stainless steel.
Characteristics of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique that contains higher manganese and lower nickel compared to 300 series. It offers good corrosion resistance, excellent formability, and moderate strength, making it a cost-effective alternative to 304 stainless steel in many applications.
1. Chemical and Mechanical Features
High manganese content replaces some of the nickel, reducing cost
Carbon content is generally higher than 304, giving moderate strength
Bien toughness and ductility, suitable for cold working
2. Résistance à la corrosion
Resistant to atmospheric corrosion, mild chemicals, and water
Slightly lower corrosion resistance compared to 300 series, especially in chloride environments
Suitable for indoor and mildly corrosive outdoor conditions
3. Formability and Fabrication
Excellent caractéristiques de déformation à froid: bending, drawing, and deep-drawing
Can be rolled into sheets, strips, and coils
Easily welded using standard methods, though some grades may require post-weld annealing
4. Mechanical Properties
Moderate strength in the annealed condition
Can achieve higher strength through travail à froid due to work-hardening
Retains good toughness at low temperatures
5. Heat Resistance
Performs adequately at moderate temperatures
Not suitable for high-temperature or prolonged heat exposure applications
6. Cost Advantage
Reduced nickel content lowers material cost while maintaining acceptable corrosion resistance and mechanical properties
Popular in kitchenware, appliances, and architectural applications where cost is a key factor
Résumé
200 series stainless steel offers good corrosion resistance, excellent formability, moderate strength, and cost efficiency. It is widely used in appliances, kitchenware, automotive trim, and indoor architectural applications, serving as a more economical alternative to 300 series stainless steel.
Caractéristiques
Fabrication
Fabrication of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique connu pour son excellent formability, moderate strength, and cost-effectiveness. Its fabrication characteristics make it suitable for cold forming, welding, and machining in a wide range of applications.
1. Cold Working
Excellent ductility and formability allow deep drawing, bending, rolling, and stamping.
Can be formed into complex shapes such as sheets, strips, coils, and decorative panels.
Work hardens faster than 300 series stainless steel, so intermediate annealing may be required for extensive forming.
2. Hot Working
Can be hot worked at temperatures between 1200–900°C (2190–1650°F).
Proper temperature control is needed to prevent grain growth or reduced toughness.
Suitable for forging, extrusion, and hot rolling operations.
3. Welding
Can be welded using conventional methods: TIG, MIG, SMAW, and resistance welding.
Low carbon content or stabilized variants reduce risk of sensibilisation et la corrosion intergranulaire.
Post-weld annealing or passivation may be performed to restore corrosion resistance in welded areas.
4. Machining
Moderate machinability; higher manganese content may make cutting slightly more challenging than 300 series.
Use sharp tools, proper lubrication, and controlled feed rates to avoid work hardening and tool wear.
5. Surface Treatment
Can be polished, brushed, or patterned for architectural and decorative applications.
Pickling and passivation may enhance corrosion resistance after fabrication.
Résumé
200 series stainless steel offers excellent fabrication capabilities, including cold forming, hot working, welding, and machining. Its combination of formability, moderate strength, and corrosion resistance en fait, il est idéal pour kitchenware, household appliances, automotive trim, and architectural components.
Soudabilité
Weldability of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique avec excellente soudabilité, though its higher manganese and lower nickel content require some considerations compared to 300 series stainless steel. Proper welding techniques ensure strong, corrosion-resistant joints.
1. Suitable Welding Methods
TIG (Gas Tungsten Arc Welding, GTAW) – preferred for precision welding and thin sections
MIG (Gas Metal Arc Welding, GMAW) – suitable for thicker sections and faster welding
SMAW (Shielded Metal Arc Welding) – effective for structural components
Resistance welding (spot or seam) – used for sheet metal fabrication
2. Considérations sur le soudage
High work-hardening rate may cause slight cracking in the heat-affected zone (HAZ) if not controlled.
Preheating is generally not required for most applications.
Use compatible filler metals to maintain corrosion resistance and mechanical strength.
3. Filler Metals
Recommended filler metals: matching 200 series or 300 series stainless steels
Low-carbon or stabilized grades help reduce risk of intergranular corrosion after welding
4. Post-Weld Treatments
Stress relieving may be applied for heavily welded components to reduce internal stresses
Décapage et passivation improve corrosion resistance of welded areas
For applications requiring higher corrosion resistance, consider post-weld solution annealing
5. Limites
Slightly lower corrosion resistance compared to 300 series in chloride environments
High manganese content can slightly reduce weld pool fluidity, requiring careful heat input control
Cold-working before welding may increase hardness in the HAZ
Usinabilité
Machinability of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique avec usinabilité moyenne. Its higher manganese and lower nickel content compared to 300 series stainless steel affect its cutting characteristics. Proper machining techniques are required to achieve optimal results.
1. General Machinability
L'usinabilité est modéré, generally slightly lower than 304 stainless steel.
Tends to work harden rapidly during cutting, which can lead to tool wear and surface finish issues if not controlled.
Convient à turning, milling, drilling, and tapping with appropriate tooling.
2. Recommandations d'outils
Utiliser sharp, high-quality cutting tools (carbide or high-speed steel).
Maintain rigid setup to minimize vibration.
Appliquer adequate cutting speed, feed, and depth of cut to prevent work hardening.
3. Cooling and Lubrication
Utiliser cutting fluid or coolant to reduce heat buildup and extend tool life.
Proper lubrication improves surface finish and prevents galling.
4. Work-Hardening Considerations
Cold working or previous forming increases hardness in the material.
Avoid repeated cuts in the same area to prevent rapid tool wear.
Light finishing passes are recommended to achieve smooth surfaces.
5. Applications Related to Machining
Composants requis precision machining, such as fasteners, brackets, and appliance parts
Sheet metal forming followed by light machining for finishing
Industrial and decorative parts where usinabilité moyenne is acceptable
Résumé
200 series stainless steel has usinabilité moyenne, influenced by its high work-hardening rate and manganese content. En utilisant sharp tools, proper speeds, feeds, and cooling, it can be efficiently machined for appliances, architectural, automotive, and light industrial applications.
Résistance à la corrosion
Corrosion Resistance of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique avec bonne résistance à la corrosion in many environments. While slightly lower than 300 series due to its reduced nickel content, it still performs well in indoor, mild outdoor, and non-aggressive chemical environments.
1. Résistance générale à la corrosion
Résiste atmospheric corrosion in indoor and mild outdoor conditions.
Convient à household appliances, kitchenware, and decorative applications.
Forms a protective couche d'oxyde de chrome that prevents surface oxidation.
2. Resistance to Chlorides
Résistance modérée à pitting and crevice corrosion in chloride-containing environments.
Déconseillé pour marine or highly saline environments.
3. Intergranular Corrosion
May be susceptible to corrosion intergranulaire if welded without low-carbon or stabilized grades.
En utilisant 200 series low-carbon or stabilized variants reduces this risk.
4. Chemical Resistance
Resistant to mild acids and alkalis, such as those found in household and light industrial environments.
Convient à food contact equipment where aggressive chemicals are not present.
5. Applications Related to Corrosion Resistance
Kitchen sinks, cookware, and appliances
Interior architectural panels and decorative components
Light-duty industrial equipment in non-aggressive environments
Résumé
200 series stainless steel provides bonne résistance à la corrosion in indoor, mild outdoor, and non-aggressive chemical environments. While slightly less resistant than 300 series, it is suitable for appliances, kitchenware, architectural, and light industrial applications, offering a cost-effective balance between corrosion resistance and performance.
Travail à froid
Cold Working of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique avec excellent ductility and formability, making it highly suitable for cold working processes. Cold working improves mechanical strength through écrouissage while retaining good corrosion resistance.
1. Procédés de travail de base
Roulement : Sheets, strips, and coils can be cold-rolled to precise thicknesses.
Pliage et Formage : Ideal for panels, trims, brackets, and complex shapes.
Deep Drawing: Suitable for sinks, kitchenware, and appliance components.
Stamping and Punching: Works well for industrial and decorative parts.
2. Durcissement par travail
Cold working increases yield strength and tensile strength significantly.
High work-hardening rate allows for strong, durable components without additional alloying.
Overworking may reduce ductility, so recuit intermédiaire may be required for extensive deformation.
3. Considérations relatives à la fabrication
Cold working should be done gradually to prevent cracking.
Sharp tooling and proper lubrication improve surface finish and reduce tool wear.
Les composants travaillés à froid peuvent nécessiter stress relief or annealing for applications requiring uniform mechanical properties.
4. Applications liées à l'usinage à froid
Kitchenware: sinks, trays, cookware
Appliance components: refrigerator panels, oven trays
Architectural panels, decorative trims, and furniture
Automotive parts: interior panels, trims, and brackets
Résumé
200 series stainless steel has excellent cold working characteristics, allowing it to be rolled, bent, formed, and deep-drawn into complex shapes. Cold working enhances strength while maintaining good corrosion resistance, making it ideal for kitchenware, appliances, architectural, and automotive applications.
Traitement thermique
Heat Treatment of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique that is generally non-hardenable by conventional heat treatment. Its mechanical properties are primarily controlled through travail à froid rather than heat treatment. However, heat treatment processes are sometimes used for stress relief, annealing, or restoring ductility after extensive fabrication.
1. Annealing
Performed to soften the material, relieve internal stresses, and restore ductility.
Température de recuit typique : 1010–1120°C (1850–2050°F) for austenitizing.
Rapid cooling (water quenching or air cooling) is used to preserve the austenitic structure.
2. Gestion du stress
Applied after cold working or welding to reduce residual stresses.
Temperatures are typically in the range of 450–650 °C (840–1200 °F).
Helps prevent distortion and improves dimensional stability in fabricated components.
3. Stabilization
Unlike 321 or 347 stainless steel, 200 series does not require niobium or titanium stabilization.
Low-carbon variants reduce the risk of sensibilisation during welding.
4. Effects of Heat Treatment
Restaure ductility after extensive cold working.
Réduit hardness induced by work hardening.
Does not significantly increase strength through conventional quenching or tempering.
5. Applications liées au traitement thermique
Cold-worked kitchenware, appliances, and decorative panels needing stress relief
Welded components requiring stabilité dimensionnelle
Formed industrial parts where residual stress removal is needed
Résumé
200 series stainless steel is primarily strengthened through cold working. Heat treatment is generally used for annealing and stress relief to restore ductility and reduce residual stresses. It does not respond to conventional hardening, making it ideal for kitchenware, appliances, architectural, and light industrial applications where moderate strength and corrosion resistance are sufficient.
Résistance à la chaleur
Heat Resistance of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique avec résistance modérée à la chaleur. While it performs well at elevated temperatures, it is not designed for prolonged exposure to very high temperatures or highly oxidizing environments like 300 series or stabilized stainless steels (e.g., 321, 347).
1. Température de service continue
Convient à continuous service up to approximately 425°C (800°F).
Prolonged exposure above this temperature may reduce corrosion resistance and mechanical properties.
2. Exposition intermittente
Can withstand intermittent exposure up to 870°C (1600°F) dans des atmosphères oxydantes.
Extended exposure may lead to scaling or oxidation on the surface.
3. Résistance à l'oxydation
Forms a protective couche d'oxyde de chrome at elevated temperatures, reducing surface degradation.
Resistance is adequate for indoor and moderate industrial applications.
4. Limites
Not suitable for high-temperature chemical or marine environments.
Mechanical properties, such as tensile strength and ductility, may degrade under prolonged high heat.
Unlike stabilized grades, it does not resist intergranular attack during high-temperature service.
5. Applications liées à la résistance à la chaleur
Kitchen appliances exposed to heat, such as ovens and stove components
Industrial equipment operating at moderate temperatures
Architectural components and panels in heated environments
Light-duty machinery or equipment requiring heat tolerance but not extreme high-temperature resistance
Résumé
200 series stainless steel offers résistance modérée à la chaleur, suitable for continuous service up to 425°C (800°F) et une exposition intermittente jusqu'à 870°C (1600°F). It is ideal for appliances, architectural components, and industrial applications where moderate heat resistance is sufficient but does not require the high-temperature performance of 300 series or stabilized stainless steels.
Travail à chaud
Hot Working of 200 Series Stainless Steel
200 series stainless steel is an acier inoxydable austénitique avec excellentes caractéristiques de travail à chaud. Hot working processes allow shaping and forming of the steel at elevated temperatures while maintaining ductility and minimizing work hardening.
1. Hot Working Temperature
Suitable for hot working between 1200–900°C (2190–1650°F).
Proper temperature control is critical to prevent grain growth or reduced toughness.
2. Procédés de travail à chaud
Laminage à chaud : Sheets, plates, and strips can be rolled to desired thickness.
Forgeage Suitable for producing structural components and heavy parts.
Extrusion : Can form tubes, rods, and profiles at elevated temperatures.
Hot Pressing and Forming: Allows shaping complex components with reduced risk of cracking.
3. Avantages du travail à chaud
Réduit écrouissage comparé à l'usinage à froid.
Améliore ductilité et ténacité in the finished component.
Enables the production of large, complex parts that cannot be formed cold.
4. Traitements post-forge
Recuit may be applied to restore uniform mechanical properties and relieve residual stresses.
Décapage et passivation improve corrosion resistance after hot working.
5. Applications liées au travail à chaud
Structural components in appliances, machinery, and light industrial equipment
Sheets, plates, and strips for architectural and decorative panels
Automotive trim, brackets, and supports requiring shaping at elevated temperatures
Résumé
200 series stainless steel exhibits excellent hot working performance, allowing for rolling, forging, extrusion, and complex forming at 1200–900°C. Hot working reduces work hardening, enhances ductility, and enables production of large or intricate parts, making it suitable for appliances, industrial equipment, architectural, and automotive applications.