Acier inoxydable, austénitique
S310H Stainless Steel (S31009) Pipe & Fittings
A high carbon modification of 310 developed for enhanced creep resistance.
Alloy 310 (UNS S31000) is an austenitic stainless steel developed for use in high temperature corrosion resistant applications. The alloy resists oxidation up to 2010°F (1100°C) under mildly cyclic conditions.
310H stainless steel est un high-carbon, austenitic stainless steel conçu pour excellent high-temperature strength and oxidation resistance. The “H” in 310H indicates a teneur en carbone plus élevée, which improves its creep resistance at elevated temperatures compared to standard 310 stainless steel.
This steel is widely used in applications industrielles à haute température, such as fours, échangeurs de chaleur et équipements de traitement thermique, where it maintains mechanical integrity and corrosion resistance under prolonged exposure to heat and oxidizing environments.
TELECHARGER LE PDF
Gamme
Veuillez noter
Si vous ne voyez pas ce que vous cherchez, veuillez contacter votre Centre de services local avec vos exigences spécifiques.
S310H Stainless Steel Related Specifications
| Système / Standard | Pays / Région | Grade / Désignation |
| AISI | ÉTATS-UNIS | 310H |
| Nations Unies | International | S31009 |
| FR / Numéro de dossier. | Europe | 1.4845 |
| Nom EN | Europe | X8CrNi25-21 |
| ASTM A240 | ÉTATS-UNIS | 310H (plate, sheet, strip) |
| ASTM A213 | ÉTATS-UNIS | TP310H (boiler / HX tubes) |
| ASTM A312 | ÉTATS-UNIS | TP310H (seamless pipe) |
| ASTM A403 | ÉTATS-UNIS | WP310H (butt-weld fittings) |
| RU | Chine | 07Cr25Ni20 (310H type) |
| ISJ | Japon | SUS310H |
Propriétés
Composition chimique
S31009 Pipe
ASTM A312
| Élément chimique | % Présent |
| Carbone (C) | 0.04 - 0.10 |
| Chrome (Cr) | 24.00 - 26.00 |
| Nickel (Ni) | 19.00 - 22.00 |
| Manganèse (Mn) | 0.00 - 2.00 |
| Phosphore (P) | 0.00 - 0.05 |
| Soufre (S) | 0.00 - 0.03 |
| Silicium (Si) | 0.00 - 1.00 |
| Fer (Fe) | Équilibre |
Propriétés mécaniques
Pipe
ASTM A312
| Propriété mécanique | Valeur |
| Limite d'élasticité conventionnelle | 205 MPa |
| La résistance à la traction | 515 MPa |
| Allongement A50 mm | 35 Min % |
Applications of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel avec excellent high-temperature strength and oxidation resistance. Its combination of mechanical integrity and corrosion resistance at elevated temperatures makes it ideal for industrial applications exposed to heat and oxidizing environments.
1. Applications Industrielles à Haute Température
Composants du four tels que râteliers, plateaux et paniers
Pièces de four et équipement de traitement thermique
Composants de chaudière et d'échangeur de chaleur exposés à des températures élevées prolongées
Équipement de traitement thermique dans les industries chimique, pétrochimique et de l'énergie
2. Industrie pétrochimique et chimique
Tuyauterie, réservoirs et cuves pour procédés chimiques à haute température
Composants manipulant des gaz oxydants ou des vapeurs à haute température
Industrial reactors and processing equipment operating under thermal stress
3. Autres applications
Composants aérospatiaux et automobiles exposés aux gaz d'échappement à haute température ou à la chaleur
Incinérateurs et chambres de combustion
Composants structurels haute température dans les machines industrielles
Résumé
310H stainless steel is used in applications that require high-temperature strength, creep resistance, and oxidation resistance. Son high-carbon, austenitic structure le rend adapté à fours, chaudières, échangeurs de chaleur, équipements chimiques et machines industrielles exposé à chaleur extrême et environnements oxydants.
Characteristics of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel connu pour son excellent high-temperature strength, oxidation resistance, and creep resistance. The elevated carbon content provides improved performance in prolonged high-temperature applications, especially compared to standard 310 stainless steel.
1. High-Temperature Strength
Maintains mechanical integrity at very high temperatures.
Suitable for continuous service up to approximately 1030°C (1885°F) et une exposition intermittente jusqu'à 1100°C (2010°F).
Higher carbon content enhances creep resistance for prolonged high-temperature operation.
2. Oxidation and Scaling Resistance
Forme stable chromium oxide layer that protects against scaling in oxidizing atmospheres.
Performe bien dans furnace, boiler, and thermal processing applications.
3. Corrosion Resistance
Bonne résistance à general corrosion in oxidizing environments.
Titanium and other stabilizing elements prevent sensitization, minimizing intergranular corrosion in welded components.
4. Mechanical Properties
Excellent ductility and toughness even at elevated temperatures.
Maintains structural stability under thermal stress and high loads.
5. Fabrication and Weldability
Can be welded using conventional methods, though careful control of heat input is recommended to avoid excessive grain growth.
May require post-weld heat treatment in certain high-temperature applications.
6. Applications Related to Characteristics
Composants de four et équipement de traitement thermique
Chaudières, échangeurs de chaleur et machines de traitement thermique
Aerospace and automotive components exposed to high temperatures
Industrial piping and structural parts for high-temperature service
Résumé
310H stainless steel is characterized by high-temperature strength, creep resistance, oxidation resistance, and good weldability. Son high-carbon, austenitic structure en fait, il est idéal pour furnaces, boilers, heat exchangers, chemical processing equipment, and other industrial applications exposé à extreme heat.
Informations supplémentaires
Fabrication
Fabrication of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel avec excellent high-temperature strength, oxidation resistance, and creep resistance. Fabrication techniques are similar to other austenitic stainless steels, but attention must be paid to high-temperature performance, weldability, and work hardening.
1. Formation
Travail à froid :
Can be bent, rolled, or deep-drawn, but work hardens rapidly.
Un recuit intermédiaire peut être nécessaire pour un formage poussé afin de restaurer la ductilité.
Travail à chaud :
Performed at 1150–900°C (2100–1650°F) to reduce work hardening and improve formability.
Suitable for forging, rolling, and extrusion of large or complex parts.
2. Soudage
Can be welded using TIG, MIG, SMAW, or FCAW.
High-carbon content increases the risk of sensitization in some cases; preheating and controlled heat input may be recommended.
Post-weld solution annealing can restore high-temperature properties and reduce residual stresses.
3. Usinage
L'usinabilité est modéré, with rapid work hardening.
Utiliser outils en carbure tranchants, proper feed rates, and coolant for best results.
Suitable for industrial components requiring precision fabrication.
4. Traitements après fabrication
Recuit Restaure la ductilité et soulage les contraintes dues à l'écrouissage ou au soudage.
Décapage ou passivation Removes scale or oxide layers and improves corrosion resistance.
5. Applications liées à la fabrication
Composants de four, équipements de traitement thermique et pièces de four.
Boilers, heat exchangers, and industrial piping
Aerospace and automotive components exposed to high-temperature service
Structural parts for chemical, petrochemical, and power generation industries
Résumé
310H stainless steel is highly fabricable using conventional forming, welding, and machining techniques. Careful control of heat input, work hardening, and post-fabrication treatments ensures high-temperature strength, corrosion resistance, and dimensional stability for furnaces, boilers, heat exchangers, and industrial machinery.
Soudabilité
Weldability of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel avec excellent high-temperature strength and oxidation resistance. Its weldability is good, but the high carbon content requires careful control of welding procedures to maintain mechanical properties and corrosion resistance.
1. General Weldability
Peut être soudé par les méthodes de soudage par fusion standard :
TIG (GTAW)
MIG (GMAW)
SMAW (Shielded Metal Arc Welding)
Soudage à fil fourré
Suitable for joining components in high-temperature and industrial applications.
2. Considerations for Welding
High carbon content increases the risk of sensibilisation, which can lead to intergranular corrosion if exposed to corrosive environments.
Controlled heat input and preheating may be required for thick sections to minimize distortion and reduce residual stresses.
Utiliser correctement métaux d'apport (commonly 310 or 310H) to maintain high-temperature properties and corrosion resistance.
3. Post-Weld Treatment
Traitement de mise en solution may be applied to restore high-temperature strength and ductility.
Décapage et passivation can remove surface oxides formed during welding and improve corrosion resistance.
4. Applications relatives à la soudabilité
Composants de four et de fourneau
Échangeurs de chaleur et pièces de chaudière
High-temperature piping and tanks in chemical and petrochemical industries
Industrial structural parts requiring welded joints for high-temperature service
Résumé
310H stainless steel has bonne soudabilité using standard techniques, but attention must be paid to carbon content, heat input, and post-weld treatments. Proper welding ensures strong, corrosion-resistant joints suitable for high-temperature industrial, chemical, and power generation applications.
Usinabilité
Machinability of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel avec excellent high-temperature strength and oxidation resistance. Like other austenitic stainless steels, it exhibits moderate to low machinability due to its tendency to work harden rapidly.
1. Écrouissage
310H stainless steel work hardens quickly, especially during light cuts or interrupted cuts.
Excessive work hardening can cause l'usure de l'outil, une mauvaise finition de surface et des inexactitudes dimensionnelles.
Utiliser outils de coupe tranchants and proper feeds to minimize work hardening.
2. Recommandations d'outils
Outils en carbure sont préférés pour une coupe efficace et une durée de vie prolongée de l'outil.
High-speed steel (HSS) tools may be used at lower cutting speeds.
Ensure rigid fixturing to reduce vibration and improve machining accuracy.
3. Conditions de coupe
Vitesses de coupe modérées à faibles are recommended to prevent overheating.
Use adequate liquide de refroidissement ou lubrification to dissipate heat and reduce tool wear.
Employ proper feed rates and depth of cut to maintain surface quality.
4. Formation des copeaux
Produit copeaux longs et ductiles due to the austenitic structure.
Utiliser chip breakers or controlled cutting techniques pour gérer efficacement les jetons.
5. Applications liées à l'usinabilité
Composants industriels nécessitant high-temperature performance and corrosion resistance
Heat exchangers, boiler components, and furnace parts
Composants haute température aérospatiaux et automobiles
Chemical processing equipment requiring precise machining
Résumé
310H stainless steel has usinabilité moyenne, with a high tendency to work harden. Using proper tooling, cutting conditions, and coolant ensures efficient machining and good surface finish. Its combination of usinabilité, résistance à haute température et résistance à la corrosion le rend adapté à industrial, chemical, power generation, and high-temperature applications.
Résistance à la corrosion
Corrosion Resistance of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel connu pour son excellente résistance à la corrosion, notamment en environments à haute température et oxydants. Its chemical composition ensures protection against various forms of corrosion while maintaining mechanical integrity under thermal stress.
1. Résistance générale à la corrosion
Résiste oxydation et calamine in air and industrial atmospheres at elevated temperatures.
Performe bien dans environnements chimiques doux.
Suitable for long-term exposure in industrial, chemical, and petrochemical applications.
2. High-Temperature Corrosion Resistance
Titanium stabilization and high chromium content help prevent sensibilisation et corrosion intergranulaire after welding or heat treatment.
Can withstand oxidizing environments at temperatures up to 1030°C (1885°F) continuous and 1100°C (2010°F) intermittent.
Forme un stable couche d'oxyde de chrome that protects against scaling and localized attack.
3. Résistance à la corrosion localisée
Bonne résistance à corrosion par crevasses et corrosion par piqûres under oxidizing conditions.
Moins adapté à environnements riches en chlorures à hautes températures, où la fissuration par corrosion sous contrainte peut se produire.
4. Applications liées à la résistance à la corrosion
Composants de four et de fourneau
Heat exchangers and boilers in chemical and petrochemical industries
High-temperature piping and tanks
Aerospace and automotive components exposed to oxidizing gases or exhaust
Résumé
310H stainless steel offers excellente résistance à la corrosion, notamment dans environments à haute température et oxydants. Titanium stabilization and high chromium content ensure resistance to intergranular corrosion and scaling, making 310H ideal for chaudières, échangeurs de chaleur et équipements industriels exposed to extreme heat.
Travail à froid
Cold Working of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel avec bonne ductilité, permettant divers travail à froid. Cold working increases strength through écrouissage but requires careful handling due to the steel’s high-carbon and austenitic structure.
1. Procédés de travail de base
Pliage et Formage : Suitable for shaping furnace parts, heat exchangers, and piping.
Roulement : Produces sheets, strips, and coils.
Emboutissage et estampage : Used for containers, trays, and intricate components.
Poinçonnage et cisaillage : Applicable for industrial and chemical equipment components.
2. Durcissement par travail
310H stainless steel le travail durcit rapidement, increasing tensile and yield strength during deformation.
Excessive cold working may reduce ductility.
Recuit intermédiaire is recommended after extensive forming to restore ductility and relieve stresses.
3. Considérations relatives à la fabrication
Appliquer déformation progressive pour éviter de fissurer ou de surmener le matériau.
Use proper tooling, lubrication, and support to maintain surface finish and dimensional accuracy.
Les composants travaillés à froid peuvent nécessiter soulagement du stress if used in high-temperature or structural applications.
4. Applications liées à l'usinage à froid
Composants de four et équipement de traitement thermique
Industrial piping, tanks, and structural parts for chemical and petrochemical applications
Composants nécessitant une résistance à la corrosion et une stabilité dimensionnelle après formage
Résumé
310H stainless steel exhibits bonnes caractéristiques de travail à froid, allowing bending, rolling, deep drawing, and stamping. Cold working improves strength through écrouissage tout en conservant une résistance à la corrosion, ce qui le rend adapté à fours, chaudières, échangeurs de chaleur et autres applications industrielles à haute température.
Traitement thermique
Heat Treatment of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel conçu pour high-temperature applications. Its heat treatment is primarily aimed at relieving stresses, restoring ductility, and optimizing high-temperature performance, rather than increasing hardness, as austenitic stainless steels are non trempable par traitement thermique conventionnel.
1. Recuit de mise en solution
Objet : Restore ductility, relieve residual stresses from fabrication or welding, and maintain high-temperature strength.
Gamme de température : 1040–1120°C (1900–2050°F)
Refroidissement Rapid air or water quenching to preserve corrosion resistance and prevent sensitization.
2. Gestion du stress
Objet : Reduce residual stresses from welding, cold working, or machining.
Gamme de température : 450–650 °C (840–1200 °F)
Améliore stabilité dimensionnelle and reduces risk of stress-related cracking.
3. Effets du traitement thermique
Restaure ductilité et ténacité dans les zones écrouies ou soudées.
Soulage contraintes internes, améliorant les performances à haute température.
Does not significantly increase strength, as 310H is not precipitation-hardenable.
4. Surface Treatment Post Heat
Picklage ou passivation may be applied after heat treatment to remove scale or oxide layers and restore the protective chromium oxide surface.
5. Applications liées au traitement thermique
Composants de four et de fourneau
Échangeurs de chaleur et pièces de chaudière
Tuyauterie industrielle et réservoirs exposés à des températures élevées
Chemical, petrochemical, and power generation equipment requiring thermal stability
Résumé
Heat treatment of 310H stainless steel focuses on recuit de mise en solution et détente des contraintes, en maintenant ductilité, résistance à la corrosion et performance à haute température. Un traitement thermique approprié garantit un fonctionnement fiable dans fours, chaudières, échangeurs de chaleur et autres applications industrielles à haute température.
Résistance à la chaleur
Heat Resistance of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel conçu pour excellent high-temperature strength and oxidation resistance. Its high carbon content provides enhanced creep resistance for prolonged service at elevated temperatures.
1. Température de service continue
Suitable for continuous service in oxidizing atmospheres up to 1030°C (1885°F).
Maintient mechanical strength, creep resistance, and corrosion resistance à températures élevées.
2. Exposition intermittente
Can withstand short-term or intermittent exposure up to 1100°C (2010°F) without significant scaling or degradation.
Suitable for components exposed to thermal cycling or fluctuating high temperatures.
3. Résistance à l'oxydation et à la formation de calamine
Forme un stable couche d'oxyde de chrome that protects against oxidation and scaling.
Titanium stabilization and high chromium content prevent sensibilisation and intergranular corrosion after welding or high-temperature service.
4. Limites
Not recommended for prolonged exposure to high-chloride environments, where stress corrosion cracking may occur.
Les chocs thermiques extrêmes doivent être évités pour prévenir fatigue thermique.
5. Applications liées à la résistance à la chaleur
Composants de four et de fourneau
Heat exchangers, boilers, and thermal processing equipment
Petrochemical and chemical industry high-temperature piping and tanks
Aerospace and automotive components exposed to extreme heat
Résumé
310H stainless steel provides excellente résistance à la chaleur, maintaining strength, creep resistance, and corrosion resistance at elevated temperatures up to 1030°C continuous and 1100°C intermittent. Its combination of oxidation resistance and high-temperature performance en fait, il est idéal pour industrial, chemical, petrochemical, and high-temperature applications.
Travail à chaud
Hot Working of 310H Stainless Steel
310H stainless steel est un high-carbon, austenitic stainless steel avec excellent high-temperature strength and oxidation resistance. Hot working allows the steel to be shaped and formed at elevated temperatures while minimizing écrouissage and preserving mechanical and corrosion-resistant properties.
1. Température de travail à chaud recommandée
Plage de travail à chaud : 1150–900°C (2100–1650°F).
Maintaining proper temperature prevents croissance du grain, ensures uniform mechanical properties, and preserves high-temperature performance.
2. Procédés de travail à chaud
Laminage à chaud : Produit des tôles, des plaques et des bandes d'épaisseur uniforme.
Forgeage Suitable for structural and high-temperature components.
Extrusion : Permet la production de barres, de tubes et de profilés complexes.
Formage à chaud etPressage. Permet le façonnage de pièces grandes ou complexes avec un risque minimal de fissures.
3. Avantages du travail à chaud
Réduit écrouissage comparé à l'usinage à froid.
Améliore ductilité, ténacité et aptitude à la déformation.
Allows production of composants larges, épais ou complexes for high-temperature service.
4. Traitements post-forge
Recuit peuvent être appliqués pour soulager les contraintes résiduelles et restaurer des propriétés mécaniques uniformes.
Picklage ou passivation improves surface corrosion resistance after hot working.
5. Applications liées au travail à chaud
Composants de four et de fourneau
Chaudières, échangeurs de chaleur et tuyauteries haute température
Équipement industriel pour les procédés chimiques et pétrochimiques
Pièces aérospatiales et automobiles nécessitant des performances à haute température
Résumé
310H stainless steel exhibits excellentes caractéristiques de travail à chaud, permettant le forgeage, le laminage, l'extrusion et le façonnage à 1150–900°C. Hot working enhances ductility, reduces work hardening, and enables the production of parts for fours, chaudières, échangeurs de chaleur et applications industrielles à haute température.