Aluminium, Commercial Alloy
5754 H22 Sheet & Plate
Excellent resistance to corrosion, especially seawater. Ideal in the marine, nuclear, chemical and oil & gas industries.
Aluminium alloy 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres such as marine, nuclear, chemical, oil & gas industry applications.
It has higher strength than 5251. This high strength makes 5754 highly suited to flooring applications.
Plate can be cut to customer requirements. Contact your local Service Centre for further details.
Please note that mechanical properties shown are for H22.
DOWNLOAD PDF
Range
PLEASE NOTE
If you do not see what you are looking for, please contact your local service centre with your specific requirements.
5754 H22 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA | 5754-H22 |
| UNS | International | A95754 (5754-H22) |
| EN / DIN | Europe | EN AW-5754-H22 / 3.3535 |
| EN Name | Europe | AlMg3-H22 |
| GB | China | 5754-H22 |
| BS | UK | 5754-H22 (sheet / plate) |
| AFNOR | France | A-G3M-H22 |
Properties
Chemical Composition
Alloy 5754
| Chemical Element | % Present |
| Manganese (Mn) | 0.00 - 0.50 |
| Iron (Fe) | 0.00 - 0.40 |
| Magnesium (Mg) | 2.60 - 3.60 |
| Silicon (Si) | 0.00 - 0.40 |
| Chromium (Cr) | 0.00 - 0.30 |
| Copper (Cu) | 0.00 - 0.10 |
| Manganese + Chromium (Mn+Cr) | 0.10 - 0.60 |
| Other (Each) | 0.00 - 0.05 |
| Others (Total) | 0.00 - 0.15 |
| Titanium (Ti) | 0.00 - 0.15 |
| Zinc (Zn) | 0.00 - 0.20 |
| Aluminium (Al) | Balance |
Mechanical Properties
Sheet & Plate 0.2mm to 40mm
| Mechanical Property | Value |
| Proof Stress | 130 Min MPa |
| Tensile Strength | 220 - 270 MPa |
| Hardness Brinell | 63 HB |
| Elongation A50 mm | 7 Min % |
General Physical Properties
| Physical Property | Value |
| Density | 2.66 g/cm³ |
| Melting Point | 600 °C |
| Thermal Expansion | 24 x 10-6/K |
| Modulus of Elasticity | 68 GPa |
| Thermal Conductivity | 147 W/m.K |
| Electrical Resistivity | 0.049 x 10-6 Ω .m |
Applications
- High strength aerospace components
- Military vehicles
- Bridges
- Weapons manufacture
- Structural applications
Characteristics
- Machinability of aluminium alloy 2014A is very good.
- Resistance to atmospheric attack is poor especially when exposed to water or salt environments. To protect against atmospheric corrosion in storage, lightly coat with lanolin based protective oil.
- Good hard anodising capability
- Good strength levels after heat treatment
Additional Information
Fabrication
| Process | Rating |
| Workability - Cold | Very Good |
| Machinability | Average |
Weldability
| Process | Rating |
| Weldability - Gas | Excellent |
| Weldability - Arc | Excellent |
| Weldability - Resistance | Excellent |
| Brazability | Poor |