High quality general purpose aluminium alloy.
Aluminium alloy 4015 is a high quality general purpose alloy. It is a close relation to 3103 AlMn alloy, but with a higher silicon content.
This alloy can be welded, anodized* or painted. (*It should be noted that the anodized finish of alloy 4015 will be much darker and less reflective that on alloys 1050 or 3103 so this is not recommended for decorative applications).
Many users now prefer to use alloy 4015 having switched from other alloys such as 1050 and 3103.
Please note that the mechanical properties quoted are for H14 temper.
PDF İNDİR
Menzil
LÜTFEN DİKKAT
Aradığınız şeyi göremiyorsanız, lütfen yerel servis merkezi özel gereksinimlerinizle.
4015 H14 Aluminium Related Specifications
| Sistem / Standart | Ülke / Bölge | Sınıf / Görevlendirme |
| AA | ABD | 4015-H14 |
| UNS | Uluslararası | A94015 (4015-H14) |
| EN / DIN | Avrupa | EN AW-4015-H14 |
| EN Adı | Avrupa | AlSi2Mn-H14 |
Özellikler
Kimyasal Bileşim
Alloy 4015
| Kimyasal Element | % Mevcut |
| Demir (Fe) | 0.00 - 0.70 |
| Bakır (Cu) | 0.00 - 0.20 |
| Magnezyum (Mg) | 0.10 - 0.50 |
| Silisyum (Si) | 1.40 - 2.20 |
| Çinko (Zn) | 0.00 - 0.20 |
| Manganez (Mn) | 0.60 - 1.20 |
| Diğer (Her biri) | 0.00 - 0.05 |
| Diğerleri (Toplam) | 0.00 - 0.15 |
| Alüminyum (Al) | Denge |
Mekanik Özellikler
Sheet 0.2mm to 3.00mm
| Mekanik Mülkiyet | Değer |
| Çekme Dayanımı | 150 - 200 MPa |
| Kanıt Stres | 120 Min MPa |
| Sertlik Brinell | 50 HB |
Genel Fiziksel Özellikler
| Fiziksel Özellikler | Değer |
| Yoğunluk | 2.72 g/cm³ |
| Erime Noktası | 600 °C |
| Termal Genleşme | 24 x 10-6/K |
| Elastisite Modülü | 70 GPa |
| Termal İletkenlik | 150-200 W/m.K |
| Elektriksel Dirençlilik | 0.023-0.029 x 10-6 Ω .m |
Uygulamalar
- Industry application include:
- Building
- Food
- Transport
- Packaging
Özellikler
- Good ductility
- Good mechanical strength
- Similar corrosion resistance to the 3000 series alloys
- Suitable for most applications in mill finish or painted
- Not recommended for use in aggressive environments
Ek Bilgi
Fabrikasyon
Corresponds to alloy 3103 in same temper but may not be a direct equivalent.
r/t performance dependent upon thickness – approx figures for H12 r/t min bend radius for 180 degree bend are shown below:
Thickness
0.5-0.8mm: r/t 0.0
0.8-1.5mm: r/t 1.0
1.5-3.0mm: r/t 2.0
| Süreç | Değerlendirme |
| Workability Cold | Çok iyi |
| İşlenebilirlik | Acceptable |
| Kaynaklanabilirlik - Gaz | Çok iyi |
| Kaynaklanabilirlik - Ark | Çok iyi |
| Kaynaklanabilirlik - Direnç | Good |
| Yüzsüzlük | Çok iyi |
| Solderability | Very good |
Kaynaklanabilirlik
Suitable for MIG and TIG welding using normal aluminium welding conditions. Recommended welding wire is 4043 (Al Si5).