Alüminyum, Ticari Alaşım
Aluminium 6082 T6 Bar & Extrusions
Structural aluminium alloy with the highest strength in the 6000 series.
Aluminium alloy 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of the 6000 series alloys and is known as a structural alloy.
In plate form, 6082 is the alloy most commonly used for machining. As a relatively new alloy, the higher strength of 6082 has seen it replace 6061 in many applications. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy.
It is difficult to produce thin walled, complicated extrusion shapes in alloy 6082. The extruded surface finish is not as smooth as other similar strength alloys in the 6000 series.In the T6 and T651 temper, alloy 6082 machines well and produces tight coils of swarf when chip breakers are used.
PDF İNDİR
Menzil
Round bar is supplied in the T6511 temper.
| Product Form | Size Range | Size Range |
| From | To | |
| Round Bar (Imperial) | 3⁄16" | 16" |
| Round Bar (Metric) | 6.0mm | 50.0mm |
| Flat Bar | 3⁄8" x 1⁄8" | 6" x 1" |
| Square Bar | 1⁄4" | 4" |
| Square Box Section | 1⁄2" x 1⁄2" x 16swg | 4" x 4" x 1⁄4 |
| Rectangular Box Section | 1" x 1⁄2" x 16swg | 6" x 3" x 3⁄8" |
| Tube | 3⁄8" OD x 16swg | 6 1⁄2" OD x 1⁄4" |
| Channel | 3⁄8" x 3⁄8 2 x 1⁄16" | 10" x 3" x 3⁄8" x 1⁄2" |
| Tee Section | 1⁄2" x 1⁄2" x 1⁄16" | 3" x 3" x 3⁄8" |
| Equal Angle | 3⁄8" x 3⁄8" x 1⁄16" | 6" x 6" x 1⁄2" |
| Unequal Angle | 3⁄4" x 1⁄4" x 1⁄16" | 6" x 3" x 3⁄8" |
LÜTFEN DİKKAT
Aradığınız şeyi göremiyorsanız, lütfen yerel servis merkezi özel gereksinimlerinizle.
6082 T6 Aluminium Related Specifications
| Sistem / Standart | Ülke / Bölge | Sınıf / Görevlendirme |
| AA | ABD | 6082-T6 |
| UNS | Uluslararası | A96082 (6082-T6) |
| EN / DIN | Avrupa | EN AW-6082-T6 / 3.2315 |
| EN Adı | Avrupa | AlSi1MgMn-T6 |
| GB | Çin | 6082-T6 |
| BS | BIRLEŞIK KRALLIK | 6082-T6 (HE30-T6, equivalent) |
Özellikler
Kimyasal Bileşim
Alloy 6082
| Kimyasal Element | % Mevcut |
| Manganez (Mn) | 0.40 - 1.00 |
| Demir (Fe) | 0.00 - 0.50 |
| Magnezyum (Mg) | 0.60 - 1.20 |
| Silisyum (Si) | 0.70 - 1.30 |
| Bakır (Cu) | 0.00 - 0.10 |
| Çinko (Zn) | 0.00 - 0.20 |
| Titanyum (Ti) | 0.00 - 0.10 |
| Krom (Cr) | 0.00 - 0.25 |
| Diğer (Her biri) | 0.00 - 0.05 |
| Diğerleri (Toplam) | 0.00 - 0.15 |
| Alüminyum (Al) | Denge |
Mekanik Özellikler
Open & Hollow Profile 5mm to 25mm Wall Thickness
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 260 Min MPa |
| Çekme Dayanımı | 310 Min MPa |
| Elongation A50 mm | 8 Min % |
| Sertlik Brinell | 95 HB |
| Elongation A | 10 Min % |
Open & Hollow Profile Up To 5mm Wall Thickness
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 250 Min MPa |
| Çekme Dayanımı | 290 Min MPa |
| Elongation A50 mm | 6 Min % |
| Sertlik Brinell | 95 HB |
| Elongation A | 8 Min % |
Tube 5mm to 25mm Wall Thickness
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 260 Min MPa |
| Çekme Dayanımı | 310 Min MPa |
| Elongation A50 mm | 8 Min % |
| Sertlik Brinell | 95 HB |
| Elongation A | 10 Min % |
Tube Up to 5mm Wall Thickness
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 250 Min MPa |
| Çekme Dayanımı | 290 Min MPa |
| Elongation A50 mm | 6 Min % |
| Sertlik Brinell | 95 HB |
| Elongation A | 8 Min % |
Bar 200mm to 250mm Dia. & A/F
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 200 Min MPa |
| Çekme Dayanımı | 270 Min MPa |
| Sertlik Brinell | 95 HB |
| Elongation A | 6 Min % |
Bar 150mm to 200mm Dia. & A/F
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 240 Min MPa |
| Çekme Dayanımı | 280 Min MPa |
| Sertlik Brinell | 95 HB |
| Elongation A | 6 Min % |
Rod & Bar 20mm to 150mm Dia. & A/F
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 260 Min MPa |
| Çekme Dayanımı | 310 Min MPa |
| Sertlik Brinell | 95 HB |
| Elongation A | 8 Min % |
Rod & Bar Up to 20mm Dia. & A/F
| Mekanik Mülkiyet | Değer |
| Kanıt Stres | 250 Min MPa |
| Çekme Dayanımı | 295 Min MPa |
| Elongation A50 mm | 6 Min % |
| Sertlik Brinell | 95 HB |
| Elongation A | 8 Min % |
Genel Fiziksel Özellikler
| Fiziksel Özellikler | Değer |
| Yoğunluk | 2.70 g/cm³ |
| Erime Noktası | 555 °C |
| Termal Genleşme | 24 x 10-6/K |
| Elastisite Modülü | 70 GPa |
| Termal İletkenlik | 180 W/m.K |
| Elektriksel Dirençlilik | 0.038 x 10-6 Ω .m |
Uygulamalar
- Highly stressed applications
- Trusses
- Bridges
- Cranes
- Transport applications
- Ore skips
- Beer barrels
- Milk churns
Özellikler
- Excellent corrosion resistance
- Medium strength
- Good machinability. In the T6 and T651 temper, alloy 6082 machines well and produces tight coils of swarf when chip breakers are used.
- Good weldability
Ek Bilgi
Kaynaklanabilirlik
- 6082 has very good weldability but strength is lowered in the weld zone. When welded to itself, alloy 4043 wire is recommended. If welding 6082 to 7005, then the wire used should be alloy 5356.
| Süreç | Değerlendirme |
| Kaynaklanabilirlik - Gaz | Good |
| Kaynaklanabilirlik - Ark | Good |
| Kaynaklanabilirlik - Direnç | Good |
| Yüzsüzlük | Good |
| Solderability | Good |
Fabrikasyon
| Süreç | Değerlendirme |
| İşlenebilirlik - Soğuk | Good |
| İşlenebilirlik | Good |