Aluminium, Commercial Alloy
2014A T6511 Bar & Extrusion
A high strength aluminium alloy which retains its strength after heat treatment.
A high strength 4 to 5% copper alloy produced in extruded bar and profile form, in the fully heat-treated condition (solution heat-treated & artificially aged).
Normally stocked in the T6511 condition (stress relieved by controlled stretching) Except for sizes under 10mm diameter and over 203.2mm diameter. (T6 only). Over 203.mm diameter is manufactured to chemical composition only.
DOWNLOAD PDF
Range
| Product Form | Imperial Sizes | Metric Sizes |
| Round Bar | 3⁄16"- 16" | 6mm - 50mm |
PLEASE NOTE
If you do not see what you are looking for, please contact your local service centre with your specific requirements.
2014A T6511 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA | 2014A-T6511 |
| UNS | International | A92014 (2014A-T6511) |
| EN / DIN | Europe | EN AW-2014A / WNr 3.1255-T6511 |
| EN Name | Europe | AlCu4SiMg(A)-T6511 |
| ASTM B221 | USA | 2014A-T6511 extruded bars / rods / shapes |
| GB | China | 2A14-T6511 |
| JIS | Japan | A2014-T6511 |
| BS (Aerospace) | UK | L168 (2014A-T6511 bars & sections) |
| AFNOR | France | A-U4SG-T6511 |
Properties
Chemical Composition
Alloy 2014
| Chemical Element | % Present |
| Silicon (Si) | 0.50 - 0.90 |
| Iron (Fe) | 0.50 max |
| Copper (Cu) | 3.90 - 5.00 |
| Zinc (Zn) | 0.25 max |
| Manganese (Mn) | 0.40 - 1.20 |
| Magnesium (Mg) | 0.20 - 0.80 |
| Titanium (Ti) | 0.15 max |
| Others (Total) | 0.15 max |
| Chromium (Cr) | 0.10 max |
| Nickel (Ni) | 0.10 max |
| Other (Each) | 0.05 max |
| Titanium + Zirconium (Ti+Zr) | 0.20 max |
| Aluminium (Al) | Balance |
Mechanical Properties
Profile 25mm to 75mm Wall Thickness
| Mechanical Property | Value |
| Proof Stress | 415 Min MPa |
| Tensile Strength | 460 Min MPa |
| Hardness Brinell | 140 HB |
| Elongation A | 7 Min % |
Profile Up to 25mm Wall Thickness
| Mechanical Property | Value |
| Proof Stress | 370 Min MPa |
| Tensile Strength | 415 Min MPa |
| Elongation A50 mm | 5 Min % |
| Hardness Brinell | 140 HB |
| Elongation A | 7 Min % |
Tube 10mm to 40mm Wall Thickness
| Mechanical Property | Value |
| Proof Stress | 400 Min MPa |
| Tensile Strength | 450 Min MPa |
| Elongation A50 mm | 4 Min % |
| Hardness Brinell | 140 HB |
| Elongation A | 6 Min % |
Tube Up to 10mm Wall Thickness
| Mechanical Property | Value |
| Proof Stress | 370 Min MPa |
| Tensile Strength | 415 Min MPa |
| Hardness Brinell | 140 HB |
| Elongation A | 7 Min % |
| Elongation A50 mm | 5 Min % |
Bar 150mm to 200mm Dia. & A/F
| Mechanical Property | Value |
| Proof Stress | 350 Min MPa |
| Tensile Strength | 430 Min MPa |
| Hardness Brinell | 140 HB |
| Elongation A | 6 Min % |
Bar 75mm to 150mm Dia. & A/F
| Mechanical Property | Value |
| Proof Stress | 420 Min MPa |
| Tensile Strength | 465 Min MPa |
| Hardness Brinell | 140 HB |
| Elongation A | 7 Min % |
Bar 25mm to 75mm Dia. & A/F
| Mechanical Property | Value |
| Proof Stress | 415 Min MPa |
| Tensile Strength | 460 Min MPa |
| Hardness Brinell | 140 HB |
| Elongation A | 7 Min % |
Rod & Bar Up to 25mm Dia. & A/F
| Mechanical Property | Value |
| Tensile Strength | 415 Min MPa |
| Proof Stress | 370 Min MPa |
| Hardness Brinell | 140 HB |
| Elongation A50 mm | 5 Min % |
| Elongation A | 6 Min % |
General Physical Properties
| Physical Property | Value |
| Density | 2.82 g/cm³ |
| Modulus of Elasticity | 71 GPa |
| Electrical Resistivity | 0.045 x 10-6 Ω .m |
| Thermal Conductivity | 138 W/m.K |
| Thermal Expansion | 23 x 10-6/K |
| Melting Point | 535 °C |
Applications
- High strength aerospace components
- Military vehicles
- Bridges
- Weapons manufacture
- Structural applications
Characteristics
- Machinability of aluminium alloy 2014A is very good.
- Resistance to atmospheric attack is poor especially when exposed to water or salt environments. To protect against atmospheric corrosion in storage, lightly coat with lanolin based protective oil.
- Good hard anodising capability
- Good strength levels after heat treatment
Additional Information
Weldability
| Process | Rating |
| Brazing & Soldering | Not Recommended |
| Oxygen | Not Recommended |
| Inert Gas | Not Recommended |
| Resistance, Spot, Beam | Excellent |
Surface Treatment
| Process | Rating |
| Protective Anodising | Fair |
| Bright Anodising | Unsuitable |
| Hard Anodising | Good |
| Colour Anodising | Fair (Dark colours only) |
| Plating | Very Good |
Corrosion Resistance
- Resistance to atmospheric attack: Poor, especially when exposed to water or salt environments.
- To protect against atmospheric corrosion in storage, lightly coat with Lanolin based protective oil.