Aluminium, Commercial Alloy
Aluminium 6082 T6 Bar & Extrusions
Lega di alluminio strutturale con la massima resistenza della serie 6000.
Aluminium alloy 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of the 6000 series alloys and is known as a structural alloy.
In plate form, 6082 is the alloy most commonly used for machining. As a relatively new alloy, the higher strength of 6082 has seen it replace 6061 in many applications. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy.
It is difficult to produce thin walled, complicated extrusion shapes in alloy 6082. The extruded surface finish is not as smooth as other similar strength alloys in the 6000 series.In the T6 and T651 temper, alloy 6082 machines well and produces tight coils of swarf when chip breakers are used.
SCARICA IL PDF
Gamma
Round bar is supplied in the T6511 temper.
| Modulo Prodotto | Size Range | Size Range |
| From | To | |
| Round Bar (Imperial) | 3⁄16" | 16" |
| Round Bar (Metric) | 6.0mm | 50.0mm |
| Flat Bar | 3⁄8" x 1⁄8" | 6" x 1" |
| Square Bar | 1⁄4" | 4" |
| Square Box Section | 1⁄2" x 1⁄2" x 16swg | 4" x 4" x 1⁄4 |
| Rectangular Box Section | 1" x 1⁄2" x 16swg | 6" x 3" x 3⁄8" |
| Tubo | 3⁄8" OD x 16swg | 6 1⁄2" OD x 1⁄4" |
| Channel | 3⁄8" x 3⁄8 2 x 1⁄16" | 10" x 3" x 3⁄8" x 1⁄2" |
| Tee Section | 1⁄2" x 1⁄2" x 1⁄16" | 3" x 3" x 3⁄8" |
| Equal Angle | 3⁄8" x 3⁄8" x 1⁄16" | 6" x 6" x 1⁄2" |
| Unequal Angle | 3⁄4" x 1⁄4" x 1⁄16" | 6" x 3" x 3⁄8" |
NOTA BENE
Se non vedi quello che stai cercando, contatta il tuo Centro servizi locale con le tue specifiche esigenze.
6082 T6 Aluminium Related Specifications
| Sistema / Standard | Paese / Regione | Grado / Qualifica |
| AA | Stati Uniti d'America | 6082-T6 |
| UNS | Internazionale | A96082 (6082-T6) |
| IT / DIN | Europa | EN AW-6082-T6 / 3.2315 |
| Nome | Europa | AlSi1MgMn-T6 |
| Regno Unito | Cina | 6082-T6 |
| BS | REGNO UNITO | 6082-T6 (HE30-T6, equivalent) |
Proprietà
Composizione chimica
Alloy 6082
| Elemento Chimico | % Presente |
| Manganese (Mn) | 0.40 - 1.00 |
| Ferro (Fe) | 0.00 - 0.50 |
| Magnesium (Mg) | 0.60 - 1.20 |
| Silicio (Si) | 0.70 - 1.30 |
| Rame (Cu) | 0.00 - 0.10 |
| Zinc (Zn) | 0.00 - 0.20 |
| Titanium (Ti) | 0.00 - 0.10 |
| Cromo (Cr) | 0.00 - 0.25 |
| Other (Each) | 0.00 - 0.05 |
| Others (Total) | 0.00 - 0.15 |
| Aluminium (Al) | Equilibrio |
Proprietà Meccaniche
Open & Hollow Profile 5mm to 25mm Wall Thickness
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 260 Min MPa |
| Resistenza alla trazione | 310 Min MPa |
| Allungamento A50 mm | 8 Min % |
| Durezza Brinell | 95 HB |
| Elongation A | 10 Min % |
Open & Hollow Profile Up To 5mm Wall Thickness
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 250 Min MPa |
| Resistenza alla trazione | 290 Min MPa |
| Allungamento A50 mm | 6 Min % |
| Durezza Brinell | 95 HB |
| Elongation A | 8 Min % |
Tube 5mm to 25mm Wall Thickness
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 260 Min MPa |
| Resistenza alla trazione | 310 Min MPa |
| Allungamento A50 mm | 8 Min % |
| Durezza Brinell | 95 HB |
| Elongation A | 10 Min % |
Tube Up to 5mm Wall Thickness
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 250 Min MPa |
| Resistenza alla trazione | 290 Min MPa |
| Allungamento A50 mm | 6 Min % |
| Durezza Brinell | 95 HB |
| Elongation A | 8 Min % |
Bar 200mm to 250mm Dia. & A/F
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 200 Min MPa |
| Resistenza alla trazione | 270 Min MPa |
| Durezza Brinell | 95 HB |
| Elongation A | 6 Min % |
Bar 150mm to 200mm Dia. & A/F
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 240 Mpa |
| Resistenza alla trazione | 280 Min MPa |
| Durezza Brinell | 95 HB |
| Elongation A | 6 Min % |
Rod & Bar 20mm to 150mm Dia. & A/F
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 260 Min MPa |
| Resistenza alla trazione | 310 Min MPa |
| Durezza Brinell | 95 HB |
| Elongation A | 8 Min % |
Rod & Bar Up to 20mm Dia. & A/F
| Proprietà meccaniche | Valore |
| Tensione di snervamento | 250 Min MPa |
| Resistenza alla trazione | 295 Min MPa |
| Allungamento A50 mm | 6 Min % |
| Durezza Brinell | 95 HB |
| Elongation A | 8 Min % |
Proprietà fisiche generali
| Proprietà fisica | Valore |
| Densità | 2.70 g/cm³ |
| Punto di fusione | 555 °C |
| Dilatazione termica | 24 x 10-6/K |
| Modulo di elasticità | 70 GPa |
| Conduttività termica | 180 W/m.K |
| Resistività elettrica | 0.038 x 10-6 Ω .m |
Applicazioni
- Highly stressed applications
- Trusses
- Bridges
- Cranes
- Transport applications
- Ore skips
- Beer barrels
- Milk churns
Characteristics
- Excellent corrosion resistance
- Medium strength
- Good machinability. In the T6 and T651 temper, alloy 6082 machines well and produces tight coils of swarf when chip breakers are used.
- Good weldability
Informazioni aggiuntive
Saldabilità
- 6082 has very good weldability but strength is lowered in the weld zone. When welded to itself, alloy 4043 wire is recommended. If welding 6082 to 7005, then the wire used should be alloy 5356.
| Process | Rating |
| Weldability - Gas | Good |
| Weldability - Arc | Good |
| Weldability - Resistance | Good |
| Brazability | Good |
| Solderability | Good |
Fabbricazione
| Process | Rating |
| Workability - Cold | Good |
| Lavorabilità | Good |