Acero inoxidable, austenítico
304 Stainless Steel (S30400)
The most versatile and widely used chromium-nickel (18/8) austenitic stainless steel.
Stainless steel types 1.4301 and 1.4307 are also known as grades 304 and 304L respectively. Type 304 is the most versatile and widely used stainless steel. It is still sometimes referred to by its old name 18/8 which is derived from the nominal composition of type 304 being 18% chromium and 8% nickel.
Tipo 304 stainless steel is an austenitic grade that can be severely deep drawn. This property has resulted in 304 being the dominant grade used in applications like sinks and saucepans.
Type 304L is the low carbon version of 304. It is used in heavy gauge components for improved weldability. Some products such as plate and pipe may be available as “dual certified” material that meets the criteria for both 304 and 304L.
304H, a high carbon content variant, is also available for use at high temperatures.
304 stainless steel is the most widely used austenitic stainless steel, known for its excellent corrosion resistance, good mechanical properties, and versatile fabrication capabilities. It is often used in industrial, architectural, and household applications.
DESCARGAR PDF
Gama
| Forma del producto | Descripción | Medidas métricas | Tamaños imperiales |
| Barra redonda | Bright Drawn H9 | 2,0mm - 25,0mm | 1⁄8" - 1" |
| Barra redonda | Smooth Turned H9/H10 | 25.0mm - 60.0mm | 1" - 3" |
| Flat Bar | Rolled Edge | 12mm x 3mm - 100mm x 12mm | |
| Square Bar | 304S11/S31 | 12mm x 12mm - 50mm x 50mm | |
| Angle | 304S31 | 20mm x 20mm x 3mm - 100mm x 100mm x 10mm | |
| Welded Ornamental Tube | Mirror Polished 600 Grit | 30mm - 50mm | 1⁄2" - 4" |
| Welded Tube | Satin Polished 320 Grit | 16mm - 50mm | 1⁄2" - 2" |
| Tubo cuadrado | Welded, Dull Polished | 12.7mm x 12.7mm - 10mm - 100mm | |
| Handrail Section | Welded, Unannealed, Dull Polished | 42.40mm - 60.30 (2.5mm wall) | 1 1⁄2" - 4 " (3mm wall) |
| Tubo cuadrado | Welded, Unpolished | 12.7mm x 12.7mm - 250mm x 250mm | |
| Tubo rectangular | Welded, Unpolished | 80mm x 40mm - 250mm x 150mm | |
| Tubo rectangular | Welded, Dull Polished | 20mm x 10mm - 150mm x 100mm |
Sheet
| Product Type | Tamaño de hoja | Espesores |
| Sheet 2B Finish | 2000 x 1000 | 0.5mm - 3.0mm |
| Sheet 2B Finish | 2500 x 1250 | 0.5mm - 6.0mm |
| Sheet 2B Finish | 3000 x 1500 | 0.9mm - 3.0mm |
| Sheet 2R (BA) Finish | 2000 x 1000 | 0.5 mm - 2.0 mm |
| Sheet 2R (BA) Finish | 2500 x 1250 | 0.5 mm - 2.0 mm |
| Polished Sheet 240 Silicon | 2000 x 1000 | 0.6mm - 3.0mm |
| Polished Sheet 240 Silicon | 2500 x 1250 | 0.7mm - 6.0mm |
| Polished Sheet 240 Silicon | 3000 x 1500 | 1.0mm - 3.0mm |
| Perforated Sheet (Round Holes) | 2000 x 1000 | 1.0mm - 1.5mm |
| Perforated Sheet (Round Holes) | 2500 x 1250 | 0.7mm - 1.5mm |
| Perforated Sheet (Square Holes) | 2000 x 1000 | 1.5mm |
| CPP Plate ID Finish | 2000 x 1000 | 3.0mm - 6.0mm |
| CPP Plate ID Finish | 2500 x 1250 | 3.0mm - 12.0mm |
| CPP Plate ID Finish | 3000 x 1500 | 3.0mm - 12.0mm |
| CPP Plate ID Finish | 4000 x 2000 | 2.0mm - 12.0mm |
| Qaurto Plate ID Finish | 5" - 125" | - |
| Welded Mesh | 90" x 48" | - |
| Treadplate | 3000 x 1000 | 3.0mm |
| Traedplate | 3000 x 1250 | 4.5mm - 8.0mm |
TENGA EN CUENTA
Si no encuentra lo que busca, póngase en contacto con su centro de servicio local con sus requisitos específicos.
304 Stainless Steel Related Specifications
| Sistema / Estándar | País / Región | Grado / Designación |
| AISI | EE.UU. | 304 |
| UNS | Internacional | S30400 |
| ES / W.Nr. | Europa | 1.4301 |
| ES Nombre | Europa | X5CrNi18-10 |
| ASTM A240 | EE.UU. | 304 (plate, sheet, strip) |
| ASTM A276 | EE.UU. | 304 (bars, shapes) |
| ASTM A213 | EE.UU. | TP304 (boiler / HX tubes) |
| ASTM A312 | EE.UU. | TP304 (seamless pipe) |
| GB | China | 0Cr18Ni9 |
| JIS | Japón | SUS304 |
| BS | Reino Unido | 304S15 / 304S31 |
| AFNOR | Francia | Z7CN18-09 |
Propiedades
Composición química
| Elemento químico | % Presente |
| Carbono (C) | 0.00 - 0.20 |
| Manganeso (Mn) | 0.00 - 1.00 |
| Silicio (Si) | 0.00 - 1.00 |
| Fósforo (P) | 0.00 - 0.04 |
| Azufre (S) | 0.00 - 0.03 |
| Cromo (Cr) | 15.00 - 17.00 |
| Níquel (Ni) | 1.25 - 2.50 |
Propiedades mecánicas
| Propiedad mecánica | Valor |
| Alargamiento A50 mm | 11 % |
| Resistencia a la tracción | 850-1000 MPa |
| Prueba Estrés | 665 MPa |
| Dureza Brinell | 248-302 HB |
Propiedades físicas generales
| Propiedad física | Valor |
| Densidad | 7.8 g/cm³ |
| Módulo de elasticidad | 200 GPa |
| Conductividad térmica | 20.2 W/m.K |
Applications of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico conocida por su excellent corrosion resistance, good mechanical properties, and versatile formability. It is widely used across industrial, household, food, and architectural applications.
1. Food and Beverage Industry
Food processing equipment, tanks, and containers
Brewing, dairy, and pharmaceutical machinery
Piping, valves, and fittings requiring hygienic surfaces
2. Chemical and Petrochemical Industry
Chemical processing equipment and storage tanks
Heat exchangers, condensers, and piping systems
Components exposed to acids, alkalis, and other corrosive environments
3. Household and Kitchen Applications
Sinks, kitchen appliances, and utensils
Decorative trims, handrails, and architectural hardware
4. Industrial and Manufacturing Applications
Pumps, valves, and fasteners in corrosive environments
Machinery and equipment exposed to moisture or mild chemicals
Structural components requiring durability and corrosion resistance
5. Medical and Pharmaceutical Applications
Surgical instruments and medical devices
Laboratory benches and components requiring sterilization
Equipment where hygiene and corrosion resistance are critical
Resumen
304 stainless steel is highly versatile, providing excellent corrosion resistance, strength, and formability. Its applications span food processing, chemical, household, medical, and industrial sectors, making it ideal for environments where durability and hygiene are essential.
Characteristics of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico widely used for its excellent corrosion resistance, good mechanical properties, and versatile formability. It is suitable for a broad range of applications in industrial, household, and architectural environments.
Composición Química
Contiene chromium (18–20%) y nickel (8–10.5%).
Low carbon content ensures good corrosion resistance and weldability.
Trace elements like manganese, silicon, and phosphorus enhance mechanical stability.
2. Resistencia a la corrosión
Excellent resistance to oxidation, atmospheric corrosion, and mild acids.
Rinde bien en indoor, outdoor, and mildly corrosive environments.
Notably resistant to rust and staining, making it ideal for hygiene-critical applications.
3. Propiedades Mecánicas
Alta tensile strength and yield strength.
Excelente ductilidad y tenacidad, even at low temperatures.
Maintains properties over a wide range of temperatures.
4. Fabrication and Formability
Excelente cold working and forming characteristics, suitable for deep drawing, bending, and stamping.
Puede ser welded easily with minimal risk of intergranular corrosion.
Machinable, though slightly less so than 303 stainless steel.
5. Heat and Temperature Resistance
Performs well at moderate temperatures, with intermittent service up to 870 °C (1600 °F).
Continuous service temperatures should remain below 925°C (1700°F).
6. Aplicaciones
Food and beverage processing equipment
Chemical and pharmaceutical machinery
Kitchen appliances, sinks, and household items
Architectural components, handrails, and decorative trims
Resumen
304 stainless steel is characterized by excellent corrosion resistance, good mechanical strength, high ductility, and versatile formability. Its combination of properties makes it ideal for industrial, household, chemical, and architectural applications, particularly where durability, hygiene, and corrosion resistance son importantes.
Información adicional
Fabricación
Fabrication of 304 Stainless Steel
304 stainless steel is a widely used acero inoxidable austenítico conocida por su excellent corrosion resistance and formability. Its fabrication characteristics make it suitable for a wide range of industrial, architectural, and household applications.
1. Formando
Trabajo en frío: 304 can be bent, drawn, stamped, or deep-drawn in the annealed condition.
Trabajo en caliente: Suitable for hot forging, rolling, or extrusion at controlled temperatures (approx. 1010–1120°C / 1850–2050°F).
Work hardens moderately during forming, which may require recocido intermedio for complex shapes.
2. Mecanizado
Machinable with appropriate cutting tools and speeds, though less machinable than 303 stainless steel.
Produces smooth finishes with careful selection of cutting fluids and tool materials.
3. Soldadura
Excellent weldability using TIG, MIG, or resistance welding.
Low carbon content (≤0.08%) minimizes carbide precipitation, reducing the risk of corrosión intergranular in welded areas.
Post-weld annealing or passivation can further enhance corrosion resistance.
4. Surface Finishing
Puede ser polished, brushed, or passivated to improve aesthetics and corrosion resistance.
Suitable for both functional and decorative applications.
5. Advantages of 304 Stainless Steel Fabrication
Versatile forming options (cold or hot working)
Good weldability for assembly of components
Can achieve high-quality surface finishes
Mantiene resistencia a la corrosión after fabrication
6. Aplicaciones
Kitchen and food processing equipment
Architectural panels, handrails, and decorative features
Tanks, piping, and industrial equipment
Medical and pharmaceutical instruments
Resumen
304 stainless steel is highly versatile for fabrication, offering excellent formability, weldability, and surface finish options. These characteristics make it ideal for industrial, architectural, and household applications requiring durability, corrosion resistance, and aesthetic appeal.
Soldabilidad
Weldability of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico widely used for its excellent corrosion resistance and mechanical properties. One of its key advantages is superior weldability, making it suitable for a wide range of industrial, architectural, and household applications.
1. Características generales de soldadura
Easily weldable using standard methods: TIG (GTAW), MIG (GMAW), spot welding, and resistance welding.
Low carbon content (≤0.08%) reduces the risk of corrosión intergranular en la zona afectada por el calor.
Produce strong, corrosion-resistant welds without significant loss of mechanical properties.
2. Técnicas de soldadura
TIG (GTAW): Provides precise control and high-quality welds, ideal for thin sheets and critical applications.
MIG (GMAW): Efficient for thicker materials and high-volume production.
Spot and resistance welding: Suitable for sheet metal assemblies.
3. Materiales de relleno
Commonly use Varillas/alambres de soldadura de acero inoxidable 304 o 308 to maintain corrosion resistance and mechanical integrity.
Selection depends on the specific application and service environment.
4. Preheating and Post-Weld Treatment
Preheating is generally unnecessary due to low carbon content.
Post-weld annealing or passivation can enhance corrosion resistance and restore surface finish if required.
5. Advantages
Excellent weld quality with minimal distortion or cracking.
Mantiene corrosion resistance and mechanical strength in welded areas.
Suitable for both thin sheets and thick sections.
6. Applications Benefiting from Weldability
Kitchen equipment, sinks, and countertops
Piping, tanks, and pressure vessels
Architectural panels, handrails, and decorative structures
Medical and pharmaceutical instruments
Resumen
304 stainless steel is highly weldable, offering strong, corrosion-resistant, and aesthetically acceptable welds. Its low carbon content ensures minimal intergranular corrosion risk, lo que lo hace ideal para industrial, architectural, and household applications requiring both durability and weld integrity.
Maquinabilidad
Machinability of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico well-known for its excellent corrosion resistance and mechanical properties. However, compared to 303 stainless steel, its machinability is moderate, requiring careful tooling and process control.
1. Características de Mecanizado
304 stainless steel el trabajo se endurece rápidamente during machining, which can increase tool wear.
Produce virutas continuas y tenaces, which may require chip breakers or special tooling.
Standard machining speeds must be reduced compared to carbon steels to avoid excessive heat.
2. Recomendaciones sobre herramientas
Materiales de la herramienta: High-speed steel (HSS), carbide, or coated carbide tools are recommended.
Velocidades de corte: Lower than mild steel; increase feed rate gradually to reduce heat buildup.
Coolant/Lubrication: Use cutting fluids to reduce friction, dissipate heat, and improve surface finish.
3. Operaciones de Mecanizado
Giro Requires slower speeds and frequent tool changes; good surface finish achievable.
Milling: Use sharp tools and moderate depth of cut; avoid overheating.
Drilling and Tapping: Pre-drill larger holes and use proper lubricants to prevent galling.
4. Ventajas
Can produce high-quality, corrosion-resistant components with proper machining practices.
Adecuado para precision parts in industrial, food, and chemical processing equipment.
5. Limitations
Less machinable than 303 stainless steel due to the absence of sulfur.
Requires careful tool selection, speed, and lubrication to avoid excessive wear and work hardening.
6. Applications Benefiting from Machinability
Food and beverage processing machinery
Piping, valves, and fittings
Industrial and chemical processing components
Medical and pharmaceutical instruments
Resumen
304 stainless steel has maquinabilidad moderada, requiring appropriate tooling, cutting speeds, and lubrication to achieve precise components. While not as easily machined as 303 stainless steel, it offers excellent corrosion resistance and mechanical properties, lo que lo hace ideal para industrial, medical, and food-processing applications.
Resistencia a la corrosión
Corrosion Resistance of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico conocida por su excelente resistencia a la corrosión, making it one of the most widely used stainless steels in industrial, architectural, and household applications.
1. Resistencia general a la corrosión
Highly resistant to oxidación y corrosión atmosférica.
Rinde bien en indoor and outdoor environments.
Maintains integrity in humid and mildly corrosive conditions.
2. Resistance to Chemicals
Excellent resistance to food acids, alkaline solutions, and many industrial chemicals.
Adecuado para food processing, chemical equipment, and pharmaceutical applications.
Less resistant than 316 stainless steel in chloride-rich or marine environments.
3. Stress and Intergranular Corrosion
Low carbon content (≤0.08%) minimizes carbide precipitation during welding.
Resistente a corrosión intergranular even after welding when properly fabricated.
Sensitive to chloride-induced pitting or crevice corrosion in high-salinity environments.
4. Surface Treatment
Puede ser polished or passivated to improve corrosion resistance.
Surface finishing enhances both appearance and longevity.
5. Applications Benefiting from Corrosion Resistance
Kitchen appliances, sinks, and cookware
Food and beverage processing equipment
Architectural panels, handrails, and decorative structures
Tanks, piping, and industrial machinery
Medical and pharmaceutical instruments
Resumen
304 stainless steel exhibits excelente resistencia a la corrosión in a wide range of environments, including industrial, food processing, and architectural applications. Su low carbon content ensures weldability without compromising corrosion resistance, making it ideal for durable and long-lasting components.
Trabajo en frío
Cold Working of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico widely used for its excellent corrosion resistance, mechanical properties, and formability. Responde bien a trabajo en frío, which can improve strength and hardness but also increases work hardening.
Características del trabajo en frío
Puede ser bent, drawn, stamped, or deep-drawn en el estado recocido.
El trabajo en frío aumenta resistencia y dureza due to strain hardening.
Excessive deformation may reduce ductility and requires careful control.
2. Técnicas
Doblado y conformado Suitable for moderate bends; sharp bends may require intermediate annealing.
Embutición Excellent, especially in thin sheets, due to good ductility.
Rolling or stamping: Can achieve complex shapes with proper tooling and process control.
3. Ventajas
El trabajo en frío mejora resistencia a la tracción y dureza without heat treatment.
Enables production of precision components and complex shapes.
Mantiene resistencia a la corrosión when proper annealing and passivation are applied after severe deformation.
4. Limitaciones
Work hardens quickly, which may require recocido intermedio for extensive forming operations.
Excessive cold working can increase pandeo interno, potentially leading to distortion or cracking in subsequent processes.
5. Applications Benefiting from Cold Working
Architectural panels, handrails, and decorative structures
Food and beverage processing equipment
Tubing, piping, and pressure vessels
Automotive and aerospace components requiring high precision
Resumen
304 stainless steel can be effectively cold worked to produce strong, precision components. Cold working enhances resistencia y dureza while retaining resistencia a la corrosión, lo que lo hace ideal para industrial, architectural, and household applications requiring durable and precisely formed parts.
Tratamiento térmico
Heat Treatment of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico widely used for its excellent corrosion resistance and formability. While 304 cannot be hardened by conventional heat treatment, it can undergo annealing or stress-relief treatments to improve ductility, reduce internal stresses, and restore properties after cold working or welding.
1. Recocido
Propósito: Relieves internal stresses, softens the material for forming, and restores ductility.
Proceso:
Calentar a 1010–1120 °C (1850–2050 °F).
Hold at temperature long enough to ensure uniform heating.
Cool rapidly in air, water, or quenching medium to avoid carbide precipitation.
Restores corrosion resistance and workability after cold working.
2. Alivio del estrés
Propósito: Reduces residual stresses caused by forming, machining, or welding.
Proceso:
Calentar a 450–650 °C (840–1200 °F).
Mantener durante 1–2 horas según el grosor de la pieza.
Enfriar lentamente a temperatura ambiente.
Minimiza distorsión, deformación o agrietamiento during subsequent processing.
3. Endurecimiento
304 stainless steel no puede ser endurecido por tratamiento térmico.
Strengthening is achieved primarily through trabajo en frío rather than quenching or tempering.
4. Surface Treatment Post Heat-Treatment
Pasivación can be applied to enhance corrosion resistance and remove free iron from the surface.
Polishing and surface finishing improve durability and aesthetics.
5. Aplicaciones
Componentes que requieren stress relief after welding or forming
Cold-worked sheets or strips needing restored ductility
Industrial and architectural parts requiring corrosion resistance and formability
Resumen
304 stainless steel has opciones limitadas de tratamiento térmico. Recocido y alivio de tensiones son los tratamientos primarios utilizados para restore ductility, relieve internal stresses, and maintain corrosion resistance. Unlike martensitic steels, 304 relies on trabajo en frío rather than heat treatment for strength enhancement, making it ideal for industrial, architectural, and household applications.
Resistencia al calor
Heat Resistance of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico conocida por su excellent corrosion resistance, mechanical properties, and versatility. It also offers good heat resistance, making it suitable for moderate temperature applications.
1. Límites de temperatura
Continuous service: Up to approximately 870 °C (1600 °F).
Intermittent service: Can withstand up to 925°C (1700°F).
Prolonged exposure above these temperatures may reduce mechanical strength and corrosion resistance.
2. Resistencia a la Oxidación
Resiste oxidación y formación de incrustaciones in air at moderate temperatures.
Rinde bien en non-oxidizing or mildly oxidizing atmospheres.
No apto para continuous high-temperature service in strongly oxidizing environments, where 309 or 310 stainless steel is preferred.
3. Mechanical Properties at Elevated Temperatures
Mantiene tensile strength and toughness at moderate temperatures.
Extended exposure to high heat may cause loss of ductility and potential grain growth.
4. Applications Benefiting from Heat Resistance
Industrial equipment exposed to moderate heat
Heat exchangers and furnace components in non-extreme environments
Kitchen appliances and food processing equipment
Architectural components exposed to sunlight or moderate heat
5. Consideraciones prácticas
Avoid prolonged service above 925°C (1700°F) para mantener la resistencia a la corrosión.
Considere higher-temperature stainless steels (e.g., 309, 310, 321) for applications exceeding these limits.
Heat treatment and surface finishing can help preserve properties at elevated temperatures.
Resumen
304 stainless steel has good heat resistance adecuado para moderate-temperature applications, maintaining strength and corrosion resistance. It is ideal for industrial, architectural, and household applications where temperatures remain within its recommended limits.
Trabajo en caliente
Hot Working of 304 Stainless Steel
304 stainless steel es un acero inoxidable austenítico conocida por su excellent corrosion resistance and formability. Puede ser trabajado en caliente de manera efectiva under controlled conditions to produce complex shapes or large deformations.
1. Características del trabajo en caliente
Adecuado para forging, rolling, extrusion, and hot bending.
Hot working reduces work hardening, allowing easier shaping compared to cold working.
High ductility allows for large deformations without cracking.
2. Rangos de temperatura recomendados
Annealed temperature range: 1010–1120°C (1850–2050°F) for hot forming operations.
Avoid overheating above 1120°C (2050°F) to prevent crecimiento del grano y menor resistencia a la corrosión.
Controlado refrigeración after hot working helps maintain mechanical properties.
3. Ventajas
Enables formation of large and complex components.
Reduces internal stresses compared to cold working.
Preserves resistencia a la corrosión when properly processed.
4. Limitaciones
Surface scaling may occur at high temperatures, requiring descaling or passivation post-processing.
Not intended for strengthening via heat treatment, as 304 is austenitic and non-hardenable.
Requiere controlled temperature and deformation rates to avoid defects.
5. Aplicaciones
Forged or rolled components requiring subsequent machining
Industrial equipment, piping, and tanks
Architectural and decorative elements with complex shapes
Automotive and aerospace structural components
Resumen
304 stainless steel can be trabajado en caliente de manera efectiva to create complex and large parts. Hot working reduces work hardening, facilitates forming, and maintains corrosion resistance, making 304 ideal for industrial, architectural, and household applications requiring durability and precision.