L111 Aluminium Alloy Bar & Extrusion T6511
Heat treatable aerospace aluminium alloy with very good corrosion resistance and weldability.
L111 is a medium strength extruded bar with an alloy strength somewhat higher than alloy 6061. It is not suitable for complex sections.
SCARICA IL PDF
Gamma
NOTA BENE
Se non vedi quello che stai cercando, contatta il tuo Centro servizi locale con le tue specifiche esigenze.
L111 T6511 Aluminium Related Specifications
| Sistema / Standard | Paese / Regione | Grade / Designation / Note |
| AA | Stati Uniti d'America | No single official AA number; L111-T6511 is a BS aerospace code |
| UNS | Internazionale | No specific UNS assigned; depends on the alloy defined in the spec |
| IT / DIN | Europa | No unique EN AW mapping; refer to the BS L111 material specification |
| GB (BS Aerospace) | United Kingdom | L111-T6511 – aluminium alloy extruded bars/sections, T6511 temper |
| JIS | Giappone | No direct JIS equivalent published |
| AFNOR | Francia | No direct AFNOR equivalent published |
Proprietà
Composizione chimica
Alloy L111
BS L111 (1971)
| Elemento Chimico | % Presente |
| Manganese (Mn) | 0.40 - 1.00 |
| Silicio (Si) | 0.70 - 1.30 |
| Magnesio (Mg) | 0.50 - 1.20 |
| Rame (Cu) | 0.00 - 0.10 |
| Ferro (Fe) | 0.00 - 0.50 |
| Stagno (Sn) | 0.00 - 0.05 |
| Cromo (Cr) | 0.00 - 0.25 |
| Nichel (Ni) | 0.00 - 0.10 |
| Piombo (Pb) | 0.00 - 0.05 |
| Titanio (Ti) | 0.00 - 0.20 |
| Zinco (Zn) | 0.00 - 0.20 |
| Alluminio (Al) | Equilibrio |
Proprietà Meccaniche
Alloy L111 - Mechanical Properties T6511 Temper for Various Dimensions
BS L111 (1971)
| Proprietà meccaniche | Valore |
| >20mm Proof Strength | 255 Min |
| >20mm Tensile Strength | 295 Min |
| >20mm Elongation | 7% min |
| 20mm - 150mm Proof Stress | 270 min |
| 20mm - 150mm Tensile Strength | 310 Min |
| 20mm - 150mm Elongation | 8% min |
| 150mm - 200mm Proof Stress | 240 Min |
| 150mm - 200mm Tensile Strength | 280 Min |
| 150mm - 200mm Elongation | 5% Min |
Proprietà fisiche generali
Alloy L111
BS L111 (1971)
| Proprietà fisica | Valore |
| Densità | 2710 g/cm³ |
| Punto di fusione | 650 °C |
| Dilatazione termica | 23.10 x 10-6/K |
| Modulo di elasticità | 70000 GPa |
| Conduttività termica | 167-216 W/m.K |
Applicazioni
- Aerospace components
- High technology applications
Caratteristiche
- Ottima resistenza alla corrosione
- Very good weldability (lowered strength values in the weld zone)
- Good machinability
- Good cold formability in T4 temper after a stabilizing heat treatment.
- Heat treatable medium high strength construction
- Medium high fatigue strength