스테인리스강, 오스테나이트계
304 Stainless Steel (S30400)
가장 다재다능하고 널리 사용되는 크롬-니켈(18/8) 오스테나이트 스테인리스 스틸입니다.
Stainless steel types 1.4301 and 1.4307 are also known as grades 304 and 304L respectively. Type 304 is the most versatile and widely used stainless steel. It is still sometimes referred to by its old name 18/8 which is derived from the nominal composition of type 304 being 18% chromium and 8% nickel.
유형 304 stainless steel is an austenitic grade that can be severely deep drawn. This property has resulted in 304 being the dominant grade used in applications like sinks and saucepans.
Type 304L is the low carbon version of 304. It is used in heavy gauge components for improved weldability. Some products such as plate and pipe may be available as “dual certified” material that meets the criteria for both 304 and 304L.
304H, a high carbon content variant, is also available for use at high temperatures.
304 stainless steel is the most widely used austenitic stainless steel, known for its excellent corrosion resistance, good mechanical properties, and versatile fabrication capabilities. It is often used in industrial, architectural, and household applications.
PDF 다운로드
범위
| Product Form | 설명 | 미터법 규격 | 제국 치수 |
| Round Bar | Bright Drawn H9 | 2.0mm - 25.0mm | 1⁄8" - 1" |
| Round Bar | Smooth Turned H9/H10 | 25.0mm - 60.0mm | 1" - 3" |
| Flat Bar | Rolled Edge | 12mm x 3mm - 100mm x 12mm | |
| Square Bar | 304S11/S31 | 12mm x 12mm - 50mm x 50mm | |
| Angle | 304S31 | 20mm x 20mm x 3mm - 100mm x 100mm x 10mm | |
| Welded Ornamental Tube | Mirror Polished 600 Grit | 30mm - 50mm | 1⁄2" - 4" |
| Welded Tube | Satin Polished 320 Grit | 16mm - 50mm | 1⁄2" - 2" |
| 정사각형 튜브 | Welded, Dull Polished | 12.7mm x 12.7mm - 10mm - 100mm | |
| Handrail Section | Welded, Unannealed, Dull Polished | 42.40mm - 60.30 (2.5mm wall) | 1 1⁄2" - 4 " (3mm wall) |
| 정사각형 튜브 | Welded, Unpolished | 12.7mm x 12.7mm - 250mm x 250mm | |
| Rectangular Tube | Welded, Unpolished | 80mm x 40mm - 250mm x 150mm | |
| Rectangular Tube | Welded, Dull Polished | 20mm x 10mm - 150mm x 100mm |
시트
| Product Type | 시트 크기 | 두께 |
| Sheet 2B Finish | 2000 x 1000 | 0.5mm - 3.0mm |
| Sheet 2B Finish | 2500 x 1250 | 0.5mm - 6.0mm |
| Sheet 2B Finish | 3000 x 1500 | 0.9mm - 3.0mm |
| Sheet 2R (BA) Finish | 2000 x 1000 | 0.5mm - 2.0mm |
| Sheet 2R (BA) Finish | 2500 x 1250 | 0.5mm - 2.0mm |
| Polished Sheet 240 Silicon | 2000 x 1000 | 0.6mm - 3.0mm |
| Polished Sheet 240 Silicon | 2500 x 1250 | 0.7mm - 6.0mm |
| Polished Sheet 240 Silicon | 3000 x 1500 | 1.0mm - 3.0mm |
| Perforated Sheet (Round Holes) | 2000 x 1000 | 1.0mm - 1.5mm |
| Perforated Sheet (Round Holes) | 2500 x 1250 | 0.7mm - 1.5mm |
| Perforated Sheet (Square Holes) | 2000 x 1000 | 1.5mm |
| CPP Plate ID Finish | 2000 x 1000 | 3.0mm - 6.0mm |
| CPP Plate ID Finish | 2500 x 1250 | 3.0mm - 12.0mm |
| CPP Plate ID Finish | 3000 x 1500 | 3.0mm - 12.0mm |
| CPP Plate ID Finish | 4000 x 2000 | 2.0mm - 12.0mm |
| Qaurto Plate ID Finish | 5" - 125" | - |
| Welded Mesh | 90" x 48" | - |
| 트레드플레이트 | 3000 x 1000 | 3.0mm |
| Traedplate | 3000 x 1250 | 4.5mm - 8.0mm |
참고 사항
원하는 내용이 표시되지 않으면 다음 연락처로 문의하세요. 지역 서비스 센터 특정 요구 사항에 따라.
304 Stainless Steel Related Specifications
| 시스템 / 표준 | 국가 / 지역 | 직급 |
| AISI | 미국 | 304 |
| UNS | 국제 | S30400 |
| EN / W.Nr. | 유럽 | 1.4301 |
| 영어 이름 | 유럽 | X5CrNi18-10 |
| ASTM A240 | 미국 | 304 (plate, sheet, strip) |
| ASTM A276 | 미국 | 304 (bars, shapes) |
| ASTM A213 | 미국 | TP304 (boiler / HX tubes) |
| ASTM A312 | 미국 | TP304 (seamless pipe) |
| 기가바이트 | 중국 | 0Cr18Ni9 |
| JIS | 일본 | SUS304 |
| BS | 영국 | 304S15 / 304S31 |
| AFNOR | 프랑스 | Z7CN18-09 |
속성
화학 성분
| 화학 원소 | % 현재 |
| 탄소(C) | 0.00 - 0.20 |
| 망간(Mn) | 0.00 - 1.00 |
| 규소 | 0.00 - 1.00 |
| 인 (P) | 0.00 - 0.04 |
| 황(S) | 0.00 - 0.03 |
| 크롬(Cr) | 15.00 - 17.00 |
| 니켈(Ni) | 1.25 - 2.50 |
기계적 특성
| 기계적 성질 | 가치 |
| 신율 A50 mm | 11 % |
| 인장 강도 | 850-1000 MPa |
| 항복 강도 | 665 MPa |
| 경도 브리넬 | 248-302 HB |
일반 물리적 성질
| 물리적 특성 | 가치 |
| 밀도 | 7.8 g/cm³ |
| 탄성 계수 | 200 GPa |
| 열 전도율 | 20.2 W/m.K |
Applications of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel known for its excellent corrosion resistance, good mechanical properties, and versatile formability. It is widely used across industrial, household, food, and architectural applications.
1. Food and Beverage Industry
Food processing equipment, tanks, and containers
Brewing, dairy, and pharmaceutical machinery
Piping, valves, and fittings requiring hygienic surfaces
2. 화학 및 석유화학 산업
Chemical processing equipment and storage tanks
Heat exchangers, condensers, and piping systems
Components exposed to acids, alkalis, and other corrosive environments
3. Household and Kitchen Applications
Sinks, kitchen appliances, and utensils
Decorative trims, handrails, and architectural hardware
4. Industrial and Manufacturing Applications
Pumps, valves, and fasteners in corrosive environments
Machinery and equipment exposed to moisture or mild chemicals
Structural components requiring durability and corrosion resistance
5. Medical and Pharmaceutical Applications
Surgical instruments and medical devices
Laboratory benches and components requiring sterilization
Equipment where hygiene and corrosion resistance are critical
요약
304 stainless steel is highly versatile, providing excellent corrosion resistance, strength, and formability. Its applications span food processing, chemical, household, medical, and industrial sectors, making it ideal for environments where durability and hygiene are essential.
Characteristics of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel widely used for its excellent corrosion resistance, good mechanical properties, and versatile formability. It is suitable for a broad range of applications in industrial, household, and architectural environments.
1. Chemical Composition
Contains chromium (18–20%) 그리고 nickel (8–10.5%).
Low carbon content ensures good corrosion resistance and weldability.
Trace elements like manganese, silicon, and phosphorus enhance mechanical stability.
2. 내식성
탁월한 내성 oxidation, atmospheric corrosion, and mild acids.
〜에서 잘 작동합니다 indoor, outdoor, and mildly corrosive environments.
Notably resistant to rust and staining, making it ideal for hygiene-critical applications.
3. 기계적 성질
높음 tensile strength and yield strength.
우수 연성 및 인성, even at low temperatures.
Maintains properties over a wide range of temperatures.
4. 재료 제작 및 성형성
우수 cold working and forming characteristics, suitable for deep drawing, bending, and stamping.
될 수 있다 welded easily with minimal risk of intergranular corrosion.
Machinable, though slightly less so than 303 stainless steel.
5. Heat and Temperature Resistance
Performs well at moderate temperatures, with intermittent service up to 870°C (1600°F).
Continuous service temperatures should remain below 925°C (1700°F).
6. Applications
Food and beverage processing equipment
Chemical and pharmaceutical machinery
Kitchen appliances, sinks, and household items
Architectural components, handrails, and decorative trims
요약
304 stainless steel is characterized by excellent corrosion resistance, good mechanical strength, high ductility, and versatile formability. Its combination of properties makes it ideal for industrial, household, chemical, and architectural applications, particularly where durability, hygiene, and corrosion resistance are important.
추가 정보
제작
Fabrication of 304 Stainless Steel
304 stainless steel is a widely used austenitic stainless steel known for its excellent corrosion resistance and formability. Its fabrication characteristics make it suitable for a wide range of industrial, architectural, and household applications.
1. 형성
Cold Working: 304 can be bent, drawn, stamped, or deep-drawn in the annealed condition.
Hot Working: Suitable for hot forging, rolling, or extrusion at controlled temperatures (approx. 1010–1120°C / 1850–2050°F).
Work hardens moderately during forming, which may require 중간 풀림 for complex shapes.
2. Machining
Machinable with appropriate cutting tools and speeds, though less machinable than 303 stainless steel.
Produces smooth finishes with careful selection of cutting fluids and tool materials.
3. Welding
우수한 용접성 using TIG, MIG, or resistance welding.
Low carbon content (≤0.08%) minimizes carbide precipitation, reducing the risk of 입계 부식 in welded areas.
Post-weld annealing or passivation can further enhance corrosion resistance.
4. Surface Finishing
될 수 있다 polished, brushed, or passivated to improve aesthetics and corrosion resistance.
Suitable for both functional and decorative applications.
5. Advantages of 304 Stainless Steel Fabrication
Versatile forming options (cold or hot working)
Good weldability for assembly of components
Can achieve high-quality surface finishes
유지 내식성 after fabrication
6. Applications
Kitchen and food processing equipment
Architectural panels, handrails, and decorative features
Tanks, piping, and industrial equipment
Medical and pharmaceutical instruments
요약
304 stainless steel is highly versatile for fabrication, offering excellent formability, weldability, and surface finish options. These characteristics make it ideal for industrial, architectural, and household applications requiring durability, corrosion resistance, and aesthetic appeal.
용접성
Weldability of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel widely used for its excellent corrosion resistance and mechanical properties. One of its key advantages is superior weldability, making it suitable for a wide range of industrial, architectural, and household applications.
1. General Welding Characteristics
Easily weldable using standard methods: TIG (GTAW), MIG (GMAW), spot welding, and resistance welding.
Low carbon content (≤0.08%) reduces the risk of 입계 부식 열영향부.
생산하다 strong, corrosion-resistant welds without significant loss of mechanical properties.
2. Welding Techniques
TIG (GTAW): Provides precise control and high-quality welds, ideal for thin sheets and critical applications.
MIG (GMAW): Efficient for thicker materials and high-volume production.
Spot and resistance welding: Suitable for sheet metal assemblies.
3. Filler Materials
Commonly use 304 or 308 stainless steel filler rods/wires to maintain corrosion resistance and mechanical integrity.
Selection depends on the specific application and service environment.
4. Preheating and Post-Weld Treatment
Preheating is generally unnecessary due to low carbon content.
Post-weld annealing or passivation can enhance corrosion resistance and restore surface finish if required.
5. Advantages
Excellent weld quality with minimal distortion or cracking.
유지 내식성과 기계적 강도 in welded areas.
Suitable for both thin sheets and thick sections.
6. Applications Benefiting from Weldability
Kitchen equipment, sinks, and countertops
Piping, tanks, and pressure vessels
Architectural panels, handrails, and decorative structures
Medical and pharmaceutical instruments
요약
304 stainless steel is highly weldable, offering strong, corrosion-resistant, and aesthetically acceptable welds. Its low carbon content ensures minimal intergranular corrosion risk, 이상적입니다 industrial, architectural, and household applications requiring both durability and weld integrity.
기계 가공성
Machinability of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel well-known for its excellent corrosion resistance and mechanical properties. However, compared to 303 stainless steel, its machinability is moderate, requiring careful tooling and process control.
1. Machining Characteristics
304 stainless steel work hardens rapidly during machining, which can increase tool wear.
생산하다 tough, continuous chips, which may require chip breakers or special tooling.
Standard machining speeds must be reduced compared to carbon steels to avoid excessive heat.
2. 도구 추천
Tool materials: High-speed steel (HSS), carbide, or coated carbide tools are recommended.
Cutting speeds: Lower than mild steel; increase feed rate gradually to reduce heat buildup.
Coolant/Lubrication: Use cutting fluids to reduce friction, dissipate heat, and improve surface finish.
3. Machining Operations
Turning: Requires slower speeds and frequent tool changes; good surface finish achievable.
Milling: Use sharp tools and moderate depth of cut; avoid overheating.
Drilling and Tapping: Pre-drill larger holes and use proper lubricants to prevent galling.
4. Advantages
Can produce high-quality, corrosion-resistant components with proper machining practices.
적합 대상 precision parts in industrial, food, and chemical processing equipment.
5. 한계
Less machinable than 303 stainless steel due to the absence of sulfur.
Requires careful tool selection, speed, and lubrication to avoid excessive wear and work hardening.
6. Applications Benefiting from Machinability
Food and beverage processing machinery
Piping, valves, and fittings
Industrial and chemical processing components
Medical and pharmaceutical instruments
요약
304 stainless steel has 보통의 가공성, requiring appropriate tooling, cutting speeds, and lubrication to achieve precise components. While not as easily machined as 303 stainless steel, it offers excellent corrosion resistance and mechanical properties, 이상적입니다 industrial, medical, and food-processing applications.
내식성
Corrosion Resistance of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel known for its excellent corrosion resistance, making it one of the most widely used stainless steels in industrial, architectural, and household applications.
1. 일반 부식 저항
Highly resistant to oxidation and atmospheric corrosion.
〜에서 잘 작동합니다 indoor and outdoor environments.
Maintains integrity in humid and mildly corrosive conditions.
2. Resistance to Chemicals
탁월한 내성 food acids, alkaline solutions, and many industrial chemicals.
적합 대상 food processing, chemical equipment, and pharmaceutical applications.
Less resistant than 316 stainless steel in chloride-rich or marine environments.
3. Stress and Intergranular Corrosion
Low carbon content (≤0.08%) minimizes 탄화물 석출 during welding.
저항력이 있는 입계 부식 even after welding when properly fabricated.
Sensitive to chloride-induced pitting or crevice corrosion in high-salinity environments.
4. Surface Treatment
될 수 있다 polished or passivated to improve corrosion resistance.
Surface finishing enhances both appearance and longevity.
5. Applications Benefiting from Corrosion Resistance
Kitchen appliances, sinks, and cookware
Food and beverage processing equipment
Architectural panels, handrails, and decorative structures
Tanks, piping, and industrial machinery
Medical and pharmaceutical instruments
요약
304 stainless steel exhibits excellent corrosion resistance in a wide range of environments, including industrial, food processing, and architectural applications. 그것의 low carbon content ensures weldability without compromising corrosion resistance, making it ideal for durable and long-lasting components.
냉간 가공
Cold Working of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel widely used for its excellent corrosion resistance, mechanical properties, and formability. It responds well to cold working, which can improve strength and hardness but also increases work hardening.
1. Cold Working Characteristics
될 수 있다 bent, drawn, stamped, or deep-drawn 풀림 상태에서.
Cold working increases 강도와 경도 due to strain hardening.
Excessive deformation may reduce ductility and requires careful control.
2. Techniques
Bending and forming: Suitable for moderate bends; sharp bends may require intermediate annealing.
Deep drawing: Excellent, especially in thin sheets, due to good ductility.
Rolling or stamping: Can achieve complex shapes with proper tooling and process control.
3. Advantages
Cold working improves tensile strength and hardness without heat treatment.
Enables production of precision components and complex shapes.
유지 내식성 when proper annealing and passivation are applied after severe deformation.
4. Limitations
Work hardens quickly, which may require 중간 풀림 for extensive forming operations.
Excessive cold working can increase internal stresses, potentially leading to distortion or cracking in subsequent processes.
5. Applications Benefiting from Cold Working
Architectural panels, handrails, and decorative structures
Food and beverage processing equipment
Tubing, piping, and pressure vessels
Automotive and aerospace components requiring high precision
요약
304 stainless steel can be effectively cold worked to produce strong, precision components. Cold working enhances 강도와 경도 while retaining 내식성, 이상적입니다 industrial, architectural, and household applications requiring durable and precisely formed parts.
열처리
Heat Treatment of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel widely used for its excellent corrosion resistance and formability. While 304 cannot be hardened by conventional heat treatment, it can undergo annealing or stress-relief treatments to improve ductility, reduce internal stresses, and restore properties after cold working or welding.
1. Annealing
목적: Relieves internal stresses, softens the material for forming, and restores ductility.
Process:
Heat to 1010–1120°C (1850–2050°F).
Hold at temperature long enough to ensure uniform heating.
Cool rapidly in air, water, or quenching medium to avoid carbide precipitation.
Restores corrosion resistance and workability after cold working.
2. 스트레스 해소
목적: Reduces residual stresses caused by forming, machining, or welding.
Process:
Heat to 450–650°C (840–1200°F).
Hold for 1–2 hours depending on part thickness.
Cool slowly to room temperature.
Minimizes distortion, warping, or cracking during subsequent processing.
3. Hardening
304 stainless steel cannot be hardened by heat treatment.
Strengthening is achieved primarily through cold working rather than quenching or tempering.
4. Surface Treatment Post Heat-Treatment
수동태 can be applied to enhance corrosion resistance and remove free iron from the surface.
Polishing and surface finishing improve durability and aesthetics.
5. Applications
요구되는 구성 요소 stress relief after welding or forming
Cold-worked sheets or strips needing restored ductility
Industrial and architectural parts requiring corrosion resistance and formability
요약
304 stainless steel has limited heat treatment options. Annealing and stress relief are the primary treatments used to restore ductility, relieve internal stresses, and maintain corrosion resistance. Unlike martensitic steels, 304 relies on cold working rather than heat treatment for strength enhancement, making it ideal for industrial, architectural, and household applications.
내열성
Heat Resistance of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel known for its excellent corrosion resistance, mechanical properties, and versatility. It also offers good heat resistance, making it suitable for moderate temperature applications.
1. Temperature Limits
Continuous service: Up to approximately 870°C (1600°F).
Intermittent service: Can withstand up to 925°C (1700°F).
Prolonged exposure above these temperatures may reduce mechanical strength and corrosion resistance.
2. Oxidation Resistance
Resists 산화 및 스케일링 in air at moderate temperatures.
〜에서 잘 작동합니다 non-oxidizing or mildly oxidizing atmospheres.
Not suitable for continuous high-temperature service in strongly oxidizing environments, where 309 or 310 stainless steel is preferred.
3. Mechanical Properties at Elevated Temperatures
유지 tensile strength and toughness at moderate temperatures.
Extended exposure to high heat may cause loss of ductility and potential grain growth.
4. Applications Benefiting from Heat Resistance
Industrial equipment exposed to moderate heat
Heat exchangers and furnace components in non-extreme environments
Kitchen appliances and food processing equipment
Architectural components exposed to sunlight or moderate heat
5. Practical Considerations
Avoid prolonged service above 925°C (1700°F) to maintain corrosion resistance.
고려 사항 higher-temperature stainless steels (e.g., 309, 310, 321) for applications exceeding these limits.
Heat treatment and surface finishing can help preserve properties at elevated temperatures.
요약
304 stainless steel has good heat resistance suitable for moderate-temperature applications, maintaining strength and corrosion resistance. It is ideal for industrial, architectural, and household applications where temperatures remain within its recommended limits.
열간 가공
Hot Working of 304 Stainless Steel
304 stainless steel is an austenitic stainless steel known for its excellent corrosion resistance and formability. It can be hot worked effectively under controlled conditions to produce complex shapes or large deformations.
1. Hot Working Characteristics
적합 대상 forging, rolling, extrusion, and hot bending.
열간 가공 reduces work hardening, allowing easier shaping compared to cold working.
High ductility allows for large deformations without cracking.
2. Recommended Temperature Ranges
Annealed temperature range: 1010–1120°C (1850–2050°F) for hot forming operations.
Avoid overheating above 1120°C (2050°F) to prevent grain growth and reduced corrosion resistance.
Controlled cooling after hot working helps maintain mechanical properties.
3. Advantages
Enables formation of large and complex components.
Reduces internal stresses compared to cold working.
Preserves 내식성 when properly processed.
4. Limitations
Surface scaling may occur at high temperatures, requiring descaling or passivation post-processing.
Not intended for strengthening via heat treatment, as 304 is austenitic and non-hardenable.
Requires controlled temperature and deformation rates to avoid defects.
5. Applications
Forged or rolled components requiring subsequent machining
Industrial equipment, piping, and tanks
Architectural and decorative elements with complex shapes
Automotive and aerospace structural components
요약
304 stainless steel can be hot worked effectively to create complex and large parts. Hot working reduces work hardening, facilitates forming, and maintains corrosion resistance, making 304 ideal for industrial, architectural, and household applications requiring durability and precision.