Aluminium, Commercial Alloy
6101 T6 Bar & Extrusion
전력 배전 부품 및 장비의 제조 및 건설에 사용되는 열처리 가능한 단조 알루미늄 합금입니다.
6101 is a heat treatable wrought alloy best suited for applications involving moderate strength and maximum electrical conductivity.
It is similar to alloy 6063, but with minor chemistry changes which enhance electrical conductivity. Although this alloy is primarily used for busbar conductor applications it is also an excellent choice for other electrical projects.
This alloy is available in various temper conditions. The wide variety of tempers provide different strengths, formability, and electrical conductivity levels which allows for design flexibility.
PDF 다운로드
범위
참고 사항
원하는 내용이 표시되지 않으면 다음 연락처로 문의하세요. 지역 서비스 센터 특정 요구 사항에 따라.
6101 T6 Aluminium Related Specifications
| System / Standard | Country / Region | Grade / Designation |
| AA | USA | 6101-T6 |
| UNS | International | A96101 (6101-T6) |
| EN / DIN | Europe | EN AW-6101-T6 |
| EN Name | Europe | AlMgSi-T6 |
| GB | China | 6101-T6 |
| BS | UK | 6101-T6 (extruded conductor alloy) |
Properties
화학 성분
6101 T6
| Chemical Element | % Present |
| 크롬(Cr) | 0.00 - 0.03 |
| 구리(Cu) | 0.00 - 0.10 |
| Iron (Fe) | 0.00 - 0.50 |
| Magnesium (Mg) | 0.35 - 0.80 |
| 망간(Mn) | 0.00 - 0.03 |
| Other (Each) | 0.00 - 0.03 |
| Others (Total) | 0.00 - 0.10 |
| Silicon (Si) | 0.30 - 0.70 |
| Zinc (Zn) | 0.00 - 0.10 |
기계적 특성
| Mechanical Property | 가치 |
| Tensile Strength | 97 MPa |
General Physical Properties
| Physical Property | 가치 |
| Density | 2.7 g/cm³ |
| Melting Point | 588 °C |
애플리케이션
- Electrical busbar conductor applications for enclosed bus electrical installations
- Power transmissions
- Power stations
Characteristics
- Good mechanical strength
- High electrical conductivity
- Good machinability
- 우수한 용접성
- Good corrosion resistance
- Easily cold worked in aged or annealed conditions
Additional Information
용접성
- Aluminum 6101 alloy can be welded using all standard welding methods. Inert gas arc welding method is the most preferred method for welding this alloy. The strength of the subsequent parts will be reduced when welded in the heat treated condition.
Heat Treatment
- Aluminum 6101 alloy does not react to heat treatment. However, heat treatment can be done by annealing and aging.
Cold Working
- Aluminum 6101 alloy can be cold worked in the aged or annealed conditions.
Forming
- Aluminum 6101 alloy can be formed using conventional methods.