Aluminium, Commercial Alloy

2014 T6511 Bar & Extrusion

A high strength aluminium alloy which retains its strength after heat treatment.

A high strength 4 to 5% copper alloy produced in extruded bar and profile form, in the fully heat-treated condition (solution heat-treated & artificially aged).

Normally stocked in the T6511 condition (stress relieved by controlled stretching) Except for sizes under 10mm diameter and over 203.2mm diameter. (T6 only). Over 203.mm diameter is manufactured to chemical composition only.

DOWNLOAD PDF

Range

Product Form Imperial Sizes Metric Sizes
Round Bar 3⁄16"- 16" 6mm - 50mm

PLEASE NOTE

If you do not see what you are looking for, please contact your local service centre with your specific requirements.

2014 T6511 Aluminium Related Specifications

System / Standard Country / Region Grade / Designation
AA USA 2014-T6511
UNS International A92014 (2014-T6511)
EN / DIN Europe EN AW-2014A / WNr 3.1255-T6511
EN Name Europe AlCu4SiMg-T6511
ASTM B221 USA 2014-T6511 extruded bars / rods / shapes
GB China 2A14-T6511
JIS Japan A2014-T6511
BS (Aerospace) UK L168 / HE15 (2014A bars & sections, T6511)
AFNOR France A-U4SG-T6511

Properties

Chemical Composition

Alloy 2014

Chemical Element % Present
Silicon (Si) 0.50 - 0.90
Iron (Fe) 0.50 max
Copper (Cu) 3.90 - 5.00
Zinc (Zn) 0.25 max
Manganese (Mn) 0.40 - 1.20
Magnesium (Mg) 0.20 - 0.80
Titanium (Ti) 0.15 max
Others (Total) 0.15 max
Chromium (Cr) 0.10 max
Nickel (Ni) 0.10 max
Other (Each) 0.05 max
Titanium + Zirconium (Ti+Zr) 0.20 max
Aluminium (Al) Balance

Profile 25mm to 75mm Wall Thickness

Mechanical Property Value
Proof Stress 415 Min MPa
Tensile Strength 460 Min MPa
Hardness Brinell 140 HB
Elongation A 7 Min %

Profile Up to 25mm Wall Thickness

Mechanical Property Value
Proof Stress 370 Min MPa
Tensile Strength 415 Min MPa
Elongation A50 mm 5 Min %
Hardness Brinell 140 HB
Elongation A 7 Min %

Tube 10mm to 40mm Wall Thickness

Mechanical Property Value
Proof Stress 400 Min MPa
Tensile Strength 450 Min MPa
Elongation A50 mm 4 Min %
Hardness Brinell 140 HB
Elongation A 6 Min %

Tube Up to 10mm Wall Thickness

Mechanical Property Value
Proof Stress 370 Min MPa
Tensile Strength 415 Min MPa
Hardness Brinell 140 HB
Elongation A 7 Min %
Elongation A50 mm 5 Min %

Bar 150mm to 200mm Dia. & A/F

Mechanical Property Value
Proof Stress 350 Min MPa
Tensile Strength 430 Min MPa
Hardness Brinell 140 HB
Elongation A 6 Min %

Bar 75mm to 150mm Dia. & A/F

Mechanical Property Value
Proof Stress 420 Min MPa
Tensile Strength 465 Min MPa
Hardness Brinell 140 HB
Elongation A 7 Min %

Bar 25mm to 75mm Dia. & A/F

Mechanical Property Value
Proof Stress 415 Min MPa
Tensile Strength 460 Min MPa
Hardness Brinell 140 HB
Elongation A 7 Min %

Rod & Bar Up to 25mm Dia. & A/F

Mechanical Property Value
Tensile Strength 415 Min MPa
Proof Stress 370 Min MPa
Hardness Brinell 140 HB
Elongation A50 mm 5 Min %
Elongation A 6 Min %
Physical Property Value
Density 2.82 g/cm³
Modulus of Elasticity 71 GPa
Electrical Resistivity 0.045 x 10-6 Ω .m
Thermal Conductivity 138 W/m.K
Thermal Expansion 23 x 10-6/K
Melting Point 535 °C

Applications

Characteristics

Additional Information

Weldability
Process Rating
Brazing & Soldering Not Recommended
Oxygen Not Recommended
Inert Gas Not Recommended
Resistance, Spot, Beam Excellent
Process Rating
Protective Anodising Fair
Bright Anodising Unsuitable
Hard Anodising Good
Colour Anodising Fair (Dark colours only)
Plating Very Good

Recherchez le produit dont vous avez besoin

Un vaste réseau de centres de services en Chine, soutenu par de solides installations de traitement.

Fraisage CNC

CLAUSE DE NON-RESPONSABILITÉ

Ces données sont uniquement indicatives et ne doivent pas remplacer les spécifications complètes. En particulier, les exigences en matière de propriétés mécaniques varient considérablement en fonction du tempérament, du produit et des dimensions du produit. Toutes les informations sont basées sur nos connaissances actuelles et sont données en toute bonne foi. La société n'accepte aucune responsabilité en ce qui concerne toute action entreprise par un tiers sur la base de ces informations. Veuillez noter que la date de ‘mise à jour de la fiche technique’ indiquée ci-dessus ne constitue pas une garantie d'exactitude ou de mise à jour de la fiche technique.

Les informations fournies dans cette fiche technique proviennent de diverses sources reconnues, y compris les normes EN, les références industrielles reconnues (imprimées ou en ligne) et les données des fabricants. Aucune garantie n'est donnée que les informations proviennent de la dernière édition de ces sources ou qu'elles sont exactes. Le matériel fourni par l'entreprise peut varier de manière significative par rapport à ces données, mais il sera conforme à toutes les normes pertinentes et applicables. Étant donné que les produits décrits peuvent être utilisés à des fins très diverses et que la Société n'a aucun contrôle sur leur utilisation, la Société exclut spécifiquement toutes les conditions ou garanties exprimées ou implicites en vertu de la loi ou autrement quant aux dimensions, aux propriétés et/ou à l'adéquation à un usage particulier, qu'elles soient exprimées ou implicites. Les conseils donnés par la Société à une tierce partie sont donnés pour l'assistance de cette partie uniquement et sans responsabilité de la part de la Société. Toutes les transactions sont soumises aux conditions de vente actuelles de la Société. L'étendue des responsabilités de la Société à l'égard de tout client est clairement définie dans ces conditions, dont une copie est disponible sur demande.

Si vous avez des questions, n'hésitez pas à nous contacter, nous sommes en ligne 24 heures par jour.