Aluminium, Commercial Alloy
Aluminium Alloy 6063 T6 Bar & Extrusion
One of the most popular alloys in the 6000 series and most widely known as an architectural alloy.
Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy. It is normally used in intricate extrusions and is most commonly supplied in the T6 temper.
ดาวน์โหลด PDF
ช่วง
| Product Form | ช่วงขนาด | ช่วงขนาด |
| From | To | |
| Flat Bar | 3⁄8" x 1⁄8" | 6" x 1" |
| Square Box Section | 1⁄2" x 1⁄2" x 16swg | 4" x 4" x 1⁄4" |
| Rectangular Box Section | 1" x 1⁄2" x 16swg | 6" x 3" x 3⁄8" |
| หลอด | 3⁄8" OD x 16swg | 6 1⁄2" OD x 1⁄4" |
| Channel | 3⁄8" x 3⁄8" x 1⁄16" | 10" x 3" x 3⁄8" x 1⁄2" |
| Equal Angle | 3⁄8" x 3⁄8" x 1⁄16" | 6" x 6" x 1⁄2" |
| Unequal Angle | 3⁄4" x 1⁄4" x 1⁄16" | 6" x 3" x 3⁄8" |
| Angle (Metric) | 25 x 25 x 3mm, 50 x 25 x 3mm, 50 x 50 x 3mm | - |
| Z Section | 3⁄4" x 1⁄2" x 1⁄16" | 1 3⁄4" x 1" x 1⁄8" |
โปรดทราบ
หากท่านไม่พบสิ่งที่ค้นหา โปรดติดต่อ ศูนย์บริการในพื้นที่ ตามข้อกำหนดเฉพาะของคุณ.
6063 T6 Aluminium Related Specifications
| ระบบ / มาตรฐาน | ประเทศ / ภูมิภาค | ระดับ / ตำแหน่ง |
| เอเอ | สหรัฐอเมริกา | 6063-T6 |
| สหประชาชาติ | นานาชาติ | A96063 (6063-T6) |
| อังกฤษ / เยอรมัน | ยุโรป | EN AW-6063-T6 / 3.32206 |
| ชื่อภาษาอังกฤษ | ยุโรป | AlMg0.7Si-T6 |
| จีบี | ประเทศจีน | 6063-T6 |
| JIS | ญี่ปุ่น | A6063-T6 |
| BS | สหราชอาณาจักร | 6063-T6 (extruded profiles) |
คุณสมบัติ
องค์ประกอบทางเคมี
Alloy 6063
| ธาตุเคมี | % นำเสนอ |
| แมงกานีส (Mn) | 0.00 - 0.10 |
| เหล็ก (Fe) | 0.00 - 0.35 |
| แมกนีเซียม (Mg) | 0.45 - 0.90 |
| ซิลิคอน (Si) | 0.20 - 0.60 |
| สังกะสี (Zn) | 0.00 - 0.10 |
| ไทเทเนียม (Ti) | 0.00 - 0.10 |
| โครเมียม (Cr) | 0.00 - 0.10 |
| ทองแดง (Cu) | 0.00 - 0.10 |
| อื่นๆ (แต่ละ) | 0.00 - 0.05 |
| อื่น ๆ (ทั้งหมด) | 0.00 - 0.15 |
| อะลูมิเนียม (Al) | ความสมดุล |
คุณสมบัติทางกล
Rod & Bar Up To 150mm Dia. & A/F
| Mechanical Property | มูลค่า |
| Proof Stress | 170 Min MPa |
| Tensile Strength | 215 Min MPa |
| Hardness Brinell | 75 HB |
| Elongation A | 10 Min % |
| Elongation A50 mm | 8 Min % |
Rod & Bar 150mm to 200mm Dia. & A/F
| Mechanical Property | มูลค่า |
| Proof Stress | 160 Min MPa |
| Tensile Strength | 195 Min MPa |
| Hardness Brinell | 75 HB |
| Elongation A | 10 Min % |
Tube Up To 25mm Wall Thickness
| Mechanical Property | มูลค่า |
| Proof Stress | 170 Min MPa |
| Tensile Strength | 215 Min MPa |
| Elongation A50 mm | 8 Min % |
| Hardness Brinell | 75 HB |
| Elongation A | 10 Min % |
Profiles Up to 10mm Wall Thickness
| Mechanical Property | มูลค่า |
| Proof Stress | 170 Min MPa |
| Tensile Strength | 215 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 75 HB |
| Elongation A | 8 Min % |
Profiles 10mm to 25mm Wall Thickness
| Mechanical Property | มูลค่า |
| Proof Stress | 160 Min MPa |
| Tensile Strength | 195 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 75 HB |
| Elongation A | 8 Min % |
คุณสมบัติทางกายภาพทั่วไป
| Process | Rating |
| Weldability - Gas | Good |
| Weldability - Arc | Very Good |
| Weldability - Resistance | Good |
| Brazability | Very Good |
| Solderability | Good |
การประยุกต์ใช้
- Extrusions
- Window frames
- Doors
- Shop fittings
- Irrigation tubing
- In balustrading the rails and posts are normally in the T6 temper and formed elbows and bends are T4
- Hydro formed tube for chassis
คุณลักษณะ
- High corrosion resistance
- Medium strength
- Good surface finish
- Readily suited to welding
- Easily anodised
- Good formability in the T4 condition
ข้อมูลเพิ่มเติม
Weldability
- 6063 is suitable for all conventional welding methods.
- Welding wire generally should be alloy 5183 or alloy 4043.
- When maximum electrical conductivity is required use alloy 4043.
- For strength and conductivity use alloy 5346 and increase the size of the weld to compensate for the lower conductivity.
| Process | Rating |
| Weldability - Gas | Good |
| Weldability - Arc | Very Good |
| Weldability - Resistance | Good |
| Brazability | Very Good |
| Solderability | Good |
Fabrication
| Process | Rating |
| Workability - Cold | Average (Acceptable) |
| Machinability | Good |